再生砂和再生粉对干粉砂浆工作性和力学性能的影响
Effect of Recycled Sand and Recycled Powder on Workability and Mechanical Properties of Dry Powder Mortar
2023年第5期
再生砂;再生粉;混凝土;工作性;力学性能;微观分析
Recycled sand; Recycled powder; Concrete; Workability; Mechanical property; Microanalysis
2023年第5期
10.19761/j.1000-4637.2023.05.095.05
凌 刚,徐智勇,胡 亮,林 希
武汉楚天名扬建材有限公司,湖北 武汉 430000

凌 刚,徐智勇,胡 亮,林 希

凌刚,徐智勇,胡亮,等.再生砂和再生粉对干粉砂浆工作性和力学性能的影响[J].混凝土与水泥制品,2023(5):95-98,102.

LING G,XU Z Y,HU L,et al.Effect of Recycled Sand and Recycled Powder on Workability and Mechanical Properties of Dry Powder Mortar[J].China Concrete and Cement Product,2023(5):95-98,102.

浏览量:
1000
摘   要:将废弃混凝土破碎、筛分制成再生砂和再生粉,研究了再生砂、再生粉分别等质量替代机制砂、石粉对干粉砂浆工作性和力学性能的影响,并对微观结构和水化产物进行了分析。结果表明:再生砂的掺入会增大砂浆的需水量、稠度损失和保水率,降低砂浆的表观密度;再生粉掺入过多会导致砂浆的需水量、表观密度和保水率降低,稠度损失增大;随着再生砂替代率的增加,砂浆的3 d抗压强度降低,28 d抗压强度先增大后减小,这主要归因于再生砂的内养护作用;再生粉对砂浆的3 d和28 d抗压强度影响不大,这主要归因于再生粉的水化作用和晶核效应;综合考虑砂浆的工作性和力学性能,建议再生砂替代率不超过40%,再生粉替代率不超过60%。 Abstract: The effects of recycled sand and recycled powder on the workability and mechanical properties of dry powder mortar were studied, and the microstructure and hydration products were analyzed. The results show that the addition of recycled sand can increase the water demand, consistency loss, and water retention rate of mortar, and reduce the apparent density of mortar. Excessive addition of recycled powder will reduce the water demand, apparent density, and water retention ratio of mortar, and increase the consistency loss. With the increase of the replacement rate of recycled sand, the compressive strength of mortar at 3 days decreases, and the compressive strength at 28 days first increases and then decreases, which is mainly due to the internal curing effect of recycled sand. The influence of recycled powder on the compressive strength of mortar at 3 days and 28 days is not significant, which is mainly due to the hydration and nucleation effects of recycled powder. Considering comprehensively the workability and mechanical properties of mortar, it is recommended that the replacement rate of recycled sand should not exceed 40%, and the replacement rate of recycled powder should not exceed 60%.
英文名 : Effect of Recycled Sand and Recycled Powder on Workability and Mechanical Properties of Dry Powder Mortar
刊期 : 2023年第5期
关键词 : 再生砂;再生粉;混凝土;工作性;力学性能;微观分析
Key words : Recycled sand; Recycled powder; Concrete; Workability; Mechanical property; Microanalysis
刊期 : 2023年第5期
DOI : 10.19761/j.1000-4637.2023.05.095.05
文章编号 :
基金项目 :
作者 : 凌 刚,徐智勇,胡 亮,林 希
单位 : 武汉楚天名扬建材有限公司,湖北 武汉 430000

凌 刚,徐智勇,胡 亮,林 希

凌刚,徐智勇,胡亮,等.再生砂和再生粉对干粉砂浆工作性和力学性能的影响[J].混凝土与水泥制品,2023(5):95-98,102.

LING G,XU Z Y,HU L,et al.Effect of Recycled Sand and Recycled Powder on Workability and Mechanical Properties of Dry Powder Mortar[J].China Concrete and Cement Product,2023(5):95-98,102.

摘要
参数
结论
参考文献
引用本文

摘   要:将废弃混凝土破碎、筛分制成再生砂和再生粉,研究了再生砂、再生粉分别等质量替代机制砂、石粉对干粉砂浆工作性和力学性能的影响,并对微观结构和水化产物进行了分析。结果表明:再生砂的掺入会增大砂浆的需水量、稠度损失和保水率,降低砂浆的表观密度;再生粉掺入过多会导致砂浆的需水量、表观密度和保水率降低,稠度损失增大;随着再生砂替代率的增加,砂浆的3 d抗压强度降低,28 d抗压强度先增大后减小,这主要归因于再生砂的内养护作用;再生粉对砂浆的3 d和28 d抗压强度影响不大,这主要归因于再生粉的水化作用和晶核效应;综合考虑砂浆的工作性和力学性能,建议再生砂替代率不超过40%,再生粉替代率不超过60%。

