粉煤灰对再生混凝土抗硫酸盐侵蚀及界面过渡区微观特性的影响
The Influence of Fly Ash on Resistance to Sulphate Erosion and the Microstructure of Interfacial Transition Zone of Recycled Con
２０19年第5期
再生混凝土；粉煤灰；抗硫酸盐侵蚀；界面过渡区；微观形貌
Regenerated concrete; Fly ash; Resistance to sulphate erosion; Interface transition zone; Micromorphology
２０19年第5期
10.19761/j.1000-4637.2019.05.092.05
朱晓云1，孙国卿2
1.天津交通职业学院，300110；2. 天津大学仁爱学院，301636

朱晓云1，孙国卿2

朱晓云,孙国卿.粉煤灰对再生混凝土抗硫酸盐侵蚀及界面过渡区微观特性的影响[J].混凝土与水泥制品,2019(5):92-96.

ZHU X Y,SUN G Q.The Influence of Fly Ash on Resistance to Sulphate Erosion and the Microstructure of Interfacial Transition Zone of Recycled Concrete[J].China Concrete and Cement Products,2019(5):92-96.

浏览量:
1000
摘 要：为了探究硫酸盐侵蚀作用下粉煤灰再生混凝土性能的变化，测试了材料配比对混凝土抗压耐蚀系数和质量损失率的影响，得到合理的材料组成，并通过SEM观察再生混凝土中老骨料-新浆体、老浆体-新浆体和老骨料-老浆体三种界面过渡区的微观形貌，解释了粉煤灰对再生混凝土抗硫酸盐侵蚀的改善机理。结果显示，增大水胶比和再生骨料替代率都会削弱混凝土的抗硫酸盐侵蚀性能，而粉煤灰的掺入能明显提高混凝土的抗硫酸盐侵蚀能力。最终确定的水胶比为0.55，再生骨料替代率和粉煤灰掺量分别为50%和30%。老骨料-新浆体界面和老骨料-老浆体界面是粉煤灰再生混凝土中的双重薄弱面，在制备时需重点处理。 Abstract: In order to investigate the change of the performance of fly ash recycled concrete under the action of sulfate erosion, the effects of material ratio on the corrosion resistance coefficient and quality loss rate of concrete were tested and reasonable material composition was obtained. The microstructures of three interfacial transition zones of old aggregate-new slurry, old slurry-new slurry and old aggregate-old slurry in recycled concrete were observed by SEM. The results show that increasing the W/B and the replacement rate of recycled aggregate will weaken the sulfate corrosion resistance of concrete, but the addition of fly ash can obviously improve the performance of concrete against sulfate erosion. The W/B, the substitution rate of recycled aggregate and the amount of fly ash were determined by 0.55, 50% and 30 % respectively. The interface between old aggregate and new slurry, old aggregate and old slurry is the double weak surface in fly ash recycled concrete, so it should emphasis on preparation.
英文名 : The Influence of Fly Ash on Resistance to Sulphate Erosion and the Microstructure of Interfacial Transition Zone of Recycled Con
刊期 : ２０19年第5期
关键词 : 再生混凝土；粉煤灰；抗硫酸盐侵蚀；界面过渡区；微观形貌
Key words : Regenerated concrete; Fly ash; Resistance to sulphate erosion; Interface transition zone; Micromorphology
刊期 : ２０19年第5期
DOI : 10.19761/j.1000-4637.2019.05.092.05
文章编号 :
基金项目 :
作者 : 朱晓云1，孙国卿2
单位 : 1.天津交通职业学院，300110；2. 天津大学仁爱学院，301636

朱晓云1，孙国卿2

朱晓云,孙国卿.粉煤灰对再生混凝土抗硫酸盐侵蚀及界面过渡区微观特性的影响[J].混凝土与水泥制品,2019(5):92-96.

ZHU X Y,SUN G Q.The Influence of Fly Ash on Resistance to Sulphate Erosion and the Microstructure of Interfacial Transition Zone of Recycled Concrete[J].China Concrete and Cement Products,2019(5):92-96.

