石灰石粉对主塔大体积混凝土性能的影响
Effects of Limestone Powder on Properties of Mass Concrete for Main Tower
2023年第4期
主塔工程;大体积混凝土;石灰石粉;流变性能;绝热温升;干燥收缩;抗压强度;抗渗性能
Main tower engineering; Mass concrete; Limestone powder; Rheological property; adiabatic temperature rise; Drying shrinkage; Compressive strength; Impermeability
2023年第4期
10.19761/j.1000-4637.2023.04.088.05
中国中铁股份有限公司科技研究开发计划项目(2020-29-重点)。
盖珂瑜1,2,龙 勇1,2,刘爱林3,黄 斌3,王亚洲1,2
1.桥梁结构健康与安全国家重点实验室,湖北 武汉 430034;2.中铁大桥科学研究院有限公司,湖北武汉 430034;3.中铁大桥局集团有限公司,湖北 武汉 430050

盖珂瑜1,2,龙 勇1,2,刘爱林3,黄 斌3,王亚洲1,2

盖珂瑜,龙勇,刘爱林,等.石灰石粉对主塔大体积混凝土性能的影响[J].混凝土与水泥制品,2023(4):88-92.

GE Ke-yu, LONG Yong, LIU Ai-lin,et al.Effects of Limestone Powder on Properties of Mass Concrete for Main Tower[J].China Concrete and Cement Products,2023(4):88-92.

浏览量:
1000
摘   要:以水泥、粉煤灰和石灰石粉为胶凝材料,制备了一种低温升主塔大体积混凝土,研究了石灰石粉掺量(5%、10%、15%)对砂浆流变性能和混凝土绝热温升、干燥收缩性能、力学性能、抗渗性能的影响,采用SEM观察了水化产物的微观形貌,并与水泥-粉煤灰-矿渣粉胶凝体系(对照组)进行了对比。结果表明:与对照组相比,掺入石灰石粉可以降低砂浆的塑性黏度和屈服应力,延缓胶凝材料的水化进程,降低混凝土的绝热温升;石灰石粉的掺量越大,抑制混凝土干燥收缩的作用越显著;随着石灰石粉掺量的增加,混凝土的抗压强度下降,但掺5%石灰石粉混凝土的抗压强度较对照组高;与对照组相比,掺石灰石粉混凝土的抗渗性能较好,掺5%石灰石粉混凝土的抗渗性能最好。 Abstract: Taking cement, fly ash and limestone powder as cementitious materials, the mass concrete with low temperature rise for main tower was prepared. The effects of limestone powder content(5%, 10%, 15%) on the rheological properties of mortar, adiabatic temperature rise, drying shrinkage, mechanical properties and impermeability of concrete were studied, and the microscopic morphology of hydration products was observed by SEM. The results were compared with those of cement-fly ash-slag powder cementitious system (control group). The results show that compared with the control group, adding limestone powder can reduce the plastic viscosity and yield stress of mortar, delay the hydration process of cementitious materials, and reduce the adiabatic temperature rise of concrete. The greater the content of limestone powder, the more significant the effect of inhibiting the drying shrinkage of concrete. With the increase of limestone powder content, the compressive strength of concrete decreases, but the compressive strength of concrete mixed with 5% limestone powder is higher than that of control group. Compared with the control group, the impermeability of concrete mixed with limestone powder is better, and the impermeability of concrete mixed with 5% limestone powder is the best.
英文名 : Effects of Limestone Powder on Properties of Mass Concrete for Main Tower
刊期 : 2023年第4期
关键词 : 主塔工程;大体积混凝土;石灰石粉;流变性能;绝热温升;干燥收缩;抗压强度;抗渗性能
Key words : Main tower engineering; Mass concrete; Limestone powder; Rheological property; adiabatic temperature rise; Drying shrinkage; Compressive strength; Impermeability
刊期 : 2023年第4期
DOI : 10.19761/j.1000-4637.2023.04.088.05
文章编号 :
基金项目 : 中国中铁股份有限公司科技研究开发计划项目(2020-29-重点)。
作者 : 盖珂瑜1,2,龙 勇1,2,刘爱林3,黄 斌3,王亚洲1,2
单位 : 1.桥梁结构健康与安全国家重点实验室,湖北 武汉 430034;2.中铁大桥科学研究院有限公司,湖北武汉 430034;3.中铁大桥局集团有限公司,湖北 武汉 430050

盖珂瑜1,2,龙 勇1,2,刘爱林3,黄 斌3,王亚洲1,2

盖珂瑜,龙勇,刘爱林,等.石灰石粉对主塔大体积混凝土性能的影响[J].混凝土与水泥制品,2023(4):88-92.

GE Ke-yu, LONG Yong, LIU Ai-lin,et al.Effects of Limestone Powder on Properties of Mass Concrete for Main Tower[J].China Concrete and Cement Products,2023(4):88-92.

