先张自平衡预应力技术在桥面板构件中的应用

Application of pre-tensioned self-equilibrium prestressing technology in bridge deck components

2023年第11期

桥面连续；先张自平衡；预应力中空管；简支空心板

Continuous deck; Pre-tensioned self-equilibrium; Pre-stressed middle air duct; Simply supported slab beam

2023年第11期

10.19761/j.1000-4637.2023.11.041.06

浙江省公路科技计划项目（2016-2-12）。

陈飞1，朱春东2，*，王勇3，4

1.嘉兴南湖学院建筑工程学院，浙江嘉兴 314001；2.嘉兴市公路与运输管理中心，浙江嘉兴 314001；3.杭州丰强工程设计咨询研究院有限公司，浙江杭州 310008；4.杭州图强工程材料有限公司，浙江杭州 310008

陈飞1，朱春东2，*，王勇3，4

陈飞,朱春东,王勇.先张自平衡预应力技术在桥面板构件中的应用[J].混凝土与水泥制品,2023(11):41-46.

CHEN F,ZHU C D,WANG Y.Application of pre-tensioned self-equilibrium prestressing technology in bridge deck components[J].China Concrete and Cement Products,2023(11):41-46.

浏览量:

1000

摘要：为解决传统桥面连续构造开裂、桥面径流渗漏的问题，采用先张自平衡预应力技术进行了桥面连续构造改造，通过预应力加载试验，研究了改造后桥面连续构造的受力性能。结果表明：在100 kN张拉力条件下，中空管的预应力损失约为16 MPa，预应力传递长度约为250 mm；桥面板构件实测储备纵向应力约为2.5~2.9 MPa；锚固区横向应力波形明显区域纵向长为350 mm，锚下劈裂应力峰值为1.20~1.30 MPa。工程实际应用表明：采用先张自平衡预应力技术的预应力桥面连续构造具有施工简便、适应性好、预应力施加可靠的特点，经过5年运营，未现可见病害，相比病害显著的传统方案具有显著的经济和社会效益。 Abstract: In order to solve the problem of cracking on traditional bridge decks and the leakage of bridge deck runoff, the pre-tensioned self-equilibrium prestressing technology was adopted to improve the mechanical performance of the link slab of the bridge deck, and the prestressed loading test was carried out. The results show that under the tensile force of 100 kN, the loss of prestress in the middle air duct is about 16 MPa, the transfer length of prestress is about 250 mm, the measured reserve compressive stress of the bridge deck component is 2.5~2.9 MPa, and the longitudinal length of the anchorage zone with obvious transverse stress waveform is 350 mm, the peak splitting stress under the anchor is 1.20~1.30 MPa. The actual bridge engineering application shows that the link slab of bridge deck using pre-tensioned self-equilibrium technology has the characteristics of simple construction, good adaptability, and reliable pre-stressed application. After 5-year operation, no visible diseases have been observed, and compared to traditional schemes, it has significant economic and social benefits.

英文名 : Application of pre-tensioned self-equilibrium prestressing technology in bridge deck components

刊期 : 2023年第11期

关键词 : 桥面连续；先张自平衡；预应力中空管；简支空心板

Key words : Continuous deck; Pre-tensioned self-equilibrium; Pre-stressed middle air duct; Simply supported slab beam

刊期 : 2023年第11期

DOI : 10.19761/j.1000-4637.2023.11.041.06

文章编号 :

基金项目 : 浙江省公路科技计划项目（2016-2-12）。

作者 : 陈飞1，朱春东2，*，王勇3，4

单位 : 1.嘉兴南湖学院建筑工程学院，浙江嘉兴 314001；2.嘉兴市公路与运输管理中心，浙江嘉兴 314001；3.杭州丰强工程设计咨询研究院有限公司，浙江杭州 310008；4.杭州图强工程材料有限公司，浙江杭州 310008

陈飞1，朱春东2，*，王勇3，4

陈飞,朱春东,王勇.先张自平衡预应力技术在桥面板构件中的应用[J].混凝土与水泥制品,2023(11):41-46.

CHEN F,ZHU C D,WANG Y.Application of pre-tensioned self-equilibrium prestressing technology in bridge deck components[J].China Concrete and Cement Products,2023(11):41-46.





摘要

参数

结论

参考文献

引用本文

Abstract: In order to solve the problem of cracking on traditional bridge decks and the leakage of bridge deck runoff, the pre-tensioned self-equilibrium prestressing technology was adopted to improve the mechanical performance of the link slab of the bridge deck, and the prestressed loading test was carried out. The results show that under the tensile force of 100 kN, the loss of prestress in the middle air duct is about 16 MPa, the transfer length of prestress is about 250 mm, the measured reserve compressive stress of the bridge deck component is 2.5~2.9 MPa, and the longitudinal length of the anchorage zone with obvious transverse stress waveform is 350 mm, the peak splitting stress under the anchor is 1.20~1.30 MPa. The actual bridge engineering application shows that the link slab of bridge deck using pre-tensioned self-equilibrium technology has the characteristics of simple construction, good adaptability, and reliable pre-stressed application. After 5-year operation, no visible diseases have been observed, and compared to traditional schemes, it has significant economic and social benefits.

