三轴循环荷载作用下混凝土的力学性能及损伤特征研究

Study on Mechanical Properties and Damage Characteristics of Concrete Under Triaxial Cyclic Loading

2023年第1期

混凝土；循环加卸载；不可逆应变；累计损伤参数

Concrete; Cyclic loading and unloading; Irreversible strain; Cumulative damage parameter

2023年第1期

10.19761/j.1000-4637.2023.01.021.04

吴建福，胡力绳，田亚洲，刘俊杰，何强

深圳中铁二局有限公司，广东深圳 518034

吴建福，胡力绳，田亚洲，刘俊杰，何强

吴建福,胡力绳,田亚洲,等.三轴循环荷载作用下混凝土的力学性能及损伤特征研究[J].混凝土与水泥制品,2023(1):21-24.

WU J F,HU L S,TIAN Y Z,et al.Study on Mechanical Properties and Damage Characteristics of Concrete Under Triaxial Cyclic Loading[J].China Concrete and Cement Products,2023(1):21-24.

浏览量:

1000

摘要：开展了不同循环加卸载（荷载分别为单轴抗压强度20%、30%、40%、50%、60%、70%和80%）作用下的三轴试验，研究了不同循环荷载作用对灌注桩混凝土力学性能的影响，并分析了混凝土的损伤特征。结果表明：在各级循环加卸载作用下，混凝土的应力-应变曲线出现内凹和右移推进现象；弹性模量随循环次数的增加先增加后减小；在各级循环内，泊松比呈“减小-稳定-增大”的变化规律，第90次循环后超过名义泊松比，混凝土损伤逐渐积累加深，轴向和横向不可逆应变均随循环次数的增加而增加；屈服阶段前混凝土的累计损伤小，屈服阶段后混凝土的横向累计损伤参数比轴向大。 Abstract: Triaxial tests were carried out under different cyclic loading and unloading (loads were 20%, 30%, 40%, 50%, 60%, 70% and 80% of the uniaxial compressive strength), and the effects of different cyclic loads on the mechanical properties of cast-in-place pile concrete were studied, and the damage characteristics of the concrete were analyzed. The results show that the stress-strain curves of concrete specimens appear concave and right shift in the cyclic loading and unloading conditions at all levels. The elastic modulus first increases and then decreases with the increase of the number of cycles. The internal Poisson′s ratio of each cycle shows a change law of "decreasing-stabilizing-increasing". After the 90th cycles, it exceeds the nominal Poisson′s ratio and the concrete damage gradually accumulates and deepens. The axial and transverse irreversible strains increase with the increase of the number of cycles. The concrete cumulative damage before the yield stage is small, and the cumulative damage parameters after the yield stage are larger than those in the axial direction.

英文名 : Study on Mechanical Properties and Damage Characteristics of Concrete Under Triaxial Cyclic Loading

刊期 : 2023年第1期

关键词 : 混凝土；循环加卸载；不可逆应变；累计损伤参数

Key words : Concrete; Cyclic loading and unloading; Irreversible strain; Cumulative damage parameter

刊期 : 2023年第1期

DOI : 10.19761/j.1000-4637.2023.01.021.04

文章编号 :

基金项目 :

作者 : 吴建福，胡力绳，田亚洲，刘俊杰，何强

单位 : 深圳中铁二局有限公司，广东深圳 518034

吴建福，胡力绳，田亚洲，刘俊杰，何强

吴建福,胡力绳,田亚洲,等.三轴循环荷载作用下混凝土的力学性能及损伤特征研究[J].混凝土与水泥制品,2023(1):21-24.

WU J F,HU L S,TIAN Y Z,et al.Study on Mechanical Properties and Damage Characteristics of Concrete Under Triaxial Cyclic Loading[J].China Concrete and Cement Products,2023(1):21-24.