摘要
参数
结论
参考文献
引用本文

摘   要:以水泥、粉煤灰和石灰石粉为胶凝材料,制备了一种低温升主塔大体积混凝土,研究了石灰石粉掺量(5%、10%、15%)对砂浆流变性能和混凝土绝热温升、干燥收缩性能、力学性能、抗渗性能的影响,采用SEM观察了水化产物的微观形貌,并与水泥-粉煤灰-矿渣粉胶凝体系(对照组)进行了对比。结果表明:与对照组相比,掺入石灰石粉可以降低砂浆的塑性黏度和屈服应力,延缓胶凝材料的水化进程,降低混凝土的绝热温升;石灰石粉的掺量越大,抑制混凝土干燥收缩的作用越显著;随着石灰石粉掺量的增加,混凝土的抗压强度下降,但掺5%石灰石粉混凝土的抗压强度较对照组高;与对照组相比,掺石灰石粉混凝土的抗渗性能较好,掺5%石灰石粉混凝土的抗渗性能最好。

Abstract: Taking cement, fly ash and limestone powder as cementitious materials, the mass concrete with low temperature rise for main tower was prepared. The effects of limestone powder content(5%, 10%, 15%) on the rheological properties of mortar, adiabatic temperature rise, drying shrinkage, mechanical properties and impermeability of concrete were studied, and the microscopic morphology of hydration products was observed by SEM. The results were compared with those of cement-fly ash-slag powder cementitious system (control group). The results show that compared with the control group, adding limestone powder can reduce the plastic viscosity and yield stress of mortar, delay the hydration process of cementitious materials, and reduce the adiabatic temperature rise of concrete. The greater the content of limestone powder, the more significant the effect of inhibiting the drying shrinkage of concrete. With the increase of limestone powder content, the compressive strength of concrete decreases, but the compressive strength of concrete mixed with 5% limestone powder is higher than that of control group. Compared with the control group, the impermeability of concrete mixed with limestone powder is better, and the impermeability of concrete mixed with 5% limestone powder is the best.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)石灰石粉的掺入降低了砂浆的塑性黏度和屈服应力,随着石灰石粉掺量的增加,砂浆的塑性黏度和屈服应力逐渐减小。
(2)与对照组相比,掺石灰石粉混凝土的绝热温升较低,水化进程明显延迟,且随着石灰石粉掺量的增加,石灰石粉对水化的延迟效果逐渐增强。
(3)掺石灰石粉混凝土的各龄期干燥收缩值基本均低于对照组,且随着石灰石粉掺量的增加,混凝土各龄期的干燥收缩值逐渐减小。

(4)掺石灰石粉混凝土的抗压强度随着石灰石粉掺量的增加而降低;与对照组相比,掺5%石灰石粉混凝土的抗压强度较高,说明掺入适量石灰石粉有利于提高混凝土的抗压强度。
(5)掺石灰石粉混凝土的电通量均低于对照组,且随着石灰石粉掺量的增加,混凝土的电通量逐渐增大,其中,掺5%石灰石粉混凝土的电通量最小,抗渗性能最好。

[1] 刘丹.大体积混凝土温度-应力场理论研究和应用现状综述[J].混凝土与水泥制品,2022(3):17-23.
[2] 周健.不同温度下水泥-矿物掺合料-膨胀剂复合胶凝体系水化特性研究[D].重庆:重庆大学,2017.
[3] 杨辉,李北星,倪嵩,等.主塔墩承台C35大体积混凝土配合比设计与性能研究[J].混凝土,2020(5):94-97.
[4] 高凡.基于早期抗裂性能的掺合料混凝土配合比优选及应用[D].杭州:浙江工业大学,2019.
[5] 李宁.复合石灰石粉-粉煤灰-矿渣再生混凝土体积稳定性研究[D].徐州:中国矿业大学,2019.
[6] 刘数华,曾力.新型掺合料对水工混凝土性能的影响[J].水力发电学报,2011,30(2):118-122.
[7] 孙庚宁,叶远胜,李艳萍,等.龙江大坝混凝土掺合料选择研究[J].东北水利水电,2009,27(6):58-60.
[8] 王成启,庄骅,张悦然,等.海工自密实高性能混凝土绝热温升试验研究[J].工业建筑,2013,43(3):88-92,155.
[9] 马勇,许垒,关羽.南京长江第四大桥南主塔混凝土配合比设计与施工控制[J].中国水运(下半月),2013,13(6):264-266,245.
[10] 肖佳,张泽的,韩凯东,等.水泥-石灰石粉浆体颗粒群特性与流变性能关系[J].建筑材料学报,2021,24(1):7-13.
[11] HE Z,CAI R J,CHEN E,et al.The Investigation of Early Hydration and Pore Structure for Limestone Powder Wastes Blended Cement Pastes[J].Construction and Building Materials,2019,229:116923.
[12] THONGSANITGARN P,WONGKEO W,CHAIPANICH A,et al.Heat of Hydration of Portland High-calcium Fly Ash Cement Incorporating Limestone Powder: Effect of Limestone Particle Size[J].Construction and Building Materials,2014,66:410-417.
[13] LI C Z,JIANG L H.Utilization of Limestone Powder as an Activator for Early-age Strength Improvement of Slag Concrete[J].Construction and Building Materials,2020,253:119257.
[14] 刘牧天,黎梦圆,王强.等强度条件下石灰石粉对混凝土收缩和耐久性的影响[J].硅酸盐通报,2014,33(8):1967-1972,1977.
[15] 肖斐,崔洪涛,陈剑雄,等.超磨细石灰石粉高强混凝土的研究[J].硅酸盐通报,2010,29(6):1303-1307.
[16] 刘数华,王军.石灰石粉对砂浆孔结构的影响[J].建筑材料学报,2011,14(4):532-535,575.
[17] 盖珂瑜,龙勇,刘俊利,等.掺合料复掺对清水混凝土性能的影响[J].混凝土与水泥制品,2022(5):12-16.
[18] WANG X Y.Analysis of Hydration and Strength Optimization of Cement-Fly Ash-Limestone Ternary Blended Concrete[J].Construction and Building Materials,2018,166:130-140.

盖珂瑜,龙勇,刘爱林,.石灰石粉对主塔大体积混凝土性能的影响[J].混凝土与水泥制品,2023(4):88-92.

GE Ke-yu, LONG Yong, LIU Ai-lin,et al.Effects of Limestone Powder on Properties of Mass Concrete for Main Tower[J].China Concrete and Cement Products,2023(4):88-92.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州