利用脱硫石膏浆液制备高强水泥基自流平砂浆的应用研究
Rescarch on Application of Preparation of High Strength Cement-based Self-leveling Mortar with Desulfurization Gypsum Slurry
2021年第11期
石灰石-石膏湿法脱硫工艺;脱硫石膏浆液;自流平砂浆;强度;耐磨性;收缩率
Limestone-gypsum wet desulfurization process; Desulfurization gypsum slurry; Self- leveling mortar; Strength; Wear resistance; Shrinkage
2021年第11期
10.19761/j.1000-4637.2021.11.085.05
江苏省生态建材与环保装备协同创新中心项目(CP201506)。
徐风广,杨凤玲,侯海军,陈小卫
盐城工学院 材料科学与工程学院,江苏 盐城 224051

徐风广,杨凤玲,侯海军,陈小卫

徐风广,杨凤玲,侯海军,等.利用脱硫石膏浆液制备高强水泥基自流平砂浆的应用研究[J].混凝土与水泥制品,2021(11):85-89.

XU Feng-guang, YANG Feng-ling, HOU Hai-jun,et al.Rescarch on Application of Preparation of High Strength Cement-based Self-leveling Mortar with Desulfurization Gypsum Slurry[J].China Concrete and Cement Products,2021(11):85-89.

浏览量:
1000
摘   要:以铝酸盐水泥为主要胶凝材料,掺入脱硫石膏浆液和普通硅酸盐水泥,制备了地面用水泥基自流平砂浆,通过宏观性能测试(强度、耐磨性和尺寸变化率)和XRD分析,研究了脱硫石膏浆液对水泥基自流平砂浆性能的影响。结果表明:当铝酸盐水泥掺量为30.3%~36.9%、脱硫石膏浆液掺量为18%~28%、普通硅酸盐水泥掺量为5.3%~6.0%、河砂掺量为35%~39%时,制备的水泥基自流平砂浆具有强度高、耐磨性好和收缩率低的特点;脱硫石膏浆液能促进基体中早期AFt的生成,保证后期AFt的生成量,从而提高脱硫石膏浆液水泥基自流平砂浆的强度。 Abstract: The cement-based self-leveling mortar for ground was prepared by using aluminate cement as main cementitious material, adding desulfurization gypsum slurry and ordinary portland cement. The influence of desulfurization gypsum slurry on the properties of cement-based self-leveling mortar was studied by macro performance tests (strength, wear resistance and dimensional change rate) and XRD analysis. The results show that the cement-based self-leveling mortar has the characteristics of high strength, good wear resistance and low shrinkage when the content of aluminate cement is 30.3%~36.9%, the content of desulfurization gypsum slurry is 18%~28%, the content of ordinary portland cement is 5.3%~6.0%, and the content of river sand is 35%~39%. The desulfurized gypsum slurry can promote the formation of early AFt in the matrix and ensure the generation of AFt in the later period, thereby improving the strength of the cement-based self-leveling mortar of the desulfurized gypsum slurry.
英文名 : Rescarch on Application of Preparation of High Strength Cement-based Self-leveling Mortar with Desulfurization Gypsum Slurry
刊期 : 2021年第11期
关键词 : 石灰石-石膏湿法脱硫工艺;脱硫石膏浆液;自流平砂浆;强度;耐磨性;收缩率
Key words : Limestone-gypsum wet desulfurization process; Desulfurization gypsum slurry; Self- leveling mortar; Strength; Wear resistance; Shrinkage
刊期 : 2021年第11期
DOI : 10.19761/j.1000-4637.2021.11.085.05
文章编号 :
基金项目 : 江苏省生态建材与环保装备协同创新中心项目(CP201506)。
作者 : 徐风广,杨凤玲,侯海军,陈小卫
单位 : 盐城工学院 材料科学与工程学院,江苏 盐城 224051

徐风广,杨凤玲,侯海军,陈小卫

徐风广,杨凤玲,侯海军,等.利用脱硫石膏浆液制备高强水泥基自流平砂浆的应用研究[J].混凝土与水泥制品,2021(11):85-89.

XU Feng-guang, YANG Feng-ling, HOU Hai-jun,et al.Rescarch on Application of Preparation of High Strength Cement-based Self-leveling Mortar with Desulfurization Gypsum Slurry[J].China Concrete and Cement Products,2021(11):85-89.

摘要
参数
结论
参考文献
引用本文

摘   要:以铝酸盐水泥为主要胶凝材料,掺入脱硫石膏浆液和普通硅酸盐水泥,制备了地面用水泥基自流平砂浆,通过宏观性能测试(强度、耐磨性和尺寸变化率)和XRD分析,研究了脱硫石膏浆液对水泥基自流平砂浆性能的影响。结果表明:当铝酸盐水泥掺量为30.3%~36.9%、脱硫石膏浆液掺量为18%~28%、普通硅酸盐水泥掺量为5.3%~6.0%、河砂掺量为35%~39%时,制备的水泥基自流平砂浆具有强度高、耐磨性好和收缩率低的特点;脱硫石膏浆液能促进基体中早期AFt的生成,保证后期AFt的生成量,从而提高脱硫石膏浆液水泥基自流平砂浆的强度。