扫二维码用手机看

[1] 张彬,朱栋,徐建炜,等.浙江省中小跨径混凝土桥梁整体状况与典型病害研究[J].重庆交通大学学报(自然科学版),2013, 32(增刊):742-746.
[2] 王立成,穆林钧,邹凯.裂缝对混凝土中水分传输影响研究进展[J].水利学报,2021,52(6):647-658,672.
[3] 马俊军,蔺鹏臻,刘应龙,等.基于元胞自动机的开裂混凝土氯离子扩散模拟与分析[J].西南交通大学学报,2022,57(2):360-368.
[4] 张菊辉,方成.氯盐侵蚀下钢筋混凝土结构寿命的预测研究进展[J].材料科学与工程学报,2019,37(5):848-854,859.
[5] 张灵灵,陆春华,徐可,等.荷载裂缝和养护龄期对混凝土内氯离子传输影响研究[J].硅酸盐通报,2020,39(4):1100-1106.
[6] 金立兵,王珍,梁新亚,等.荷载作用下混凝土中氯离子传输的数值分析方法[J].混凝土,2020(9):60-64.
[7] 王海龙,俞宁,吴远建,等.开裂混凝土中碳钢与不锈钢钢筋腐蚀速率研究[J].水力发电学报,41(9):1-10.
[8] 张予培,刘斌云,王鑫.混凝土中钢筋锈胀体积的现场测量方法[J].混凝土,2019(2):146-149.
[9] 胡志坚,夏雷雷,程晨,等.钢筋混凝土构件锈蚀开裂与锈胀力分析[J].哈尔滨工业大学学报,2020,52(3):99-105.
[10] 林红威,赵羽习,郭彩霞,等.锈胀开裂钢筋混凝土粘结疲劳性能试验研究[J].工程力学,2020,37(1):98-107.
[11] 虞爱平,赵艳林,冯依锋.锈蚀钢筋混凝土黏结破坏在线监测试验研究[J].混凝土,2013(10):151-156.
[12] 陈瑞明,向阳开,梁路,等.冻融循环与预应力共同作用下混凝土抗压强度试验研究[J].材料导报,2022,36(增刊):287-291.
[13] 韩飞,王虎,淡丹辉,等.考虑桥面不平整度的铺装层动力响应研究[J].同济大学学报(自然科学版),2017,45(9):1284-1289,1297.
[14] 薛宇欣,周勇军,赵煜,等.基于空间桥面不平顺的简支梁桥冲击系数研究[J].合肥工业大学学报(自然科学版),2021,44(3):389-395.
[15] 殷新锋,丰锦铭,刘扬,等.基于桥面退化模型的在役桥梁冲击系数研究[J].应用力学学报,2016,33(3):516-522,553.
[16] 王城泉,申永刚,王岗,等.空心板梁桥桥面连续构造的受力特性试验[J].浙江大学学报(工学版),2016,50(8):1438-1445.
[17] 庄一舟,徐亮,程俊峰,等.简支梁桥桥面连续结构力学特性理论分析[J].中国公路学报,2017,30(7):73-85.
[18] GERGESS A N,HAWI P F.Structural behavior of debonded link-slabs in continuous bridge decks[J].Journal of Bridge Engineering,2019,24(5):852-863.
[19] LEPECH M,LI V C.Application of ECC for bridge deck link slabs [J].Materials and Structures,2009,42(9):1185-1195.
[20] ZHANG L,ZHENG Y,YU Y,et al.Structural performance evaluation of ECC link slabs reinforced with FRP bars for jointless bridge decks[J].Construction and Building Materials, 2021,304:236-269.
[21] CHU K,HOSSAIN K M A,LACHEMI M.Fatigue behavior of GFRP-reinforced ECC link slabs under variable stress levels and number of cycles[J].Engineering Structures,2020,222:187-193.
[22] 郭丽萍,朱春东,范永根,等.桥面连接板修补用高延性水泥基复合材料的设计与应用[J].混凝土与水泥制品,2016(12):36-39.
[23] 邵旭东,周银东,曹君辉,等.钢简支梁的新型桥面连续结构抗弯性能试验研究[J].土木工程学报,2019,52(12):80-92.
[24] 潘志炎,茅兆祥,刘敏,等.简支梁桥面连续构造的有限元分析与改进[J].公路交通科技,2010,27(4):89-94.
[25] 王岗,谢旭,王城泉,等.简支梁桥拱型桥面连续构造的受力性能[J].浙江大学学报(工学版),2014,48(6):1049-1057.
[26] 王勇,陈向阳,朱春东.先张自平衡中空预应力棒在预应力混凝土中应用前 [C]//中国公路学会桥梁和结构工程学会.中国公路学会2017年全国桥梁学术会议论文集.广州:人民交通出版社股份有限公司,2017:642-645.
[27] 林超,张程林,王勇.预应力中空棒构件设计与力学特性[J].山东大学学报(工学版),2020,50(5):7-9.

上一个

预制混凝土构件U型连接筋的单肢锚固性能试验研究

下一个

盾构砂对减水剂吸附行为及水泥砂浆流变性能的影响

头部文案

先张自平衡预应力技术在桥面板构件中的应用

相关文件