Abstract: The effects of recycled sand and recycled powder on the workability and mechanical properties of dry powder mortar were studied, and the microstructure and hydration products were analyzed. The results show that the addition of recycled sand can increase the water demand, consistency loss, and water retention rate of mortar, and reduce the apparent density of mortar. Excessive addition of recycled powder will reduce the water demand, apparent density, and water retention ratio of mortar, and increase the consistency loss. With the increase of the replacement rate of recycled sand, the compressive strength of mortar at 3 days decreases, and the compressive strength at 28 days first increases and then decreases, which is mainly due to the internal curing effect of recycled sand. The influence of recycled powder on the compressive strength of mortar at 3 days and 28 days is not significant, which is mainly due to the hydration and nucleation effects of recycled powder. Considering comprehensively the workability and mechanical properties of mortar, it is recommended that the replacement rate of recycled sand should not exceed 40%, and the replacement rate of recycled powder should not exceed 60%.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)在保证砂浆初始稠度相当的情况下,随着再生砂替代率的增加,砂浆的需水量、稠度损失和保水率均有所增大,表观密度有所降低,推荐再生砂的替代率不超过40%。
(2)在保证砂浆初始稠度相当的情况下,当再生粉的替代率不大于60%时,砂浆的需水量、表观密度、稠度损失和保水率与基准组相当,但当再生粉的替代率大于60%后,砂浆的需水量、表观密度和保水率降低,稠度损失增大,推荐再生粉的替代率不超过60%。
(3)随着再生砂替代率的增加,砂浆的3 d抗压强度降低,28 d抗压强度先增大后减小,其中,当再生砂的替代率不大于40%时,砂浆的28 d抗压强度比基准组的28 d抗压强度高。
(4)再生粉对砂浆的3 d、28 d抗压强度无明显影响。

[1] 陆凯安.我国建筑垃圾的现状与综合利用[J].施工技术,1998,28(5):44-45.
[2] 罗清海,陈晓明,王衍金,等.工程建筑垃圾处置的调查和分析[J].中国资源综合利用,2009,27(6):29-31.
[3] RAKSHVIR M,BARAI S V.Studies on Recycled Aggregates-Based Concrete[J].Waste Management and Research,2006,24(3):225-233.
[4] 崔旭东,时雪燕.双碳背景下建筑废弃物资源化利用问题研究[J].建设科技,2022(9):32-35.
[5] 董璇.建筑垃圾再生利用的环境性能分析[D].青岛:山东科技大学,2011.
[6] 李湘洲.国外建筑垃圾利用现状及我国的差距[J].砖瓦世界,2012(6):9-13.
[7] 陈旭勇,刘榴,程书凯,等.再生粗骨料品质和掺量对再生混凝土力学性能的影响[J].混凝土与水泥制品,2021(12):89-93.
[8] 艾洪祥,刘洋,卢霄,等.再生细骨料的级配优化及对混凝土性能的影响[J].混凝土与水泥制品,2022(7):92-96.
[9] 王亚松,覃铃玲,李松,等.建筑垃圾再生骨料改性技术研究进展[J].混凝土与水泥制品,2022(9):99-105.
[10] 刘斌.建筑垃圾再生细骨料及微粉制备再生砂浆试验研究[D].郑州:郑州大学,2019.
[11] XIAO J Z,LI J B,ZHANG C.Mechanical Properties of Recycled Aggregate Concrete Under Uniaxial Loading[J].Cement and Concrete Research,2005,35(6):1187-1194.
[12] 毋雪梅,杨久俊,黄明.建筑垃圾磨细粉作矿物掺合料对水泥物理力学性能的影响[J].新型建筑材料,2004(4):16-18.
[13] 高琦,肖建庄,赵艳娜,等.再生细骨料干混砂浆力学性能试验研究[J].混凝土与水泥制品,2021(3):93-96.
[14] 吴姝娴,谈海涛,左俊卿.再生微粉对混凝土强度的影响研究[J].山西建筑,2011,37(35):122-123.
[15] 樊耀虎,李滢,康晓明.再生微粉和粉煤灰对胶砂力学性能及微观结构影响研究[J].硅酸盐通报,2019,38(2):537-542.
[16] 李贞,刘加平,肖建庄.再生细骨料对砂浆自收缩与干燥收缩的正负效应[J].建筑结构学报,2020,41(S2):427-435.

凌刚,徐智勇,胡亮,.再生砂和再生粉对干粉砂浆工作性和力学性能的影响[J].混凝土与水泥制品,2023(5):95-98,102.

LING G,XU Z Y,HU L,et al.Effect of Recycled Sand and Recycled Powder on Workability and Mechanical Properties of Dry Powder Mortar[J].China Concrete and Cement Product,2023(5):95-98,102.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州