轻质碱渣-氯氧镁水泥基材料性能研究及孔结构特征分析

Experimental Study on Properties and Pore Structure Characteristics of Light Alkali Residue-magnesium Oxychloride Cement-based Materials

2022年第4期

碱渣；氯氧镁水泥；力学性能；导热系数；耐水性；孔结构

Alkali residue; Magnesium oxychloride cement; Mechanical property; Thermal conductivity; Water resistance; Pore structure

2022年第4期

10.19761/j.1000-4637.2022.04.078.06

“十三五”科技支撑计划项目（2018YFD1101002-03）。

余海燕，胡林童

天津城建大学材料科学与工程学院，天津 300384

余海燕，胡林童

余海燕,胡林童.轻质碱渣-氯氧镁水泥基材料性能研究及孔结构特征分析[J].混凝土与水泥制品,2022(4):78-83.

YU H Y,HU L T.Experimental Study on Properties and Pore Structure Characteristics of Light Alkali Residue-magnesium Oxychloride Cement-based Materials[J].China Concrete and Cement Products,2022(4):78-83.

浏览量:

1000

摘要：以碱渣、MgO、MgSO4·7H2O等为主要原材料，制备了轻质碱渣-氯氧镁水泥基材料，研究了养护温度、发泡剂掺量、稳泡剂掺量对轻质碱渣-氯氧镁水泥基材料性能的影响，并对其孔结构进行了分析。结果表明：当养护温度为60 ℃、发泡剂掺量为5%、稳泡剂掺量为6%时，轻质碱渣-氯氧镁水泥基材料的各项性能最优，干密度为597 kg/m3、抗压强度为2.7 MPa、导热系数为0.21 W/（m·K）、吸水率为15.1%、软化系数为0.83、28 d收缩率为0.17%。 Abstract: Light alkali residue-magnesium oxychloride cement-based materials were prepared with alkali residue, magnesium oxide and magnesium sulfate heptahydrate as the main raw materials. The effects of curing temperature, foaming agent content and foam stabilizer content on the properties of light alkali residue-magnesium oxychloride cement-based materials were studied, and the pore structure was analyzed. The results show that when the curing temperature is 60 ℃, the content of foaming agent is 5% and the content of foam stabilizer is 6%, the properties of light alkali residue-magnesium oxychloride cement-based materials are the best, with dry density of 597 kg/m3, compressive strength of 2.7 MPa, thermal conductivity of 0.21 W/（m·K）, water absorption of 15.1%, softening coefficient of 0.83 and 28 d shrinkage rate of 0.17%.

英文名 : Experimental Study on Properties and Pore Structure Characteristics of Light Alkali Residue-magnesium Oxychloride Cement-based Materials

刊期 : 2022年第4期

关键词 : 碱渣；氯氧镁水泥；力学性能；导热系数；耐水性；孔结构

Key words : Alkali residue; Magnesium oxychloride cement; Mechanical property; Thermal conductivity; Water resistance; Pore structure

刊期 : 2022年第4期

DOI : 10.19761/j.1000-4637.2022.04.078.06

文章编号 :

基金项目 : “十三五”科技支撑计划项目（2018YFD1101002-03）。

作者 : 余海燕，胡林童

单位 : 天津城建大学材料科学与工程学院，天津 300384

余海燕，胡林童

余海燕,胡林童.轻质碱渣-氯氧镁水泥基材料性能研究及孔结构特征分析[J].混凝土与水泥制品,2022(4):78-83.





摘要

参数

结论

参考文献

引用本文

摘要：以碱渣、MgO、MgSO₄·7H₂O等为主要原材料，制备了轻质碱渣-氯氧镁水泥基材料，研究了养护温度、发泡剂掺量、稳泡剂掺量对轻质碱渣-氯氧镁水泥基材料性能的影响，并对其孔结构进行了分析。结果表明：当养护温度为60 ℃、发泡剂掺量为5%、稳泡剂掺量为6%时，轻质碱渣-氯氧镁水泥基材料的各项性能最优，干密度为597 kg/m³、抗压强度为2.7 MPa、导热系数为0.21 W/（m·K）、吸水率为15.1%、软化系数为0.83、28 d收缩率为0.17%。

Abstract: Light alkali residue-magnesium oxychloride cement-based materials were prepared with alkali residue, magnesium oxide and magnesium sulfate heptahydrate as the main raw materials. The effects of curing temperature, foaming agent content and foam stabilizer content on the properties of light alkali residue-magnesium oxychloride cement-based materials were studied, and the pore structure was analyzed. The results show that when the curing temperature is 60 ℃, the content of foaming agent is 5% and the content of foam stabilizer is 6%, the properties of light alkali residue-magnesium oxychloride cement-based materials are the best, with dry density of 597 kg/m³, compressive strength of 2.7 MPa, thermal conductivity of 0.21 W/（m·K）, water absorption of 15.1%, softening coefficient of 0.83 and 28 d shrinkage rate of 0.17%.