摘要
参数
结论
参考文献
引用本文
摘   要：为了探究硫酸盐侵蚀作用下粉煤灰再生混凝土性能的变化，测试了材料配比对混凝土抗压耐蚀系数和质量损失率的影响，得到合理的材料组成，并通过SEM观察再生混凝土中老骨料-新浆体、老浆体-新浆体和老骨料-老浆体三种界面过渡区的微观形貌，解释了粉煤灰对再生混凝土抗硫酸盐侵蚀的改善机理。结果显示，增大水胶比和再生骨料替代率都会削弱混凝土的抗硫酸盐侵蚀性能，而粉煤灰的掺入能明显提高混凝土的抗硫酸盐侵蚀能力。最终确定的水胶比为0.55，再生骨料替代率和粉煤灰掺量分别为50%和30%。老骨料-新浆体界面和老骨料-老浆体界面是粉煤灰再生混凝土中的双重薄弱面，在制备时需重点处理。
Abstract: In order to investigate the change of the performance of fly ash recycled concrete under the action of sulfate erosion, the effects of material ratio on the corrosion resistance coefficient and quality loss rate of concrete were tested and reasonable material composition was obtained. The microstructures of three interfacial transition zones of old aggregate-new slurry, old slurry-new slurry and old aggregate-old slurry in recycled concrete were observed by SEM. The results show that increasing the W/B and the replacement rate of recycled aggregate will weaken the sulfate corrosion resistance of concrete, but the addition of fly ash can obviously improve the performance of concrete against sulfate erosion. The W/B, the substitution rate of recycled aggregate and the amount of fly ash were determined by 0.55, 50% and 30 % respectively. The interface between old aggregate and new slurry, old aggregate and old slurry is the double weak surface in fly ash recycled concrete, so it should emphasis on preparation.
关键词:
再生混凝土；粉煤灰；抗硫酸盐侵蚀；界面过渡区；微观形貌
扫二维码用手机看
未找到相应参数组，请于后台属性模板中添加
（1）水胶比越大粉煤灰再生混凝土的抗硫酸盐侵蚀性能越差；随着再生骨料取代率的增大，混凝土抗硫酸盐侵蚀性能逐渐衰减；再生混凝土的抗硫酸盐侵蚀能力随粉煤灰掺量增大而增强。综合考虑，粉煤灰再生混凝土的水胶比为0.55，再生骨料取代率为50%，粉煤灰掺量为30%。
（2）从SEM测试的微观形貌分析，再生混凝土中老骨料-新浆体界面过渡区的孔隙率最高，结构最为疏松薄弱，老骨料-老浆体界面过渡区次之，而老浆体-新浆体界面过渡区孔隙率相对最低，结构最为致密。表明老骨料-新浆体界面和老骨料-老浆体界面是再生混凝土结构中的双重薄弱面，在混凝土制备时需重点处理，可将再生骨料表面的旧砂浆除去。
（3）随着干湿循环次数的增多，在硫酸盐过度侵蚀下，水泥石中短柱状的钙矾石发生分解生成过硫酸盐，而过硫酸盐的膨胀作用导致界面过渡区出现孔隙和微裂缝，结构的致密性变差，混凝土性能极度劣化；粉煤灰的二次水化，火山灰效应和微骨料效应使界面过渡区致密性增强，再生混凝土抗硫酸盐侵蚀能力提高。
[1] 肖开涛．再生混凝土的性能及改性研究[D]．武汉:武汉理工大学,2004．
[2] 李秋义,朱亚光,高嵩．我国高品质再生骨料制备技术及质量评定方法[J]．青岛理工大学学报:自然科学版,2009(4):1-4．
[3] 刘秉洁．西安市建筑垃圾资源化研究[D]．西安:长安大学,2013．
[4] 蔻世聪,潘智生．不同强度混凝土制造的再生骨料对高性能混凝土力学性能的影响[J]．硅酸盐学报,2011(3):7-11．
[5] 冷发光,马孝轩,田冠飞．混凝土抗硫酸盐侵蚀试验方法[J]．东南大学学报,2006,36(2):45-48．
[6] 袁晓露,李北星,崔巩,等．硫酸盐侵蚀环境下混凝土强度的经时变化模型[J]．长江科学院院报,2010,27(3):59-61．
[7] 梁咏宁,袁迎曙．硫酸钠和硫酸镁溶液中混凝土腐蚀破坏的机理[J]．硅酸盐学报,2007,35(4):504-508．
[8] 覃荷瑛．再生混凝土氯离子渗透性试验研究及细观数值模拟[D]．南宁:广西大学,2012．
[9] 闫洪生．再生混凝土的硫酸盐腐蚀试验研究[J]．混凝土,2013(5):13-20．
[10] 施惠生,刘金为．再生混凝土微观结构特征及其耐久性改善技术[J]．水泥工程,2009(4):67-71．
[11] 张增起,张波,阎培渝,等．大掺量粉煤灰混凝土长零期的微观结构[J]．电子显微学报,2014,33(6):516-520．
[12] 魏宏云,周卫峰,李源渊．掺加矿粉和粉煤灰的混凝土渗透性能分析[J]．公路工程,2015,40(5):150-154．
[13] 宋超,肖伯强．磨细粉煤灰对混凝土ITZ微观结构的影响[J]．粉煤灰综合利用,2015(1):48-56．

朱晓云,孙国卿.粉煤灰对再生混凝土抗硫酸盐侵蚀及界面过渡区微观特性的影响[J].混凝土与水泥制品,2019(5):92-96.

ZHU X Y,SUN G Q.The Influence of Fly Ash on Resistance to Sulphate Erosion and the Microstructure of Interfacial Transition Zone of Recycled Concrete[J].China Concrete and Cement Products,2019(5):92-96.

上一个
黏土砖再生粗骨料生态混凝土制备及微观性能研究
下一个
钢渣粉部分替代煅烧MgO对MPC混凝土性能的影响

相关文件

更多
暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设：中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设：中企动力 苏州