SAP掺量对UHPC性能的影响及机理研究

Study on the Influence and Mechanism of SAP Content on UHPC Performance

2023年第3期

高吸水性树脂；超高性能混凝土；抗压强度；收缩；耐久性能

Super absorbent polymer(SAP); Ultra-high performance concrete(UHPC); Compressive strength; Shrinkage; Durability

2023年第3期

10.19761/j.1000-4637.2023.03.006.04

中国中铁股份有限公司科技研究开发计划项目（2019-重点-05）。

姜鹏1，李信1，2，陈露一1，2

1．中铁大桥局集团有限公司，湖北武汉 430050；2．桥梁结构健康与安全国家重点实验室，湖北武汉 430034

姜鹏1，李信1，2，陈露一1，2

姜鹏,李信,陈露一.SAP掺量对UHPC性能的影响及机理研究[J].混凝土与水泥制品,2023(3):6-9.

JIANG P,LI X,CHEN L Y.Study on the Influence and Mechanism of SAP Content on UHPC Performance[J].China Concrete and Cement Products,2023(3):6-9.

浏览量:

1000

摘要：针对UHPC收缩大、抗裂性差等问题，将经预湿水处理的高吸水性树脂SAP掺入UHPC中，对比研究了SAP掺量对UHPC性能的影响，并分析其作用机理。结果表明：SAP能有效缓解UHPC的扩展度经时损失；随着SAP掺量的增加，UHPC的扩展度逐渐增加，而抗压强度逐渐降低，且SAP对UHPC早期抗压强度的影响更大；SAP可改善UHPC的自收缩，且掺量越大，改善效果越明显；掺量为0.1%、0.2%的SAP均能改善UHPC的抗氯离子渗透性能，但当掺量超过0.2%时，SAP会降低UHPC的抗氯离子渗透性能和抗冻性能。 Abstract: Aiming at the problems of large shrinkage and poor crack resistance of UHPC, the influence of super absorbent polymer SAP dosage on the performance of UHPC with the SAP treated with pre-wet water was studied, and its mechanism was analyzed. The results show that SAP can effectively alleviate expansion loss over time of UHPC with the increase of SAP dosage, the expansion degree of UHPC gradually increases and the compressive strength gradually decreases, and SAP has a greater influence on the early compressive strength of UHPC. SAP can improve the self-shrinkage of UHPC, the greater the dosage, the more obvious the effect. The dosage of SAP with 0.1% and 0.2% can improve the chloride ion erosion resistance of UHPC, but when the SAP dosage is more than 0.2%, it can lead to the reduction of the chloride ion erosion resistance and the frost resistance of UHPC.

英文名 : Study on the Influence and Mechanism of SAP Content on UHPC Performance

刊期 : 2023年第3期

关键词 : 高吸水性树脂；超高性能混凝土；抗压强度；收缩；耐久性能

Key words : Super absorbent polymer(SAP); Ultra-high performance concrete(UHPC); Compressive strength; Shrinkage; Durability

刊期 : 2023年第3期

DOI : 10.19761/j.1000-4637.2023.03.006.04

文章编号 :

基金项目 : 中国中铁股份有限公司科技研究开发计划项目（2019-重点-05）。

作者 : 姜鹏1，李信1，2，陈露一1，2

单位 : 1．中铁大桥局集团有限公司，湖北武汉 430050；2．桥梁结构健康与安全国家重点实验室，湖北武汉 430034

姜鹏1，李信1，2，陈露一1，2

姜鹏,李信,陈露一.SAP掺量对UHPC性能的影响及机理研究[J].混凝土与水泥制品,2023(3):6-9.

JIANG P,LI X,CHEN L Y.Study on the Influence and Mechanism of SAP Content on UHPC Performance[J].China Concrete and Cement Products,2023(3):6-9.





