粉煤灰和矿粉对OPC-SAC基路面修补材料性能的影响

Effect of fly ash and mineral powder on performance of OPC-SAC based pavement repair materials

2023年第8期

OPC-SAC基路面修补材料；凝结时间；流动度；抗压强度；拉伸黏结强度；水化热

OPC-SAC based pavement repair material; Setting time; Fluidity; Compressive strength; Tensile bond strength; Hydration heat

2023年第8期

10.19761/j.1000-4637.2023.08.093.05

任双倩1，赵世冉1，宋心2，王欢2，袁倩男1

1.陕西恒盛混凝土有限公司，陕西西安 710068；2.陕西秦汉恒盛新型建材科技股份有限公司，陕西西安712000

任双倩1，赵世冉1，宋心2，王欢2，袁倩男1

任双倩,赵世冉,宋心,等.粉煤灰和矿粉对OPC-SAC基路面修补材料性能的影响[J].混凝土与水泥制品,2023(8):93-96,104.

REN S Q,ZHAO S R,SONG X,et al.Effect of fly ash and mineral powder on performance of OPC-SAC based pavement repair materials[J].China Concrete and Cement Products,2023(8):93-96,104.

浏览量:

1000

摘要：研究了m粉煤灰∶m矿粉（1∶0、2∶1、1∶1、1∶2、0∶1）对普通硅酸盐水泥-硫铝酸盐水泥（OPC-SAC）基路面修补材料凝结时间、流动度、抗压强度、拉伸黏结强度和水化放热行为的影响。结果表明：掺入粉煤灰和矿粉会降低OPC-SAC基路面修补材料的水化放热量和水化放热速率，延长凝结时间，增大流动度，降低抗压强度，提高拉伸黏结强度；随着矿物掺合料中矿粉占比的增大，OPC-SAC基路面修补材料的凝结时间延长，流动度、抗压强度和拉伸黏结强度均先增大后减小，最佳m粉煤灰∶m矿粉为1∶2。 Abstract: The effects of mfly ash∶mmineral powder (1∶0, 2∶1, 1∶1, 1∶2, 0∶1) on the setting time, fluidity, compressive strength, tensile bond strength and hydration exothermic behavior of ordinary Portland cement-sulphoaluminate cement(OPC-SAC) based pavement repair materials were studied. The results show that adding fly ash and mineral powder can reduce the hydration heat release and hydration heat release rate of OPC-SAC based pavement repair materials, extend the setting time, increase fluidity, reduce compressive strength, and improve tensile bond strength. As the content of mineral powder in the admixture increases, the setting time of OPC-SAC based pavement repair materials is prolonged, and the fluidity, compressive strength, and tensile bond strength first increase and then decrease. The optimal ratio of mfly ash∶mmineral powder is 1∶2.

英文名 : Effect of fly ash and mineral powder on performance of OPC-SAC based pavement repair materials

刊期 : 2023年第8期

关键词 : OPC-SAC基路面修补材料；凝结时间；流动度；抗压强度；拉伸黏结强度；水化热

Key words : OPC-SAC based pavement repair material; Setting time; Fluidity; Compressive strength; Tensile bond strength; Hydration heat

刊期 : 2023年第8期

DOI : 10.19761/j.1000-4637.2023.08.093.05

文章编号 :

基金项目 :

作者 : 任双倩1，赵世冉1，宋心2，王欢2，袁倩男1

单位 : 1.陕西恒盛混凝土有限公司，陕西西安 710068；2.陕西秦汉恒盛新型建材科技股份有限公司，陕西西安712000

任双倩1，赵世冉1，宋心2，王欢2，袁倩男1

任双倩,赵世冉,宋心,等.粉煤灰和矿粉对OPC-SAC基路面修补材料性能的影响[J].混凝土与水泥制品,2023(8):93-96,104.

REN S Q,ZHAO S R,SONG X,et al.Effect of fly ash and mineral powder on performance of OPC-SAC based pavement repair materials[J].China Concrete and Cement Products,2023(8):93-96,104.





