单侧压对冻融混凝土劈拉损伤特性的影响
Influence of Unilateral Pressure on the Split Tensile Damage Characteristics of Freeze-thaw Deteriorated Concrete
2022年第6期
混凝土;单侧压;冻融循环;劈拉强度;声发射;损伤
Concrete; Unilateral pressure; Freeze-thaw cycle; Split tensile strength; Acoustic emission; Damage
2022年第6期
10.19761/j.1000-4637.2022.06.021.06
国家自然科学基金项目(51579139、51709155、52079072)。
李文博a,b,王乾峰a,b,彭 刚a,b,赵 茗a,b,程卓群a,b
三峡大学 a.土木与建筑学院;b.三峡库区地质灾害教育部重点实验室,湖北 宜昌 443002

李文博a,b,王乾峰a,b,彭 刚a,b,赵 茗a,b,程卓群a,b

李文博,王乾峰,彭刚,等.单侧压对冻融混凝土劈拉损伤特性的影响[J].混凝土与水泥制品,2022(6):21-26.

LI W B,WANG Q F,PENG G,et al.Influence of Unilateral Pressure on the Split Tensile Damage Characteristics of Freeze-thaw Deteriorated Concrete[J].China Concrete and Cement Products,2022(6):21-26.

浏览量:
1000
摘   要:对冻融混凝土进行了不同单侧压下的劈拉试验,分析了冻融循环次数和单侧压对混凝土劈拉性能的影响,并结合声发射技术研究了混凝土在劈拉过程中的损伤发展,建立了混凝土损伤演化方程。结果表明:随着冻融循环次数的增加,混凝土冻融劣化程度加深,峰值应力明显降低;相同冻融循环次数下,单侧压越大,混凝土的峰值应力越大;经历冻融循环后的混凝土损伤发展速度加快,单侧压的存在对混凝土的损伤发展起到延阻作用;考虑冻融循环次数和单侧压作用的混凝土劈拉损伤演化曲线均可分为损伤初始发展阶段、损伤稳定发展阶段和损伤快速发展阶段。 Abstract: The split tensile test of freeze-thaw concrete under different unilateral compression was carried out. The influence of the number of freeze-thaw cycles and unilateral compression on the split tensile performance of concrete was analyzed, and the damage of concrete during the split tensile process was studied by acoustic emission technology. The concrete damage evolution formula was established. The results show that as the number of freeze-thaw cycles increases, the degree of freeze-thaw degradation of concrete deepens, and the peak stress decreases significantly. Under the same number of freeze-thaw cycles, the greater the unilateral pressure, the greater the peak stress of concrete. The development speed of concrete damage after the freeze-thaw cycles is accelerated, and the existence of unilateral pressure has an effect of extending resistance on concrete damage. The split tensile damage evolution curve of concrete considering the number of freeze-thaw cycles and unilateral pressure can be divided into initial damage development stage, stable damage development stage, and rapid damage development stage.
英文名 : Influence of Unilateral Pressure on the Split Tensile Damage Characteristics of Freeze-thaw Deteriorated Concrete
刊期 : 2022年第6期
关键词 : 混凝土;单侧压;冻融循环;劈拉强度;声发射;损伤
Key words : Concrete; Unilateral pressure; Freeze-thaw cycle; Split tensile strength; Acoustic emission; Damage
刊期 : 2022年第6期
DOI : 10.19761/j.1000-4637.2022.06.021.06
文章编号 :
基金项目 : 国家自然科学基金项目(51579139、51709155、52079072)。
作者 : 李文博a,b,王乾峰a,b,彭 刚a,b,赵 茗a,b,程卓群a,b
单位 : 三峡大学 a.土木与建筑学院;b.三峡库区地质灾害教育部重点实验室,湖北 宜昌 443002

李文博a,b,王乾峰a,b,彭 刚a,b,赵 茗a,b,程卓群a,b

李文博,王乾峰,彭刚,等.单侧压对冻融混凝土劈拉损伤特性的影响[J].混凝土与水泥制品,2022(6):21-26.

LI W B,WANG Q F,PENG G,et al.Influence of Unilateral Pressure on the Split Tensile Damage Characteristics of Freeze-thaw Deteriorated Concrete[J].China Concrete and Cement Products,2022(6):21-26.

摘要
参数
结论
参考文献
引用本文

摘   要:对冻融混凝土进行了不同单侧压下的劈拉试验,分析了冻融循环次数和单侧压对混凝土劈拉性能的影响,并结合声发射技术研究了混凝土在劈拉过程中的损伤发展,建立了混凝土损伤演化方程。结果表明:随着冻融循环次数的增加,混凝土冻融劣化程度加深,峰值应力明显降低;相同冻融循环次数下,单侧压越大,混凝土的峰值应力越大;经历冻融循环后的混凝土损伤发展速度加快,单侧压的存在对混凝土的损伤发展起到延阻作用;考虑冻融循环次数和单侧压作用的混凝土劈拉损伤演化曲线均可分为损伤初始发展阶段、损伤稳定发展阶段和损伤快速发展阶段。

