多功能防腐阻锈剂对钢筋混凝土性能的影响

Effect of Multifunctional Sulfate-Resistant and Corrosion-Inhibition Admixture on Properties of Reinforced Concrete

2023年第5期

防腐阻锈剂；抗蚀；力学性能；膨胀率；混凝土；钢筋；砂浆

Sulfate-resistant and corrosion-inhibition admixture; Corrosion resistance; Mechanical property; Expansion rate; Concrete; Steel bar; Mortar

2023年第5期

10.19761/j.1000-4637.2023.05.032.04

刘喜旭1，张小平2，严涵2，马琳2，柯伟席2

1.武汉三源特种建材有限责任公司，湖北武汉 430070；2.武汉源锦建材科技有限公司，湖北武汉 430070

刘喜旭1，张小平2，严涵2，马琳2，柯伟席2

刘喜旭,张小平,严涵,等.多功能防腐阻锈剂对钢筋混凝土性能的影响[J].混凝土与水泥制品,2023(5):32-35.

LIU X X,ZHANG X P,YAN H.Effect of Multifunctional Sulfate-resistant and Corrosion-inhibition Admixture on Properties of Reinforced Concrete[J].China Concrete and Cement Product,2023(5):32-35.

浏览量:

1000

摘要：研制了一种防腐阻锈剂（MA），并研究了其对钢筋混凝土力学性能、耐久性能的影响。结果表明：基于对照组，掺MA的混凝土7 d和28 d抗压强度比分别为115%和108%，其氯离子扩散系数比为71.94%；通过钢筋耐盐水浸渍试验发现，MA具有良好的阻锈效果；掺MA的砂浆抗蚀系数为1.13，20 ℃和40 ℃水浴养护下砂浆的7 d限制膨胀率分别为0.028%和0.035%，28 d限制膨胀率分别为0.040%和0.039%，具有一定的补偿收缩作用。 Abstract: A multifunctional sulfate-resistant and corrosion-inhibition admixture(MA) was developed, and its effects on the mechanical properties and durability of reinforced concrete were studied. The results show that based on the control group, the 7 d and 28 d compressive strength ratios of concrete doped with MA are 115% and 108%, respectively. The chloride ion diffusion coefficient ratio of concrete is 71.94%. The salt water immersion test of steel bar shows that MA has good rust resistance effect. The corrosion resistance coefficient of mortar doped with MA is 1.13, and the 7 d limit expansion rates of mortar measured at 20 ℃ and 40 ℃ water conservation conditions are 0.028% and 0.035%, respectively, and the limited expansion rates of 28 d are 0.040% and 0.039%, respectively, and has a certain effect of compensating shrinkage.

英文名 : Effect of Multifunctional Sulfate-Resistant and Corrosion-Inhibition Admixture on Properties of Reinforced Concrete

刊期 : 2023年第5期

关键词 : 防腐阻锈剂；抗蚀；力学性能；膨胀率；混凝土；钢筋；砂浆

Key words : Sulfate-resistant and corrosion-inhibition admixture; Corrosion resistance; Mechanical property; Expansion rate; Concrete; Steel bar; Mortar

刊期 : 2023年第5期

DOI : 10.19761/j.1000-4637.2023.05.032.04

文章编号 :

基金项目 :

作者 : 刘喜旭1，张小平2，严涵2，马琳2，柯伟席2

单位 : 1.武汉三源特种建材有限责任公司，湖北武汉 430070；2.武汉源锦建材科技有限公司，湖北武汉 430070

刘喜旭1，张小平2，严涵2，马琳2，柯伟席2

刘喜旭,张小平,严涵,等.多功能防腐阻锈剂对钢筋混凝土性能的影响[J].混凝土与水泥制品,2023(5):32-35.

LIU X X,ZHANG X P,YAN H.Effect of Multifunctional Sulfate-resistant and Corrosion-inhibition Admixture on Properties of Reinforced Concrete[J].China Concrete and Cement Product,2023(5):32-35.





