粉煤灰与稻草纤维复掺对混凝土力学性能的影响

Study on the Mechanical Properties of Fly Ash and Straw Fiber Composite Concrete

2021年第11期

混凝土；粉煤灰；稻草纤维；力学性能

Concrete; Fly ash; Straw fiber; Mechanical property

2021年第11期

10.19761/j.1000-4637.2021.11.064.05

省级大学生创新创业训练计划项目（S202010359335）。

刘涛，赵明皓，聂国豪，韩龙宇，林锋，巫绪涛

合肥工业大学土木与水利工程学院，安徽宣城 242000

刘涛，赵明皓，聂国豪，韩龙宇，林锋，巫绪涛

刘涛,赵明皓,聂国豪,等.粉煤灰与稻草纤维复掺对混凝土力学性能的影响[J].混凝土与水泥制品,2021(11):64-67,72.

LIU T,ZHAO M H,NIE G H.Study on the Mechanical Properties of Fly Ash and Straw Fiber Composite Concrete[J].China Concrete and Cement Products,2021(11):64-67,72.

浏览量:

1000

摘要：研究了丝状、杆状稻草纤维分别与粉煤灰复掺对混凝土力学性能的影响。结果表明：随着稻草纤维和粉煤灰掺量的增加，混凝土的抗压强度、劈裂抗拉强度和抗折强度总体呈下降趋势，但稻草纤维能够有效改善混凝土的脆性破坏形态；丝状稻草纤维对混凝土性能的不利影响小于杆状稻草纤维；当丝状稻草纤维掺量为0.3%、粉煤灰掺量为20%时，混凝土的抗压强度较高；当丝状稻草纤维掺量为0.3%、粉煤灰掺量为10%时，混凝土的劈裂抗拉强度较高；当丝状稻草纤维掺量为0.3%、粉煤灰掺量为20%时，混凝土的抗折强度较高。 Abstract: The effects of filamentary straw fiber and rod-shaped straw fiber and fly ash on mechanical properties of concrete were studied. The results show that the compressive strength, splitting tensile strength and flexural strength of concrete generally decrease with the increase of straw fiber content and fly ash content, but straw fiber can effectively improve the brittle damage pattern of concrete. The adverse effect of filamentous straw fiber on the performance of concrete is less than that of rod-shaped straw fiber. The compressive strength of the concrete is higher when the filamentary straw fiber content is 0.3% and the fly ash content is 20%. The splitting tensile strength of the concrete is higher when the filamentary straw fiber content is 0.3% and the fly ash content is 10%. The flexural strength of the concrete is higher when the filamentary straw fiber content is 0.3% and the fly ash content is 20%.

英文名 : Study on the Mechanical Properties of Fly Ash and Straw Fiber Composite Concrete

刊期 : 2021年第11期

关键词 : 混凝土；粉煤灰；稻草纤维；力学性能

Key words : Concrete; Fly ash; Straw fiber; Mechanical property

刊期 : 2021年第11期

DOI : 10.19761/j.1000-4637.2021.11.064.05

文章编号 :

基金项目 : 省级大学生创新创业训练计划项目（S202010359335）。

作者 : 刘涛，赵明皓，聂国豪，韩龙宇，林锋，巫绪涛

单位 : 合肥工业大学土木与水利工程学院，安徽宣城 242000

刘涛，赵明皓，聂国豪，韩龙宇，林锋，巫绪涛

刘涛,赵明皓,聂国豪,等.粉煤灰与稻草纤维复掺对混凝土力学性能的影响[J].混凝土与水泥制品,2021(11):64-67,72.

LIU T,ZHAO M H,NIE G H.Study on the Mechanical Properties of Fly Ash and Straw Fiber Composite Concrete[J].China Concrete and Cement Products,2021(11):64-67,72.





