寒冷地区混凝土路面砖的力学及耐久性能研究

Study on Mechanical Properties and Durability of Precast Concrete Paving Units in Cold Area

2023年第3期

混凝土路面砖；抗折强度；抗盐冻性能；抗冻性能；正交试验

Precast concrete paving units; Flexural strength; Salt freezing resistance; Frost resistance; Orthogonal test

2023年第3期

10.19761/j.1000-4637.2023.03.060.04

魏清河1，冯启彪2

1.兰州市南河道管理工作办公室，甘肃兰州730020；2.兰州宏方新型建材科技有限公司，甘肃兰州730020

魏清河1，冯启彪2

魏清河,冯启彪.寒冷地区混凝土路面砖的力学及耐久性能研究[J].混凝土与水泥制品,2023(3):60-63.

WEI Q H,FENG Q B.Study on Mechanical Properties and Durability of Precast Concrete Paving Units in Cold Area[J].China Concrete and Cement Products,2023(3):60-63.

浏览量:

1000

摘要：采用正交试验法研究了防水剂掺量、减水剂掺量、聚丙烯纤维掺量和水胶比对混凝土路面砖力学、抗冻及抗盐冻性能的影响。结果表明：随着防水剂掺量的增加，试件的抗折强度先增大后减小，强度损失率和单位面积质量损失减小；随着减水剂掺量的增加，试件的抗折强度增大，强度损失率和单位面积质量损失减小；随着聚丙烯纤维掺量的增加，试件的抗折强度增大，强度损失率和单位面积质量损失减小；随着水胶比的增加，试件抗折强度先增大后减小，强度损失率先减小后增大，单位面积质量损失增大；综合考虑力学性能、抗冻性能和抗盐冻性能，推荐混凝土路面砖的防水剂掺量为2.0%、减水剂掺量为2.0%、聚丙烯纤维掺量为0.5%、水胶比为0.25。 Abstract: The influence of waterproof agent content, water-reducing agent content, polypropylene fiber content and water-binder ratio on the mechanical properties, frost resistance and salt freezing resistance of precast concrete paving units was studied by orthogonal test method. The results show that with the increase of waterproof agent content, the flexural strength of the specimen first increases and then decreases, and the strength loss rate and mass loss per unit area decrease. With the increase of water-reducing agent content, the flexural strength of the specimen increases, and the strength loss rate and mass loss per unit area decrease. With the increase of polypropylene fiber content, the flexural strength of the specimen increases, and the strength loss rate and mass loss per unit area decrease. With the increase of water-binder ratio, the flexural strength of the specimen first increases and then decreases, the strength loss first decreases and then increases, and the mass loss per unit area increases. Considering the mechanical properties, frost resistance and salt freezing resistance of precast concrete paving units, the recommended content of waterproof agent is 2.0%, water-reducing agent is 2.0%, polypropylene fiber is 0.5%, and water-binder ratio is 0.25.

英文名 : Study on Mechanical Properties and Durability of Precast Concrete Paving Units in Cold Area

刊期 : 2023年第3期

关键词 : 混凝土路面砖；抗折强度；抗盐冻性能；抗冻性能；正交试验

Key words : Precast concrete paving units; Flexural strength; Salt freezing resistance; Frost resistance; Orthogonal test

刊期 : 2023年第3期

DOI : 10.19761/j.1000-4637.2023.03.060.04

文章编号 :

基金项目 :

作者 : 魏清河1，冯启彪2

单位 : 1.兰州市南河道管理工作办公室，甘肃兰州730020；2.兰州宏方新型建材科技有限公司，甘肃兰州730020

魏清河1，冯启彪2

魏清河,冯启彪.寒冷地区混凝土路面砖的力学及耐久性能研究[J].混凝土与水泥制品,2023(3):60-63.

WEI Q H,FENG Q B.Study on Mechanical Properties and Durability of Precast Concrete Paving Units in Cold Area[J].China Concrete and Cement Products,2023(3):60-63.