Abstract: The split tensile test of freeze-thaw concrete under different unilateral compression was carried out. The influence of the number of freeze-thaw cycles and unilateral compression on the split tensile performance of concrete was analyzed, and the damage of concrete during the split tensile process was studied by acoustic emission technology. The concrete damage evolution formula was established. The results show that as the number of freeze-thaw cycles increases, the degree of freeze-thaw degradation of concrete deepens, and the peak stress decreases significantly. Under the same number of freeze-thaw cycles, the greater the unilateral pressure, the greater the peak stress of concrete. The development speed of concrete damage after the freeze-thaw cycles is accelerated, and the existence of unilateral pressure has an effect of extending resistance on concrete damage. The split tensile damage evolution curve of concrete considering the number of freeze-thaw cycles and unilateral pressure can be divided into initial damage development stage, stable damage development stage, and rapid damage development stage.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)随着冻融循环次数的增加,混凝土的冻融劣化程度加深,峰值应力出现明显下降趋势;相同冻融循环次数下,随着单侧压的增大,峰值应力呈现出增大的趋势。
(2)20次冻融循环后,有单侧压作用时,混凝土在劈拉过程中达到声发射能量最大值所需要的时间明显减小,经历冻融循环作用后的混凝土损伤发展速度加快;单侧压的存在对混凝土损伤发展起到一定的延阻作用。
(3)考虑冻融循环次数和单侧压作用的混凝土劈拉损伤演化曲线均可分为三个阶段:损伤初始发展阶段、损伤稳定发展阶段、损伤快速发展阶段。
(4)本文将声发射技术用于混凝土的损伤研究,建立了损伤值D与应力水平、声发射能量水平关系的表达式,拟合相关系数均较高,该方法可用于混凝土结构的损伤评价、损伤检测和可靠性预报。

[1] HASAN M,OKUYAMA H,SATO Y,et al.Stress-strain Model of Concrete Damaged by Freezing and Thawing Cycles[J].Journal of Advanced Concrete Technology,2004,2(1):89-99.
[2] 李金玉,曹建国,许文雨,等.混凝土冻融破坏机理的研究[J].水利学报,1999(1):41-49. 
[3] 候春平,陈灯红,彭刚,等.冻融劣化混凝土冰冻状态动态轴压本构特征研究[J].实验力学,2020,35(6):1101-1112. 
[4] 覃丽坤,宋玉普,姚家伟.普通混凝土在冻融循环后的力学性能研究[J].大连民族学院学报,2010,12(3):236-238. 
[5] 商怀帅,宋玉普,覃丽坤,等.冻融循环后在三向受压荷载下混凝土性能的试验研究[J].水利学报,2006(7):874-879.
[6] 宋玉普,徐秀娟,刘浩.冻融循环后全级配混凝土及其湿筛混凝土的力学性能比较[J].水利学报,2012(1):69-75. 
[7] 覃丽坤,宋玉普,陈浩然,等.双轴拉压混凝土在冻融循环后的力学性能及破坏准则[J].岩石力学与工程学报,2005(10):1740-1745. 
[8] 王立成.不同种类混凝土冻融循环后双轴压压统一强度准则[J].水电能源科学,2012(1):159-161. 
[9] 周雁玲,曹大富,葛文杰,等.冻融循环对完全碳化混凝土轴拉性能的影响[J].混凝土与水泥制品,2021(6):1-7.
[10] 濮琦,薛万银,蒋林华,等.冻融循环作用下混凝土断裂损伤特性研究[J].混凝土与水泥制品,2020(7):30-33.
[11] 苏捷,方志,杨钻.混凝土单轴受压性能尺寸效应的试验研究[J].工业建筑,2012,42(6):122-126. 
[12] 操佩,彭刚,柳琪,等.冻融劣化混凝土的单轴动态力学特性研究[J].水利水电技术,2016,47(12):105-110. 
[13] 徐童淋,彭刚,杨乃鑫,等.混凝土冻融劣化后动态单轴抗压特性试验研究[J].水利水运工程学报,2017(6):69-78. 
[14] 吴聪,彭刚.冻融劣化混凝土动态轴压弹塑性损伤研究[J].西安理工大学学报,2019,35(1):102-108. 
[15] 刘博文,彭刚,王孝政,等.不同冻融循环次数混凝土单轴压缩试验[J].水利水运工程学报,2017(1):32-36.
[16] 彭刚,王乾峰,陈灯红,等.基于声发射参数的混凝土循环加卸载动态损伤破坏特性研究[J].三峡大学学报(自然科学版),2015,37(6):1-9. 
[17] 彭竹君,肖洋,王乾峰,等.基于声发射技术的冻融劣化混凝土单双轴动态抗压试验[J].水电能源科学,2019,37(2):131-134. 
[18] 黄超,彭刚,肖洋,等.冻融混凝土基于声发射技术的单轴动态劈拉损伤特性研究[J].水利水电技术,2018,49(6):198-203. 
[19] 中华人民共和国住房和城乡建设部.普通混凝土长期性能和耐久性能试验方法标准:GB/T 50082—2009[S].北京:中国标准出版社,2012. 
[20] 贺誉.混凝土劈拉特性的率效应研究[D].宜昌:三峡大学,2014. 
[21] 纪洪广,张天森,蔡美峰,等.混凝土材料损伤的声发射动态检测试验研究[J].岩石力学与工程学报,2000(2):165-168. 
[22] 吴彬,胡伟华,文沛军.应力空间下基于区间搜索法的混凝土动态损伤临界点确定[J].长江科学院院报,2017,34(3):130-133.

李文博,王乾峰,彭刚,.单侧压对冻融混凝土劈拉损伤特性的影响[J].混凝土与水泥制品,2022(6):21-26.

LI W B,WANG Q F,PENG G,et al.Influence of Unilateral Pressure on the Split Tensile Damage Characteristics of Freeze-thaw Deteriorated Concrete[J].China Concrete and Cement Products,2022(6):21-26.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州