钢渣微粉对超高性能混凝土（UHPC）性能的影响

Effect of Steel Slag Powder on the Properties of Ultra-high Performance Concrete (UHPC)

2021年第11期

钢渣微粉；超高性能混凝土；石英粉；水胶比；工作性；抗压强度

Steel slag powder；Ultra-high performance concrete; Quartz powder; Water-binder ratio; Workability; Compressive strength

2021年第11期

10.19761/j.1000-4637.2021.11.082.04

广西创新驱动重大专项项目（桂科 AA19254030）；广西研究生教育创新计划项目（C21YJM00JZ02）。

唐咸远，郭彬，马杰灵，罗杰

桂林电子科技大学建筑与交通工程学院，广西桂林 541004

唐咸远，郭彬，马杰灵，罗杰

唐咸远,郭彬,马杰灵,等.钢渣微粉对超高性能混凝土（UHPC）性能的影响[J].混凝土与水泥制品,2021(11):82-84,89.

TANG X y,GUO B,MA J l,et al.Effect of Steel Slag Powder on the Properties of Ultra-high Performance Concrete (UHPC)[J].China Concrete and Cement Products,2021(11):82-84,89.

浏览量:

1000

摘要：研究了钢渣微粉替代石英粉对超高性能混凝土(UHPC)性能的影响。结果表明：水胶比分别为0.18、0.19的UHPC试件的28 d抗压强度均在120 MPa以上，且水胶比为0.19的UHPC的工作性更好，流动度为195 mm；钢渣微粉替代石英粉对UHPC试件的抗压强度无明显影响；在钢渣微粉掺量为100%的情况下，控制水胶比为0.20、水灰比为0.35、胶砂比为1.63时，可配制28 d抗压强度为147.5 MPa的UHPC。 Abstract: The effect of steel slag powder instead of quartz powder on the properties of ultra-high performance concrete (UHPC) was studied. The results show that the 28 d compressive strength of UHPC specimens with water-binder ratio of 0.18 and 0.19 is more than 120 MPa, and the workability of UHPC with water-binder ratio of 0.19 is better and the fluidity is 195 mm. The substitution of steel slag powder for quartz powder has no obvious effect on the compressive strength of UHPC specimens. When the content of steel slag powder is 100%, the water-binder ratio is 0.20, the water-cement ratio is 0.35 and the binder-sand ratio is 1.63, and the 28 d compressive strength of UHPC can reach 147.5 MPa.

英文名 : Effect of Steel Slag Powder on the Properties of Ultra-high Performance Concrete (UHPC)

刊期 : 2021年第11期

关键词 : 钢渣微粉；超高性能混凝土；石英粉；水胶比；工作性；抗压强度

Key words : Steel slag powder；Ultra-high performance concrete; Quartz powder; Water-binder ratio; Workability; Compressive strength

刊期 : 2021年第11期

DOI : 10.19761/j.1000-4637.2021.11.082.04

文章编号 :

基金项目 : 广西创新驱动重大专项项目（桂科 AA19254030）；广西研究生教育创新计划项目（C21YJM00JZ02）。

作者 : 唐咸远，郭彬，马杰灵，罗杰

单位 : 桂林电子科技大学建筑与交通工程学院，广西桂林 541004

唐咸远，郭彬，马杰灵，罗杰

唐咸远,郭彬,马杰灵,等.钢渣微粉对超高性能混凝土（UHPC）性能的影响[J].混凝土与水泥制品,2021(11):82-84,89.

TANG X y,GUO B,MA J l,et al.Effect of Steel Slag Powder on the Properties of Ultra-high Performance Concrete (UHPC)[J].China Concrete and Cement Products,2021(11):82-84,89.





摘要

参数

结论

参考文献

引用本文

Abstract: The effect of steel slag powder instead of quartz powder on the properties of ultra-high performance concrete (UHPC) was studied. The results show that the 28 d compressive strength of UHPC specimens with water-binder ratio of 0.18 and 0.19 is more than 120 MPa, and the workability of UHPC with water-binder ratio of 0.19 is better and the fluidity is 195 mm. The substitution of steel slag powder for quartz powder has no obvious effect on the compressive strength of UHPC specimens. When the content of steel slag powder is 100%, the water-binder ratio is 0.20, the water-cement ratio is 0.35 and the binder-sand ratio is 1.63, and the 28 d compressive strength of UHPC can reach 147.5 MPa.

