NaOH和聚合物乳液复合改性橡胶混凝土的性能研究
Study on Performance of NaOH and Polymer Lotion Composite Modified Crumb Rubber Concrete
2023年第6期
橡胶混凝土;橡胶颗粒;聚合物乳液改性;复合改性;力学性能;抗冻性能
Crumb rubber concrete; Rubber particle; Polymer lotion modification; Composite modification; Mechanical property; Frost resistance
2023年第6期
10.19761/j.1000-4637.2023.06.094.04
苏有文,杨钦淞,高梦秋
西南科技大学 土木工程与建筑学院,四川 绵阳621000

苏有文,杨钦淞,高梦秋

苏有文,杨钦淞,高梦秋.NaOH和聚合物乳液复合改性橡胶混凝土的性能研究[J].混凝土与水泥制品,2023(6):94-97.

SU Y W,YANG Q S,GAO M Q.Study on Performance of NaOH and Polymer Lotion Composite Modified Crumb Rubber Concrete[J].China Concrete and Cement Product,2023(6):94-97.

浏览量:
1000
摘   要:为了研究NaOH和聚合物乳液复合改性橡胶混凝土的性能,对橡胶颗粒采用浓度为4%的NaOH溶液进行12 h浸泡处理,然后将其等体积取代9.5%的河砂,并掺入不同种类(丁苯乳胶、合成树脂、乳化沥青)和掺量(1%、2%、3%、4%、5%)的聚合物乳液对橡胶混凝土(CRC)进行复合改性,研究了聚合物乳液的种类和掺量对CRC力学、抗冻性能的影响。结果表明:随着聚合物乳液掺量的增加,试件的抗压、抗折强度先增大后减小,其中,2%合成树脂对试件抗压、抗折强度的提高效果最好;对于CRC的抗冻性能,3种聚合物乳液的最佳掺量均为3%,其中,丁苯乳胶、合成树脂对CRC抗冻性能的改善效果相对较好,乳化沥青的改善效果相对较差。 Abstract: In order to study the performance of the NaOH and polymer lotion composite modified crumb rubber concrete, the rubber particles were soaked in NaOH solution with concentration of 4% for 12 hours, and then replaced river sand with equal volume(9.5%) of rubber particles, and the different types (styrene butadiene latex, synthetic resin, emulsified asphalt) and contents (1%, 2%, 3%, 4%, 5%) of polymer lotion were added to crumb rubber concrete (CRC). The effects of type and content of polymer lotion on the mechanical properties and frost resistance of CRC were studied. The results show that with the increase of polymer lotion content, the compressive strength and flexural strength of the specimen first increase and then decrease. Among them, 2% synthetic resin has the best effect on improving the compressive strength and flexural strength. For the frost resistance of CRC, the optimal content of all three polymer lotions is 3%. Among them, styrene butadiene latex and synthetic resin have relatively good improvement effects on the frost resistance of CRC, while emulsified asphalt has relatively poor improvement effects.
英文名 : Study on Performance of NaOH and Polymer Lotion Composite Modified Crumb Rubber Concrete
刊期 : 2023年第6期
关键词 : 橡胶混凝土;橡胶颗粒;聚合物乳液改性;复合改性;力学性能;抗冻性能
Key words : Crumb rubber concrete; Rubber particle; Polymer lotion modification; Composite modification; Mechanical property; Frost resistance
刊期 : 2023年第6期
DOI : 10.19761/j.1000-4637.2023.06.094.04
文章编号 :
基金项目 :
作者 : 苏有文,杨钦淞,高梦秋
单位 : 西南科技大学 土木工程与建筑学院,四川 绵阳621000

苏有文,杨钦淞,高梦秋

苏有文,杨钦淞,高梦秋.NaOH和聚合物乳液复合改性橡胶混凝土的性能研究[J].混凝土与水泥制品,2023(6):94-97.

SU Y W,YANG Q S,GAO M Q.Study on Performance of NaOH and Polymer Lotion Composite Modified Crumb Rubber Concrete[J].China Concrete and Cement Product,2023(6):94-97.

摘要
参数
结论
参考文献
引用本文

摘   要:为了研究NaOH和聚合物乳液复合改性橡胶混凝土的性能,对橡胶颗粒采用浓度为4%的NaOH溶液进行12 h浸泡处理,然后将其等体积取代9.5%的河砂,并掺入不同种类(丁苯乳胶、合成树脂、乳化沥青)和掺量(1%、2%、3%、4%、5%)的聚合物乳液对橡胶混凝土(CRC)进行复合改性,研究了聚合物乳液的种类和掺量对CRC力学、抗冻性能的影响。结果表明:随着聚合物乳液掺量的增加,试件的抗压、抗折强度先增大后减小,其中,2%合成树脂对试件抗压、抗折强度的提高效果最好;对于CRC的抗冻性能,3种聚合物乳液的最佳掺量均为3%,其中,丁苯乳胶、合成树脂对CRC抗冻性能的改善效果相对较好,乳化沥青的改善效果相对较差。