摘要

参数

结论

参考文献

引用本文

Abstract: Aiming at the problems of large shrinkage and poor crack resistance of UHPC, the influence of super absorbent polymer SAP dosage on the performance of UHPC with the SAP treated with pre-wet water was studied, and its mechanism was analyzed. The results show that SAP can effectively alleviate expansion loss over time of UHPC with the increase of SAP dosage, the expansion degree of UHPC gradually increases and the compressive strength gradually decreases, and SAP has a greater influence on the early compressive strength of UHPC. SAP can improve the self-shrinkage of UHPC, the greater the dosage, the more obvious the effect. The dosage of SAP with 0.1% and 0.2% can improve the chloride ion erosion resistance of UHPC, but when the SAP dosage is more than 0.2%, it can lead to the reduction of the chloride ion erosion resistance and the frost resistance of UHPC.

扫二维码用手机看

[1] 王晖.超高性能混凝土（UHPC）研究综述[J].混凝土与水泥制品,2022(4):25-28.
[2] 钟蕴为,吴永魁,文许高媛,等.超高性能混凝土(UHPC)基本性能研究综述[J].混凝土与水泥制品,2021(9):1-4.
[3] 王洋,邵旭东,沈秀将,等.钢板条-UHPC组合桥面结构静力及疲劳试验[J].中国公路学报,2021,34(8):261-272.
[4] 文庆军,邓华,王凯,等.带钢板UHPC湿接缝梁的抗剪性能试验研究[J].混凝土与水泥制品,2022(11):39-43.
[5] 郑七振,刘阳阳,龙莉波,等.超高性能混凝土连接的装配式现浇混凝土框架抗震性能[J].工业建筑,2019,49(10):85-91.
[6] 李文超.钢混组合结构装配式UHPC桥面板接缝构造与力学性能研究[D].南京:东南大学,2018.
[7] 唐瑜,宫献伟,张如意,等.塞尔维亚中国文化中心UHPC双层幕墙设计施工技术研究[J].建筑结构,2022,52(S1):2974-2979.
[8] 黄政宇,王嘉.高吸水性树脂对超高性能混凝土性能的影响[J].硅酸盐通报,2012,31(3):539-544.
[9] 马先伟,张家科,刘剑辉.高性能水泥基材料内养护剂用高吸水树脂的研究进展[J].硅酸盐学报,2015,43(8):1099-1110．
[10] 孔祥明,张珍林.高吸水性树脂对高强混凝土浆体孔结构的影响[J].硅酸盐学报,2013,41(11):1474-1480.
[11] 秦鸿根,高美蓉,庞超明,等.SAP内养护剂改善膨胀混凝土性能及其机理研究[J].建筑材料学报,2011,14(3):394-399.
[12] 甘冰清,倪修全.高吸水性树脂(SAP)对混凝土收缩的影响[J].四川建材,2015,41(1):10-11.
[13] 陈德鹏,钱春香,高桂波.高吸水树脂对混凝土收缩开裂的改善作用及其机理[J].功能材料,2007(3):475-478.
[14] 史才军,吕奎喜,马先伟,等.高吸水性树脂对自密实混凝土性能的影响[J].材料导报,2015,29(20):118-124.
[15] 邵力.高吸水性树脂(SAP)对自密实混凝土性能的影响[D].广州:广州大学,2018.
[16] 钟佩华.高吸水性树脂(SAP)对高强混凝土自收缩性能的影响及作用机理[D].重庆:重庆大学,2015.
[17] 孔祥明,张珍林.高吸水性树脂对高强混凝土自收缩的减缩机理[J].硅酸盐学报.2014,42(2):150-155.
[18] 中华人民共和国住房和城乡建设部.普通混凝土拌合物性能试验方法标准:GB/T 50080—2016[S].北京:中国建筑工业出版社,2017.
[19] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
[20] 中华人民共和国住房和城乡建设部.普通混凝土长期性能和耐久性能试验方法标准:GB/T 50082—2009[S].北京:中国建筑工业出版社,2010.
[21] 杨鲁,李化建,杨长辉,等.高吸水树脂基内养护混凝土研究进展[J].材料导报,2011,25(S2):459-461.
[22] 王立霞.高吸水性树脂对低水胶比混凝土性能的影响[J].混凝土与水泥制品,2013(7):7-10.

上一个

甲酸钾除冰液作用下机场道面混凝土单面冻融试验研究

下一个

SiO2溶胶和CNTs杂化增强水泥基复合材料性能研究

头部文案

SAP掺量对UHPC性能的影响及机理研究

相关文件