摘要

参数

结论

参考文献

引用本文

摘要：研究了m_粉煤灰∶m_矿粉（1∶0、2∶1、1∶1、1∶2、0∶1）对普通硅酸盐水泥-硫铝酸盐水泥（OPC-SAC）基路面修补材料凝结时间、流动度、抗压强度、拉伸黏结强度和水化放热行为的影响。结果表明：掺入粉煤灰和矿粉会降低OPC-SAC基路面修补材料的水化放热量和水化放热速率，延长凝结时间，增大流动度，降低抗压强度，提高拉伸黏结强度；随着矿物掺合料中矿粉占比的增大，OPC-SAC基路面修补材料的凝结时间延长，流动度、抗压强度和拉伸黏结强度均先增大后减小，最佳m粉煤灰∶m矿粉为1∶2。

Abstract: The effects of mfly ash∶mmineral powder (1∶0, 2∶1, 1∶1, 1∶2, 0∶1) on the setting time, fluidity, compressive strength, tensile bond strength and hydration exothermic behavior of ordinary Portland cement-sulphoaluminate cement(OPC-SAC) based pavement repair materials were studied. The results show that adding fly ash and mineral powder can reduce the hydration heat release and hydration heat release rate of OPC-SAC based pavement repair materials, extend the setting time, increase fluidity, reduce compressive strength, and improve tensile bond strength. As the content of mineral powder in the admixture increases, the setting time of OPC-SAC based pavement repair materials is prolonged, and the fluidity, compressive strength, and tensile bond strength first increase and then decrease. The optimal ratio of mfly ash∶mmineral powder is 1∶2.

扫二维码用手机看

[1] 张琳.水泥混凝土路面快速修补材料的研究与开发[D].西安:长安大学,2009.
[2] 傅智.水泥混凝土路面施工技术[M].上海:同济大学出版社,2004.
[3] 张德明,王永超.水泥混凝土路面快速修补材料综述[J].公路交通科技(应用技术版),2015,11(4):85-86,89.
[4] 叶勇.混凝土路面快速修补材料研究[J].公路交通科技(应用技术版),2014,10(1):53-55.
[5] 张春阳,江守恒.路面快速修补材料力学性能研究[J].低温建筑技术,2014,36(5):22-23.
[6] 雷毅.水泥混凝土路面快速修补用聚合物改性水泥基材料的研究[D].长沙:湖南大学,2014.
[7] 李保红.水泥混凝土路面局部破损快速修补材料的研究[D].长沙:湖南大学,2005.
[8] TANG S W,ZHU H G,LI Z J,et al.Hydration stage identification and phase transformation of calcium sulfoaluminate cement at early age[J].Construction and Building Materials,2015,75:11-18.
[9] 杨云.外掺硫铝酸盐水泥对混凝土早期强度影响研究[D].重庆:重庆大学,2019.
[10] TRAUCHESSEC R,MECHLING J M,LECOMTE A,et al.Hydration of ordinary Portland cement and calcium sulfoaluminate cement blends[J].Cement and Concrete Composites,2015,56:106-114.
[11] 李红英,马志恒,周少煜,等.矿物掺料对复合胶凝快速修补材料的性能影响[J].江苏建材,2015(1):22-25.
[12] 简险峰,王栋民,黄天勇,等.普通硅酸盐水泥基矿物掺合料对硫铝酸盐水泥性能的影响[J].硅酸盐通报,2014,33(4):984-987.
[13] 丁向群,赵欣悦,徐晓婉,等.矿物掺合料对硫铝酸盐水泥-普通硅酸盐水泥复合体系性能的影响[J].新型建筑材料,2020,47(3):40-44.
[14] 左李萍,蒙海宁,许彦明,等.粉煤灰与矿粉对地聚物水泥性能影响的研究[J].砖瓦,2018(10):29-32.
[15] 何廷树,王福川.土木工程材料[M].北京:中国建筑工业出版社,2013.
[16] 吕进,刘建忠.不同矿物掺合料对钢纤维与混凝土粘结性能的影响[C]//江苏省硅酸盐学会.江苏省第九届混凝土新技术研讨会论文集.南京:江苏省硅酸盐学会,2014:112-113.

上一个

聚丙烯酰胺对钢渣混凝土性能的影响

下一个

超疏水铁尾矿石的制备及其对混凝土性能的影响

头部文案

粉煤灰和矿粉对OPC-SAC基路面修补材料性能的影响

相关文件