扫二维码用手机看

[1] 王德辉,史才军,吴林妹.超高性能混凝土在中国的研究和应用[J].硅酸盐通报,2016(1):141-149.
[2] 陈宝春,韦建刚,苏家战,等．超高性能混凝土应用进展[J].建筑科学与工程学报,2019,36(2):10-20.
[3] 余睿,范定强,水中和,等.基于颗粒最紧密堆积理论的超高性能混凝土配合比设计[J].硅酸盐学报,2020,48(8):1145-1154.
[4] 朋改非,杨娟,石云兴,等.超高性能混凝土抗高温爆裂性能试验研究[J].建筑材料学报,2017,20(2):229-233,238.
[5] 樊俊江,於林锋.超高性能混凝土(UHPC)在装配式建筑中的应用及质量控制指标[J].混凝土与水泥制品,2020(9):1-4.
[6] 张高展,魏琦,丁庆军,等.超高性能混凝土配合比设计模型,水化硬化机理及微观结构的研究进展[J].混凝土与水泥制品,2020(1):10-14,19.
[7] GUANG Y,NGUYEN V T.Mitigation of autogenous shrinkage of ultra-high performance concrete by rice husk ash [J].Journal of the Chinese Ceramic Society,2012,40(2):212-216.
[8] 庄一舟,郑海彬,季韬,等.稻壳灰替代硅灰对超高性能混凝土性能影响的试验研究[J].混凝土与水泥制品,2012(6):10-14.
[9] KATSIOTIS N S,TSAKIRIDIS P E,VELISSARIOU D,et al.Utilization of ferronickel slag as additive in Portland cement: A hydration leaching study [J].Waste and Biomass Valorization,2015,6(2):177-189.
[10] 祁皑,刘旭宏,杨绵越,等.掺镍铁渣-矿渣复合微粉混凝土配合比设计[J].混凝土与水泥制品,2019(12):7-12.
[11] 王佳雷,肖佳,郭明磊,等.活性稻壳灰改善水泥-石灰石粉胶凝材料强度及作用机理研究[J].建筑材料学报,2020,23(5):1001-1007.
[12] 陈永亮,石磊,杜金洋,等.铁尾矿轻质保温墙体材料的制备及性能研究[J].建筑材料学报,2019,22(5):721-729.
[13] 刘云霄,李晓光,张春苗,等.铁尾矿砂水泥基灌浆料性能研究[J].建筑材料学报,2019,22(4):538-544.
[14] 王茹,王高勇,张韬,等.稻壳灰在丁苯聚合物/水泥复合胶凝材料凝结硬化过程中的作用[J].硅酸盐学报,2017,45(2)190-195.
[15] 侯贵华,许仲梓.稻壳制备高性能材料研究进展[J].硅酸盐学报,2006(2):204-209.
[16] 汪知文,李碧雄.稻壳灰应用于水泥混凝土的研究进展[J].材料导报,2020,34(9):9003-9011.
[17] 陆海飞,田伟光,徐佳林,等.红土镍矿冶炼镍铁废渣综合利用的研究进展[J].材料导报,2018,32(S2):444-448.
[18] 李灿华,仇金辉,向晓东,等.道路用钢渣标准体系的构建与展望[J].钢铁研究,2016,44(3):57-62.
[19] 明阳,李顺凯,沈尔卜,等.低水化热低收缩超高性能混凝土(UHPC)试验研究[J].混凝土与水泥制品,2019(3):6-9.
[20] 祖庆贺,臧军,沈晓冬.粗粒度区间钢渣微粉在UHPC中的应用研究[J].混凝土与水泥制品,2019(8):1-3.

上一个

利用脱硫石膏浆液制备高强水泥基自流平砂浆的应用研究

下一个

橡胶改性泡沫混凝土的物理力学性能及耐高温性能研究

头部文案

钢渣微粉对超高性能混凝土（UHPC）性能的 影响

相关文件

钢渣微粉对超高性能混凝土（UHPC）性能的影响