摘要

参数

结论

参考文献

引用本文

Abstract: The influence of waterproof agent content, water-reducing agent content, polypropylene fiber content and water-binder ratio on the mechanical properties, frost resistance and salt freezing resistance of precast concrete paving units was studied by orthogonal test method. The results show that with the increase of waterproof agent content, the flexural strength of the specimen first increases and then decreases, and the strength loss rate and mass loss per unit area decrease. With the increase of water-reducing agent content, the flexural strength of the specimen increases, and the strength loss rate and mass loss per unit area decrease. With the increase of polypropylene fiber content, the flexural strength of the specimen increases, and the strength loss rate and mass loss per unit area decrease. With the increase of water-binder ratio, the flexural strength of the specimen first increases and then decreases, the strength loss first decreases and then increases, and the mass loss per unit area increases. Considering the mechanical properties, frost resistance and salt freezing resistance of precast concrete paving units, the recommended content of waterproof agent is 2.0%, water-reducing agent is 2.0%, polypropylene fiber is 0.5%, and water-binder ratio is 0.25.

扫二维码用手机看

[1] 徐云生,帅同杰.钢渣路面砖中试生产技术及应用研究[J].建材发展导向,2013(2):204-206.
[2] 王武祥.透性混凝土路面砖的种类和性能[J].建砌块与砌块建筑,2003(1):30-32.
[3] 王友利.自动化生产线彩色混凝土路面砖工艺控制与研讨[J].居业,2017,52(11):102-103.
[4] 陈晋栋,王武祥,张磊蕾．国内外水泥基透水混凝土路面砖的研究进展[J]．建筑砌块与砌块建筑,2016(5):5-6,8-10．
[5] 霍亮.透性混凝土路面材料的制备及性能研究[D].南京:东南大学,2004.
[6] LUN Y X,ZHOU M K,CAI X,et al.Methods for Improving Volume Stability of Steel Slag as Fine Aggregate[J].Journal of Wuhan University of Technology-Materials Science Edition, 2008,23(5):737-742.
[7] 周家慧,杨建永,李钧.不同因素对透水混凝土性能的影响[J].混凝土与水泥制品,2022(5):30-33.
[8] 黄冬辉,崔璨,汤斐宇,等.基于孔结构特征的透水混凝土性能研究进展[J].混凝土与水泥制品,2021(12):20-23.
[9] 中南,石云兴.透水混凝土及其应用技术[M].北京:中国建筑工业出版社,2011.
[10] 王俊岭,秦全城,等.塑料网格砂基透水砖铺装系统的径流控制试验研究[J].新型建筑材料,2015(1):13-16.
[11] 海燕,刘华章.混凝土透水砖的配合比设计、生产与施工[J].新型建筑材料,2007(7):27-29.
[12] 李龙飞,张桐瑞,刘继远,等.影响普通混凝土透水路面砖耐久性因素的研究[J].山西建筑,2020(4):110-111.
[13] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.通用硅酸盐水泥:GB 175—2007[S].北京:中国标准出版社,2007.
[14] 国家发展和改革委员会.砂浆、混凝土防水剂:JC/T 474—2008[S].北京:建材工业出版社,2008.
[15] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.混凝土外加剂:GB 8076—2008[S].北京:中国标准出版社,2008.
[16] 中华人民共和国住房和城乡建设部.普通混凝土配合比设计规程:JGJ 55—2011[S].北京:中国建筑工业出版社,2011.
[17] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.混凝土路面砖:GB/T 28635—2012[S].北京:中国标准出版社,2012.

上一个

钢纤维混凝土的受力破坏机制及力学性能研究

下一个

关于我国预制混凝土桩行业绿色低碳化发展途径的几点思考

头部文案

寒冷地区混凝土路面砖的力学及耐久性能研究

相关文件