摘要

参数

结论

参考文献

引用本文

Abstract: The effects of filamentary straw fiber and rod-shaped straw fiber and fly ash on mechanical properties of concrete were studied. The results show that the compressive strength, splitting tensile strength and flexural strength of concrete generally decrease with the increase of straw fiber content and fly ash content, but straw fiber can effectively improve the brittle damage pattern of concrete. The adverse effect of filamentous straw fiber on the performance of concrete is less than that of rod-shaped straw fiber. The compressive strength of the concrete is higher when the filamentary straw fiber content is 0.3% and the fly ash content is 20%. The splitting tensile strength of the concrete is higher when the filamentary straw fiber content is 0.3% and the fly ash content is 10%. The flexural strength of the concrete is higher when the filamentary straw fiber content is 0.3% and the fly ash content is 20%.

扫二维码用手机看

[1] 陈登,宋旭艳,姜正平,等.秸秆与粉煤灰复掺对混凝土性能的影响[J].混凝土与水泥制品,2020(4):100-103.
[2] 陈斌,卢玉斌,苏实,等.秸秆纤维对混凝土拉伸性能的影响[J].混凝土与水泥制品,2017(10):85-88.
[3] 蹇守卫,汪婷,马保国,等.改性水稻秸秆对水泥基材料性能影响研究[J].材料导报,2014,28(6):132-135.
[4] 梁永哲,陈毅,刘大翔,等.外掺植物纤维对冻融作用下植被混凝土抗剪强度的影响[J].水土保持通报,2016,36(2):136-139,145.
[5] 何栋梁,杨伟军,成彦惠.植物纤维保温免拆模板抗折强度试验研究[J].硅酸盐通报,2019,38(3):289-294.
[6] 梁磊,赵文,李艺,周啟,程云虹.增强纤维的加入对混凝土抗冲击性能的影响[J].混凝土与水泥制品,2007(1):44-46.
[7] 王雪,翟颠颠,郭远臣,等.剑麻纤维增强混凝土力学性能研究[J].硅酸盐通报,2017(7):327-330.
[8] 张强,李耀庄,刘保华.秸秆资源在混凝土中应用的研究进展[J].硅酸盐通报,2015(4):1000-1003.
[9] 孙婧,麻建锁,蔡焕琴,等.利用玉米秸秆制备浮石复合混凝土的试验研究[J].混凝土,2013(7):138-140,143.
[10] 徐辉.植物纤维增强水泥基复合材料的性能研究[D].南京:南京水利科学研究院,2006.
[11] 谭曦,苏有文.稻草纤维混凝土物理力学性能试验研究[J].混凝土与水泥制品,2016(5):86-90.
[12] 李超飞,苏有文,陈国平,等.稻草纤维混凝土性能研究[J].混凝土,2013(10):30-32,37.
[13] 廖昭印,雷劲松,陈梦婷,等.稻草纤维水泥基复合材料力学性能试验研究[J].混凝土与水泥制品,2017(7):51-54.
[14] 孙道胜,王辉,刘开伟,等.低湿度半浸泡环境下粉煤灰对砂浆试件硫酸盐侵蚀性能的影响[J].材料导报,2020,34(14):14079-14086.
[15] 曹润倬,周茗如,周群,等.超细粉煤灰对超高性能混凝土流变性、力学性能及微观结构的影响[J].材料导报,2019(16):2684-2689.
[16] 张强,李耀庄,刘保华.秸秆资源在混凝土中应用的研究进展[J].硅酸盐通报,2015,34(4):1000-1003.
[17] 苏继龙,郑书河.纤维增强复合材料中桥联纤维对裂纹的阻裂机理[J].纤维复合材料,2006,23(1):9-11.
[18] 张学元,王丹丹,张道明,等.稻草纤维轻骨料混凝土力学性能影响因素研究[J].硅酸盐通报,2019,38(5):1369-1376.
[19] 肖力光,李会生,张奇志.秸秆纤维水泥基复合材料性能的研究[J].吉林建筑工程学院学报,2005(1):1-6.
[20] 李黎,曹明莉,冯嘉琪.纤维增强水泥基复合材料的纤维混杂效应研究进展[J].应用基础与工程科学学报,2018,26(4):843-853.

上一个

钢筋混凝土框架结构与框架薄壳结构的抗震性能和CO2排放研究

下一个

CFRP编织管约束混凝土短柱轴压性能试验研究

头部文案

粉煤灰与稻草纤维复掺对混凝土力学性能的 影响

相关文件

粉煤灰与稻草纤维复掺对混凝土力学性能的影响