Abstract: In order to study the performance of the NaOH and polymer lotion composite modified crumb rubber concrete, the rubber particles were soaked in NaOH solution with concentration of 4% for 12 hours, and then replaced river sand with equal volume(9.5%) of rubber particles, and the different types (styrene butadiene latex, synthetic resin, emulsified asphalt) and contents (1%, 2%, 3%, 4%, 5%) of polymer lotion were added to crumb rubber concrete (CRC). The effects of type and content of polymer lotion on the mechanical properties and frost resistance of CRC were studied. The results show that with the increase of polymer lotion content, the compressive strength and flexural strength of the specimen first increase and then decrease. Among them, 2% synthetic resin has the best effect on improving the compressive strength and flexural strength. For the frost resistance of CRC, the optimal content of all three polymer lotions is 3%. Among them, styrene butadiene latex and synthetic resin have relatively good improvement effects on the frost resistance of CRC, while emulsified asphalt has relatively poor improvement effects.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)随着聚合物乳液掺量的增加,试件的抗压、抗折强度均先增大后减小,2%的丁苯乳胶对CRC抗压、抗折强度的提高效果最好。
(2)随着冻融循环次数的增加,不同聚合物乳液掺量试件的的质量损失率先减小后增大,相对动弹性模量则呈降低趋势;对于抗冻性能而言,3种聚合物乳液的最佳掺量均为3%,其中,丁苯乳胶、合成树脂对CRC抗冻性能的提升效果较乳化沥青更好。
 

[1] 商务部.中国再生资源回收行业发展报告(2020)[J].中国轮胎资源综合利用,2021(9):36-38. 
[2] 陆杨瑞雪,易文,刘奥林,等.废弃轮胎橡胶颗粒改良砂土路用性能试验研究[J].工程技术研究,2020(6):147-149.
[3] 薛刚,刘利强.橡胶混凝土受压性能试验研究[J].混凝土,2022(3):105-108.
[4] 闻洋,贺希茂,崔浩,等.橡胶粉掺量和粒径对橡胶混凝土抗冻性能的试验[J].沈阳建筑大学学报(自然科学版),2022,38(1):135-141.
[5] 杨长辉,田义,王磊,等.NaOH预处理对橡胶混凝土性能的影响[J].土木建筑与环境工程,2016,38(2):44-50. 
[6] 郑邦容,唐延丰,李佳骏,等.橡胶混凝土力学性能与耐久性能研究进展[J].混凝土与水泥制品,2022(9):88-91.
[7] 吴安利,高峰,郝贠洪,等.改性橡胶混凝土在复合盐冻融循环-风沙冲蚀作用下损伤研究[J].硅酸盐通报,2020,39(11):3609-3616,3635. 
[8] YOUSSF O,MILLS J E,HASSANLI R.Assessment of the Mechanical Performance of Crumb Rubber Concrete[J].Construction and Building Materials,2016,125:175-183. 
[9] IMAN M,HADI K,KIRK V.Enhancing Mechanical Performance of Rubberised Concrete Pavements with Sodium Hydroxide Treatment[J].Materials and Structures,2016,49(3):813-827. 
[10] COPETTI C M,BORGES P M,SQUIAVON J Z,et al.Evaluation of Tire Rubber Surface Pre-Treatment and Silica Fume on Physical-Mechanical Behavior and Microstructural Properties of Concrete[J].Journal of Cleaner Production,2020,256:120670.
[11] 李伟,黄振,王晓初,等.胶乳改性橡胶混凝土基本力学性能研究[J].建筑科学,2015,31(3):68-72.
[12] 李庆来,王美华,陈龙珠,等.乳化沥青改性橡胶混凝土试验研究[J].混凝土,2014(3):98-101. 
[13] 陈卓明,李丽娟,熊哲.橡胶混凝土胶凝材料改进试验研究[J].混凝土与水泥制品,2019(9):90-94.
[14] 沙涛.橡胶颗粒混凝土技术性能分析及改良工艺研究[D].吉林:吉林大学,2015. 
[15] 王卫中,冯忠绪.混凝土搅拌工艺方案比较[J].工程机械,2006(11):62-65,115.

苏有文,杨钦淞,高梦秋.NaOH和聚合物乳液复合改性橡胶混凝土的性能研究[J].混凝土与水泥制品,2023(6):94-97.

SU Y W,YANG Q S,GAO M Q.Study on Performance of NaOH and Polymer Lotion Composite Modified Crumb Rubber Concrete[J].China Concrete and Cement Product,2023(6):94-97.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州