摘要

参数

结论

参考文献

引用本文

Abstract: Triaxial tests were carried out under different cyclic loading and unloading (loads were 20%, 30%, 40%, 50%, 60%, 70% and 80% of the uniaxial compressive strength), and the effects of different cyclic loads on the mechanical properties of cast-in-place pile concrete were studied, and the damage characteristics of the concrete were analyzed. The results show that the stress-strain curves of concrete specimens appear concave and right shift in the cyclic loading and unloading conditions at all levels. The elastic modulus first increases and then decreases with the increase of the number of cycles. The internal Poisson′s ratio of each cycle shows a change law of "decreasing-stabilizing-increasing". After the 90th cycles, it exceeds the nominal Poisson′s ratio and the concrete damage gradually accumulates and deepens. The axial and transverse irreversible strains increase with the increase of the number of cycles. The concrete cumulative damage before the yield stage is small, and the cumulative damage parameters after the yield stage are larger than those in the axial direction.

扫二维码用手机看

[1] 王德辉,史才军,吴林妹,等.超高性能混凝土在中国的研究和应用[J].硅酸盐学报,2016,35(1):141-149.
[2] 王文彬.水泥混凝土路面裂缝成因与防控[J].混凝土与水泥制品,2019(6):84-87.
[3] 王吉山.水泥混凝土道路的施工与养护的方法探讨[J].建材与装饰,2020(2):247-248.
[4] 谭盐宾,谢永江,李化建,等.高速铁路CRTSⅢ型板式无砟轨道自密实混凝土性能研究[J].铁道建筑,2015(1):132-136.
[5] 王方刚,陆加越,徐文.高速铁路CRTSⅢ型板式无砟轨道自密实混凝土制备与性能研究[J].混凝土与水泥制品,2018(7):42-46.
[6] 李化建,谢永江.我国铁路混凝土结构耐久性研究的进展及发展趋势[J].铁道建筑,2016(2):1-8.
[7] 乔雨,杨宁,牟荣峰,等.乌东德大坝低热水泥全级配混凝土强度性能试验研究[J].水利水电技术(中英文),2021,52(1):236-247.
[8] 瞿祖旭,殷崑雁.观音岩电站右岸大坝碾压混凝土配合比优化设计[J].人民长江,2015,46(20):72-76.
[9] SAKR M A,EL-KHORIBY S R,KHALIFA T M,et al.Modeling of RC Shear Walls Strengthened with Ultra-high Performance Fiber Reinforced Concrete(UHPFRC) Jackets[J].Engineering Structures,2019,200(9):1-13.
[10] 金立兵,梁新亚,霍承鼎,等.地下混凝土筒仓仓壁力学性能工程试验与数值分析[J].土木与环境工程学报(中英文),2020,42(3):40-45.
[11] 李杰,任晓丹.混凝土随机损伤力学研究进展[J].建筑结构学报,2014,35(4):20-29.
[12] 魏莱,邱莎,李孟,等.汇聚世界智慧,共享桥梁盛宴,2017中国桥博会在武汉举行[J].中华建设,2017,151(12):40-43.
[13] 王长青,肖建庄,李秋义.循环往复荷载作用下约束再生混凝土力学性能试验[J].建筑结构学报,2020,41(2):436-442.
[14] 朱蕾,陈龙,王磊,等.循环荷载作用下泡沫混凝土强度特性研究[J].混凝土,2020(9):37-45.
[15] 刘杰,吴辉琴,陈宇良,等.早龄期普通混凝土直剪性能及损伤耗能分析[J].混凝土与水泥制品,2021(2):79-83.
[16] 杲晓龙,王俊颜,郭君渊,等.循环荷载作用下超高性能混凝土的轴拉力学性能及本构关系模型[J].复合材料学报,2021,38(11):3925-3938.
[17] 刘俊卿,石同心,陈诚诚.基于声发射技术的高强度混凝土循环荷载下轴压损伤特性试验研究[J].四川建筑科学研究,2021,47(2):77-84.
[18] 李建涛,于江,秦拥军.混凝土材料损伤裂纹演化过程的研究综述[J].混凝土与水泥制品,2017(12):10-13.
[19] 中华人民共和国住房和城乡建设部.工程岩体试验方法标准:GB/T 50266—2013[S].北京:中国计划出版社,2013.
[20] 刘海涛,秦涛.砂岩循环加卸载下损伤特性及声发射Kaiser效应研究[J].煤炭科学技术,2019,47(6):73-80.

上一个

降黏型聚羧酸减水剂的制备技术研究进展

下一个

掺石灰石粉的清水混凝土性能与工艺研究

头部文案

三轴循环荷载作用下混凝土的力学性能及损伤特征研究

相关文件