扫二维码用手机看

[1] 刘大成,李悦,刘艳娟,等.氨碱法制纯碱废渣制备免烧砖[J].环境工程学报,2016,10(6):3249-3254.
[2] 刘春原,赵献辉,赵越,等.C-S-H凝胶对掺元明粉碱渣拌合土性能的影响[J].土木工程学报,2015(S2):341-345.
[3] 刘春原,赵献辉,朱楠,等.粉煤灰基地质聚合物力学性能及碱渣改性机理[J].硅酸盐通报,2017,36(2):679-685,691.
[4] 张惠灵,徐克猛,陈永亮,等.利用建筑垃圾和碱渣制备蒸压加气混凝土[J].环境工程学报,2019,13(2):441-448.
[5] 马加骁,张鹏,白晓宇,等.碱渣土地基承载性能试验[J].科学技术与工程,2019,19(30):303-309.
[6] ZHAO X H,LIU C Y,WANG L,et al.Physical and Mechanical Properties and Micro Characteristics of Fly Ash-based Geopolymers Incorporating Soda Residue[J].Cement and Concrete Composites,2019:125-136.
[7] 侯贵华.碱渣烧制白色水泥适宜煅烧温度的研究[J].化工矿物与加工,2002(6):17-19.
[8] 杨医博,普永强,严卫军,等.碱渣用作砂浆保水剂的试验研究[J].材料导报,2017,31(20):114-118.
[9] 马加骁,闫楠,白晓宇,等.不同物态配比碱渣-粉煤灰混合料强度特性[J].岩土工程学报,2021,43(5):893-900.
[10] HE J,WANG X Q,SU Y,et al.Shear Strength of Stabilized Clay Treated with Soda Residue and Ground Granulated Blast Furnace Slag[J].Journal of Materials in Civil Engineering,2019,31(3):06018029.
[11] ZHA F S,LIU C M,KANG B,et al.Acid Rain Leaching Behavior of Zn-contaminated Soils Solidified/Stabilized Using Cement-soda Residue [J].Chemosphere,2021,281:130916.
[12] 胡林童.碱渣-氯氧镁水泥制品的制备及其性能研究[D].天津:天津城建大学,2021.
[13] 中华人民共和国住房和城乡建设部.泡沫混凝土:JG/T 266—2011[S].北京:中国标准出版社,2011.
[14] 中华人民共和国工业和信息化部.泡沫混凝土制品性能试验方法:JC/T 2357—2016[S].北京:建材工业出版社,2016.
[15] 中华人民共和国住房和城乡建设部.建筑砂浆基本性能试验方法标准:JGJ/T 70—2009[S].北京:中国建筑工业出版社,2009.
[16] 马秋.发泡氯氧镁胶凝材料的发泡体系及改性研究[D]. 津:河北工业大学,2018.
[17] 郑卫新.氯氧镁水泥泡沫混凝土设计与应用基础研究[D].北京:中国科学院大学,2019.
[18] 祁非,张长森.外加剂对氯氧镁发泡水泥的性能的影响[J].建筑节能,2017(1):69-72.
[19] 习雨同.泡沫混凝土气孔结构与性能研究[D].南京:南京航天航空大学,2016.
[20] 朱明,王方刚,张旭龙,等.泡沫混凝土孔结构与导热性能的关系研究[J].武汉理工大学学报,2013,35(3):20-25.
[21] 宋学锋,杨萍.泡沫掺量对发泡碱激发矿渣聚合物性能和孔隙特征的影响[J].硅酸盐通报,2017,36(3):905-909.

上一个

《混凝土与水泥制品》热点专题征稿启事

下一个

基于Weibull分布的再生混凝土中钢筋锈蚀预测

头部文案

轻质碱渣-氯氧镁水泥基材料性能研究及孔结构特征分析

相关文件