碱化稻草纤维对尾砂充填体力学性能的影响

Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill

2022年第7期

尾砂充填体；稻草纤维；碱化处理；抗压强度；微观分析

Tailings backfill; Straw fiber; Alkalization treatment; Compressive strength; Microscopic analysis

2022年第7期

10.19761/j.1000-4637.2022.07.060.04

市校（院所）科技合作项目-市属高校产学研项目（2019-SG-17）。

张竞，李骏

福州理工学院应用科学与工程学院，福建福州 350000

张竞，李骏

张竞,李骏.碱化稻草纤维对尾砂充填体力学性能的影响[J].混凝土与水泥制品,2022(7):60-63.

ZHANG J,LI J.Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill[J].China Concrete and Cement Products,2022(7):60-63.

浏览量:

1000

摘要：将经过浓度为4%的NaOH溶液碱化处理过的稻草纤维作为加筋材料用于尾砂充填体试件的制备，研究了灰砂比、碱化稻草纤维的长度和掺量对尾砂充填体试件抗压强度的影响，并借助扫描电镜（SEM）从微观角度分析了碱化稻草纤维的作用机理。结果表明：随着碱化稻草纤维掺量的增加，试件的抗压强度下降；随着碱化稻草纤维长度的增加，试件的抗压强度先增大后减小；未碱化稻草纤维对试件抗压强度的降低程度显著大于碱化稻草纤维；随着灰砂比的减小，试件的抗压强度降低。 Abstract: The straw fiber alkalized by 4% NaOH solution was used as reinforcement material for the preparation of tailings backfill specimens. The effects of cement-sand ratio, length and content of alkalized straw fiber on the compressive strength of tailings backfill specimens were studied, and the action mechanism of alkalized straw fiber was analyzed by SEM. The results show that the compressive strength of the specimen decreases with the increase of the alkalized straw fiber content. With the increase of the length of alkalized straw fiber, the compressive strength of the specimen first increases and then decreases. The reduction degree of the compressive strength of the specimen by the non-alkalized straw fiber is significantly greater than that of the alkalized straw fiber. With the decrease of cement sand ratio, the compressive strength of the specimen decreases.

英文名 : Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill

刊期 : 2022年第7期

关键词 : 尾砂充填体；稻草纤维；碱化处理；抗压强度；微观分析

Key words : Tailings backfill; Straw fiber; Alkalization treatment; Compressive strength; Microscopic analysis

刊期 : 2022年第7期

DOI : 10.19761/j.1000-4637.2022.07.060.04

文章编号 :

基金项目 : 市校（院所）科技合作项目-市属高校产学研项目（2019-SG-17）。

作者 : 张竞，李骏

单位 : 福州理工学院应用科学与工程学院，福建福州 350000

张竞，李骏

张竞,李骏.碱化稻草纤维对尾砂充填体力学性能的影响[J].混凝土与水泥制品,2022(7):60-63.

ZHANG J,LI J.Effect of Alkalized Straw Fiber on Mechanical Properties of Tailings Backfill[J].China Concrete and Cement Products,2022(7):60-63.





摘要

参数

结论

参考文献

引用本文

Abstract: The straw fiber alkalized by 4% NaOH solution was used as reinforcement material for the preparation of tailings backfill specimens. The effects of cement-sand ratio, length and content of alkalized straw fiber on the compressive strength of tailings backfill specimens were studied, and the action mechanism of alkalized straw fiber was analyzed by SEM. The results show that the compressive strength of the specimen decreases with the increase of the alkalized straw fiber content. With the increase of the length of alkalized straw fiber, the compressive strength of the specimen first increases and then decreases. The reduction degree of the compressive strength of the specimen by the non-alkalized straw fiber is significantly greater than that of the alkalized straw fiber. With the decrease of cement sand ratio, the compressive strength of the specimen decreases.

扫二维码用手机看

[1] 王昆,杨鹏,KAREN H E,等.尾矿库溃坝灾害防控现状及发展[J].工程科学学报,2018(5):526-539.
[2] 张海波,宋卫东,许英霞.充填采矿技术应用发展及存在问题研究[J].黄金,2010,31(1):23-25.
[3] 徐文彬,李乾龙,田明明.聚丙烯纤维加筋固化尾砂强度及变形特性[J].工程科学学报,2019(12):1618-1626.
[4] ROMUALDI J P,MANDEL J A.Tensile Strength of Concrete Affected by Uniformly Distributed and Closely Spaced Short Lengths of Wire Reinforcement[J].ACI Materials Journal,1964,61(6):657-672.
[5] 喻智,史秀志,陈新,等.用于研究纤维尾砂胶结充填材料单轴压缩性能的新型人工智能模型(英文)[J].Transactions of Nonferrous Metals Society of China,2021(4):1087-1102.
[6] 薛改利.掺纤维尾砂充填体多尺度力学特性及损伤演化机理研究[D].北京:北京科技大学,2020.
[7] 孙位,刘长武,吴帆,等.聚丙烯纤维高水材料力学性能的试验研究[J].金属矿山,2018(1):53-57.
[8] 马国伟,李之建,易夏玮,等.纤维增强膏体充填材料的宏细观试验[J].北京工业大学学报,2016(3):406-412.
[9] 赵康,宋宇峰,于祥,等.不同纤维作用下尾砂胶结充填体早期力学特性及损伤本构模型研究[J].岩石力学与工程学报,2022,41(2):282-291.
[10] 杨凯.稻草纤维粉末混凝土空心砌块的力学及热工性能研究[D].绵阳:西南科技大学,2016.
[11] 张学元,王丹丹,张道明,等.稻草纤维轻骨料混凝土力学性能影响因素研究[J].硅酸盐通报,2019,38(5):1369-1376.
[12] 王明江.稻壳/稻草纤维水泥基材料的制备与性能[D].哈尔滨:哈尔滨工业大学,2012.
[13] 宁淑嫔.夹心秸秆混凝土砌块导热及力学性能研究[D].长春:吉林建筑大学,2020.
[14] 尹如霞.稻草纤维微粒水泥基复合材料抗冲击性能试验研究[D].绵阳:西南科技大学,2019.
[15] 宋学朋.碱化水稻秸秆基尾砂胶结充填体动静力学性能演化机制研究[D].赣州:江西理工大学,2021.
[16] 李艺,赵文.混杂纤维混凝土阻裂增韧及耐久性能[M].北京:科学出版社,2012.

上一个

添加纤维材料的混凝土预制复合墙体应用分析

下一个

玄武岩纤维混凝土动态力学性能及数值模拟

头部文案

碱化稻草纤维对尾砂充填体力学性能的影响

相关文件