HRB500钢筋轻骨料混凝土柱轴压承载力试验研究及可靠度分析

Test and reliability analysis of the axial compressive bearing capacity of HRB500 reinforced lightweight aggregate concrete columns

2024年第1期

高强钢筋；页岩陶粒混凝土；轴压柱；承载力；可靠度

High-strength steel bar; Shale ceramsite concrete; Axial compression column; Bearing capacity; Reliability

2024年第1期

10.19761/j.1000-4637.2024.01.051.05

张威，邵永健*，朱号令

苏州科技大学土木工程学院，江苏苏州 215011

张威，邵永健*，朱号令

张威,邵永健,朱号令.HRB500钢筋轻骨料混凝土柱轴压承载力试验研究及可靠度分析[J].混凝土与水泥制品,2024(1):51-55.

ZHANG W,SHAO Y J,ZHU H L,et al.Test and reliability analysis of the axial compressive bearing capacity of HRB500 reinforced lightweight aggregate concrete columns[J].China Concrete and Cement Products,2024(1):51-55.

浏览量:

1000

摘要：为了研究高强钢筋页岩陶粒混凝土轴压柱的承载力，制作了8根试件，研究了配筋率、配箍率、混凝土强度等对其承载力和破坏形态的影响。此外，得到了相关文献的有关统计参数，采用JC法，并利用Matlab软件编程迭代求解高强钢筋页岩陶粒混凝土轴压柱的可靠度指标。结果表明：在其他设计参数相同前提下，轴压柱的可靠度指标随着配筋率、配箍率、稳定系数以及截面面积的增大而增大，随着荷载效应比的增大而降低；JGJ/T 12—2019《轻骨料混凝土应用技术标准》中的轴心受压承载力计算公式可以满足GB 50068—2018《建筑结构可靠性设计统一标准》中的可靠指标要求。 Abstract: In order to study the reliability of high-strength reinforced shale ceramsite concrete columns under axial compression, 8 specimens were made and the effects of factors such as reinforcement ratio, hoop ratio, and concrete strength on the bearing capacity and failure mode were studied. In addition, relevant statistical parameters of the specimens were obtained by analyzing relevant literature, and the JC method was used to iteratively solve the reliability index of high-strength reinforced shale ceramsite concrete axial compression columns by using Matlab software programming. The results show that under the same design parameters, the reliability index of axial compression columns increases with the increase of reinforcement ratio, hoop ratio, concrete strength, and cross-sectional area, but decreases with the increase of load ratio. The analysis also indicates that the formula for calculating the axial compressive bearing capacity of the JGJ/T 12—2019 Technical Standard for Application of Lightweight Aggregate Concrete can meet the requirements of the reliability index in the GB 50068—2018 Unified Standard for Reliability Design of Building Structures.

英文名 : Test and reliability analysis of the axial compressive bearing capacity of HRB500 reinforced lightweight aggregate concrete columns

刊期 : 2024年第1期

关键词 : 高强钢筋；页岩陶粒混凝土；轴压柱；承载力；可靠度

Key words : High-strength steel bar; Shale ceramsite concrete; Axial compression column; Bearing capacity; Reliability

刊期 : 2024年第1期

DOI : 10.19761/j.1000-4637.2024.01.051.05

文章编号 :

基金项目 :

作者 : 张威，邵永健*，朱号令

单位 : 苏州科技大学土木工程学院，江苏苏州 215011

张威，邵永健*，朱号令

张威,邵永健,朱号令.HRB500钢筋轻骨料混凝土柱轴压承载力试验研究及可靠度分析[J].混凝土与水泥制品,2024(1):51-55.