Abstract: The cement-based self-leveling mortar for ground was prepared by using aluminate cement as main cementitious material, adding desulfurization gypsum slurry and ordinary portland cement. The influence of desulfurization gypsum slurry on the properties of cement-based self-leveling mortar was studied by macro performance tests (strength, wear resistance and dimensional change rate) and XRD analysis. The results show that the cement-based self-leveling mortar has the characteristics of high strength, good wear resistance and low shrinkage when the content of aluminate cement is 30.3%~36.9%, the content of desulfurization gypsum slurry is 18%~28%, the content of ordinary portland cement is 5.3%~6.0%, and the content of river sand is 35%~39%. The desulfurized gypsum slurry can promote the formation of early AFt in the matrix and ensure the generation of AFt in the later period, thereby improving the strength of the cement-based self-leveling mortar of the desulfurized gypsum slurry.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1) 脱硫石膏浆液水泥基自流平砂浆的最佳配合比为:铝酸盐水泥掺量为30.3%~36.9%、脱硫石膏浆液掺量为18%~28%、普通硅酸盐水泥掺量为5.3%~6.0%、河砂掺量为35%~39%。
(2)脱硫石膏浆液能够增强水泥基自流平砂浆强度和耐磨性,降低收缩率和生产成本。
(3)脱硫石膏浆液中的石膏颗粒较一般脱硫石膏中的粉体颗粒更细,在水中的溶解速度更快,有利于促进水泥早期水化产物AFt的生成,保证后期AFt的生成量。

[1] KOUJI O,THOMAS A.Investigation into relations among technological properties, hydration kinetics and early age hydration of self-leveling underlayments[J].Cement and Concrete Research,2010(40):1034-1040.

[2] 耿春女,钱华,李小平,等.脱硫石膏农业利用进展与展望[J].环境污染治理技术与设备,2006,7(12):15-19.
[3] 张瑶,任耘,刘佰龙,等.烧结脱硫石膏的综合利用现状[J].硅酸盐通报,2015,34(12):3563-3570.
[4] 尤彩霞,袁李军,孙娜,等.电厂脱硫石膏制水泥缓凝剂二水石膏的研究[J].无机盐工业,2019(12):71-74.
[5] 郭大江,袁运法,胡浩然,等.脱硫石膏性能研究及其在普通硅酸盐水泥中的应用[J].硅酸盐通报,2010,29(2):357-360.
[6] 沈建生,徐亦冬,游伟国.脱硫石膏钢渣无熟料水泥对软土固化效果的研究[J].硅酸盐通报,2018,37(12):3888-3891.
[7] 贺坤,李小平,徐晨,等.烟气脱硫石膏对滨海盐渍土的改良效果[J].环境科学研究,2018,31(3):547-554.
[8] 刘小杰,李建鹏,吕庆,等.脱硫石膏综合利用的现状与展望[J].化工环保,2017,37(6):611-615.
[9] 彭明强,叶蓓红.脱硫石膏用于自流平砂浆的研究[J].建筑材料学报,2012(3):406-409,421.
[10] 黄天勇,陈旭峰,章银祥,等.分级铁尾矿砂对石膏基自流平砂浆性能的影响[J].混凝土与水泥制品,2018(7):91-94,100.
[11] 何玉鑫,瞿县,华苏东,等.工业副产品石膏自流平材料的研究进展[J].材料导报,2014,28(5):345-347.
[12] 吴金明,唐凯靖.脱硫石膏基自流平砂浆耐水性改善及机理研究[J].非金属矿,2018,41(4):43-45.
[13] 娄有信,杨子,徐惠国.高强脱硫石膏砌块的制备及微观结构研究[J].辽宁师范大学学报,2019,42(1):83-87.
[14] 李静静.硅灰对石膏基自流平砂浆性能的影响研究[J].混凝土与水泥制品,2020(5):80-82.
[15] 吴金明,唐凯靖.纤维素醚与脱硫石膏基自流平砂浆相容性试验研究[J].混凝土与水泥制品,2018(11):79-82.
[16] 沈威.水泥工艺学[M].武汉:武汉工业大学出版社,2013.
[17] 王培铭,孙磊,徐玲玲.硅酸盐水泥与铝酸盐水泥混合体系的研究和应用[J].材料导报,2013,27(1):139-143.
[18] 杨峰,李英丁,蒋勇.石膏和高铝水泥对自流平砂浆性能的影响[J].非金属矿,2018,41(6):48-50.
[19] 黄天勇,章银祥,陈旭峰.石膏掺量对三元胶凝体系水泥基自流平砂浆的影响[J].硅酸盐通报,2019,38(6):1738-1742.
[20] 丁汝茜,高礼雄,姚燕,等.二水石膏和普通水泥复掺对铝酸盐水泥基砂浆性能的影响[J].混凝土与水泥制品,2018(1):11-16.

徐风广,杨凤玲,侯海军,.利用脱硫石膏浆液制备高强水泥基自流平砂浆的应用研究[J].混凝土与水泥制品,2021(11):85-89.

XU Feng-guang, YANG Feng-ling, HOU Hai-jun,et al.Rescarch on Application of Preparation of High Strength Cement-based Self-leveling Mortar with Desulfurization Gypsum Slurry[J].China Concrete and Cement Products,2021(11):85-89.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州