摘要

参数

结论

参考文献

引用本文

Abstract: A multifunctional sulfate-resistant and corrosion-inhibition admixture(MA) was developed, and its effects on the mechanical properties and durability of reinforced concrete were studied. The results show that based on the control group, the 7 d and 28 d compressive strength ratios of concrete doped with MA are 115% and 108%, respectively. The chloride ion diffusion coefficient ratio of concrete is 71.94%. The salt water immersion test of steel bar shows that MA has good rust resistance effect. The corrosion resistance coefficient of mortar doped with MA is 1.13, and the 7 d limit expansion rates of mortar measured at 20 ℃ and 40 ℃ water conservation conditions are 0.028% and 0.035%, respectively, and the limited expansion rates of 28 d are 0.040% and 0.039%, respectively, and has a certain effect of compensating shrinkage.

扫二维码用手机看

[1] 金伟良,吴航通,许晨,等.钢筋混凝土结构耐久性提升技术研究进展[J].水利水电科技进展,2015,35(5):68-76,135.
[2] 张召才.钢筋混凝土的玉米蛋白阻锈剂研制及其阻锈机理研究[D].哈尔滨:哈尔滨工业大学,2020.
[3] 刘晨曦.氯离子侵蚀下混凝土中钢筋锈蚀规律及钢筋混凝土结构时变可靠度分析[D].天津:天津大学,2020.
[4] 刘志勇,缪昌文,周伟玲,等.迁移性阻锈剂对混凝土结构耐久性的保持和提升作用[J].硅酸盐学报,2008,234(10):1494-1500.
[5] 陈逸群,左俊卿,房霆宸,等.阳离子型混凝土阻锈剂防腐蚀性能研究[J].混凝土与水泥制品,2019(11):9-11,16.
[6] 仵江涛,何锐,王笑风,等.硫酸盐侵蚀混凝土内外影响因素及影响机理研究进展[J].硅酸盐通报,2019,38(1):110-117.
[7] 王志峰.混凝土防腐剂在钢筋混凝土管材生产中的应用[J].混凝土与水泥制品,2006(2):28-29.
[8] 兰瑞鑫,李扬,叶梦琦.氯盐侵蚀下开裂混凝土耐久性可靠度研究[J].湖北工业大学学报,2021,36(4):85-90.
[9] 刘国强,刘来宝.掺氧化镁膨胀剂混凝土的抗硫酸盐侵蚀性能研究[J].硅酸盐通报,2022,41(4):1293-1300.
[10] 蒋明辉.盐湖地区防腐阻锈剂在钢筋混凝土中的作用机理研究[D].呼和浩特:内蒙古科技大学,2022.
[11] 陈蓓,李响,张兴师.防腐阻锈剂对混凝土性能影响试验研究[J].硅酸盐通报,2017,36(5):1790-1795.
[12] 杭美艳,赵文磊,董素芬.抗复合盐侵蚀防腐阻锈剂对混凝土性能影响研究[J].硅酸盐通报,2019,38(1):283-288,293.
[13] 陈剑毅,胡明玉,肖烨,等.复杂环境下矿物掺合料混凝土的耐久性研究[J].硅酸盐通报,2011,30(3):639-644.
[14] 战美秋,齐柠,李梅.钢筋混凝土结构硫酸盐化学侵蚀破坏机理研究[J].河南建材,2020(4):61-62.
[15] 刘立,丁小富,李长成,等.混凝土抗侵蚀防腐剂抗蚀系数试验方法研究[J].混凝土与水泥制品,2020(10):17-20.
[16] 徐俊伟.复合阻锈剂对钢筋混凝土性能的影响研究[D].呼和浩特:内蒙古科技大学,2020.
[17] 曹丰泽,高玉亭,张慧杰,等.MgO膨胀剂在大体积混凝土结构中的抗裂效果研究[J].混凝土与水泥制品,2021(8):24-27.
[18] 马泽琛,吴英红,周海鹏.大体积混凝土裂缝控制[J].中国住宅设施,2021(10):119-120.
[19] 吴淼.钼酸盐阻锈剂对钢筋耐蚀性能影响研究[D].南京:东南大学,2021.
[20] 郭良生,黄霓裳,余兴增.钼酸钠-磷酸盐对碳钢的协同缓蚀作用机理[J].材料保护,2000(2):39-40,63.

上一个

基于基本需水率法的砂浆堆积密实度测试及预测模型

下一个

石灰石粉对主塔大体积混凝土性能的影响

头部文案

多功能防腐阻锈剂对钢筋混凝土性能的影响

相关文件