摘要

参数

结论

参考文献

引用本文

Abstract: In order to study the reliability of high-strength reinforced shale ceramsite concrete columns under axial compression, 8 specimens were made and the effects of factors such as reinforcement ratio, hoop ratio, and concrete strength on the bearing capacity and failure mode were studied. In addition, relevant statistical parameters of the specimens were obtained by analyzing relevant literature, and the JC method was used to iteratively solve the reliability index of high-strength reinforced shale ceramsite concrete axial compression columns by using Matlab software programming. The results show that under the same design parameters, the reliability index of axial compression columns increases with the increase of reinforcement ratio, hoop ratio, concrete strength, and cross-sectional area, but decreases with the increase of load ratio. The analysis also indicates that the formula for calculating the axial compressive bearing capacity of the JGJ/T 12—2019 Technical Standard for Application of Lightweight Aggregate Concrete can meet the requirements of the reliability index in the GB 50068—2018 Unified Standard for Reliability Design of Building Structures.

扫二维码用手机看

[1] 邵永健,孙敏,刘强,等.陶粒混凝土局部抗压承载力的计算及其可靠度分析[J].公路交通科技,2008(4):67-72.
[2] 邵永健.轻骨料混凝土材料的强度指标及其统计参数[J].工业建筑,2007(8):82-85.
[3] 申成成.HRB600钢筋混凝土轴压短柱及偏压柱试验研究[D].天津:河北工业大学,2018.
[4] 尹新生,杜芹芹,黄春华.C105混凝土管桩轴心受压承载力的可靠度分[J].混凝土,2017(3):56-58.
[5] 毛达岭.500 MPa级钢筋混凝土受压构件受力性能研究[D].郑州:郑州大学,2008.
[6] 张程远,邵永健,朱爱萍,等.HRB500钢筋轻骨料混凝土轴心受压构件试验研究[J].混凝土与水泥制品,2018(12):61-65.
[7] 中华人民共和国住房和城乡建设部.轻骨料混凝土应用技术标准:JGJ/T 12—2019[S].北京:中国建筑工业出版,2019.
[8] 中华人民共和国住房和城乡建设部.工程结构通用规范:GB 55001—2021[S].北京:中国建筑工业出版,2021.
[9] 中华人民共和国住房和城乡建设部.混凝土结构设计规范(2015年版):GB 50010—2010[S].北京:中国建筑工业出版,2010.
[10] 中华人民共和国住房和城乡建设部.建筑结构可靠性设计统一标准:GB 50068—2018[S].北京:中国建筑工业出版社,2018.
[11] 中华人民共和国建设部.轻骨料混凝土技术规程:JGJ 51—2002[S].北京:中国建筑工业出版社,2002.
[12] 中华人民共和国住房和城乡建设部.建筑结构荷载规范:GB 50009—2012[S].北京:中国建筑工业出版社,2012.
[13] 中华人民共和国住房和城乡建设部.轻骨料混凝土结构设计规程:JGJ 12—2006[S].北京:中国建筑工业出版社,2006.
[14] 向晓峰,郭志昆,刘峰.高强轻骨料混凝土的应用与研究现状[J].工业建筑,2005,35:645-650.
[15] 中华人民共和国住房和城乡建设部.混凝土结构试验方法标准:GB/T 50152—2012[S].北京:中国建筑工业出版社,2012.
[16] 刘冬明.RPC混凝土轴心受压柱试验研究及可靠度分析[D].长沙:湖南大学,2015．
[17] 刘靓．加固轴压混凝土柱的有限元及可靠度分析[D].哈尔滨:哈尔滨工业大学,2013．
[18] 钟小平,金伟良．钢筋混凝土结构基于耐久性的可靠度设计方法[J]．土木工程学报,2016(5):31－39．
[19] 王静.500 MPa级高强钢筋混凝土受压柱试验研究分析[D]．青岛:青岛理工大学,2010．
[20] 黄展魏,王安辉,张艳芳,等.陶粒内养护超高性能混凝土(UHPC)的制备与性能研究[J].混凝土与水泥制品,2023(10):1-5.

上一个

配筋UHPC构件轴心受拉承载力计算研究

下一个

超高性能混凝土设计理论与磷石膏高质利用研究进展

头部文案

HRB500钢筋轻骨料混凝土柱轴压承载力试验研究及可靠度分析

相关文件