粉末状缓释型聚羧酸减水剂的制备及性能研究

Preparation and properties of set retarding type polycarboxylate superplasticizer powder

2024年第5期

新型聚醚大单体；离心喷雾；缓释；粉末；工业生产

New polyether large monomer; Centrifugal spray; Set retarding; Powder; Industrial production

2024年第5期

10.19761/j.1000-4637.2024.05.023.06

逄鲁峰1，2，安昊文1，3，*，赵淑静4，王恒2

1.山东建筑大学土木工程学院，山东济南 250100；2.山东华迪建筑科技有限公司，山东济南 251400；3.日照城投建设集团有限公司，山东日照 276800；4.山东省调水工程运行维护中心青岛分中心，山东青岛 266035

逄鲁峰1，2，安昊文1，3，*，赵淑静4，王恒2

逄鲁峰,安昊文,赵淑静,等.粉末状缓释型聚羧酸减水剂的制备及性能研究[J].混凝土与水泥制品,2024(5):23-28.

PANG L F,AN H W,ZHAO S J,et al.Preparation and properties of set retarding type polycarboxylate superplasticizer powder[J].China Concrete and Cement Products,2024(5):23-28.

浏览量:

1000

摘要：以乙二醇单乙烯基聚乙二醇（EPEG）为大单体，调节丙烯酸羟乙酯和丙烯酸羟丙酯与大单体的摩尔质量比，以巯基丙酸为链转移剂，双氧水与次磷酸钠为氧化还原体系，并用中和溶剂调节减水剂母液pH值，制备了一种适用于离心喷雾干燥技术的粉末状缓释型聚羧酸减水剂PC-1000。通过正交试验确定了合成PC-1000粉末的最佳工艺参数为酸醚比3.0，酯醚比4.5，链转移剂用量0.36 %（占大单体的质量比），母液pH值为8。性能测试结果表明，通过离心喷雾技术制备出的PC-1000粉末在净浆测试中2 h流动度无损失，表现出优异的保坍效果。PC-1000粉末已在灌浆料和压浆料中成功应用。 Abstract: Ethylene glycol monovinyl polyethylene glycol (EPEG) was used as large monomer to adjust the molar mass ratio of hydroxyethyl acrylate and hydroxyl propyl acrylate to large monomer. By using mercaptopropionic acid as chain transfer agent, hydrogen peroxide and sodium hypophosphate as oxidation-reduction system, and adjusting the pH value of the mother liquor of the polycarboxylate superplasticizer with neutralizer, a kind of powder set retarding polycarboxylate superplasticizer PC-1000 powder suitable for centrifugal spray drying was prepared. The optimum process parameters are determined by the orthogonal test as follows. Acid ether ratio is 3.0, ester ether ratio is 4.5, and chain transfer agent content is 0.36%(mass ratio of large monomer). The performance test results show that the PC-1000 powder prepared by centrifugal spray technology has no loss of fluidity in 2 h in the actual slurry test, showing excellent slump retention effect. PC-1000 powder has been successfully applied in grout and pressed slurry.

英文名 : Preparation and properties of set retarding type polycarboxylate superplasticizer powder

刊期 : 2024年第5期

关键词 : 新型聚醚大单体；离心喷雾；缓释；粉末；工业生产

Key words : New polyether large monomer; Centrifugal spray; Set retarding; Powder; Industrial production

刊期 : 2024年第5期

DOI : 10.19761/j.1000-4637.2024.05.023.06

文章编号 :

基金项目 :

作者 : 逄鲁峰1，2，安昊文1，3，*，赵淑静4，王恒2

单位 : 1.山东建筑大学土木工程学院，山东济南 250100；2.山东华迪建筑科技有限公司，山东济南 251400；3.日照城投建设集团有限公司，山东日照 276800；4.山东省调水工程运行维护中心青岛分中心，山东青岛 266035

逄鲁峰1，2，安昊文1，3，*，赵淑静4，王恒2

逄鲁峰,安昊文,赵淑静,等.粉末状缓释型聚羧酸减水剂的制备及性能研究[J].混凝土与水泥制品,2024(5):23-28.

PANG L F,AN H W,ZHAO S J,et al.Preparation and properties of set retarding type polycarboxylate superplasticizer powder[J].China Concrete and Cement Products,2024(5):23-28.





摘要

参数

结论

参考文献

引用本文

Abstract: Ethylene glycol monovinyl polyethylene glycol (EPEG) was used as large monomer to adjust the molar mass ratio of hydroxyethyl acrylate and hydroxyl propyl acrylate to large monomer. By using mercaptopropionic acid as chain transfer agent, hydrogen peroxide and sodium hypophosphate as oxidation-reduction system, and adjusting the pH value of the mother liquor of the polycarboxylate superplasticizer with neutralizer, a kind of powder set retarding polycarboxylate superplasticizer PC-1000 powder suitable for centrifugal spray drying was prepared. The optimum process parameters are determined by the orthogonal test as follows. Acid ether ratio is 3.0, ester ether ratio is 4.5, and chain transfer agent content is 0.36%(mass ratio of large monomer). The performance test results show that the PC-1000 powder prepared by centrifugal spray technology has no loss of fluidity in 2 h in the actual slurry test, showing excellent slump retention effect. PC-1000 powder has been successfully applied in grout and pressed slurry.

关键词:

the

pc-1000

and

ratio

powder

large

扫二维码用手机看

[1] 逄鲁峰,李崇智,王栋民.聚羧酸高性能减水剂的合成试验研究[J].武汉理工大学学报,2009,31(7):108-110.
[2] 赵连鸿,赵红娟,刘涛,等.离心喷雾干燥温度对FCC催化剂成型的影响[J].化学工程,2020,48(4):33-36,49.
[3] 莫港宇,夏良志.聚羧酸减水剂过热蒸汽喷雾干燥数值模拟[J].化学工程,2022,50(7):32-37.
[4] 潘阳,汪源,汪苏平,等.高保坍型聚羧酸减水剂的制备及其在水溶液中的自组装行为[J].材料导报,2021,35(增刊):167-171.
[5] 马正先,宋沛霖,周在波,等.新型高保坍降粘型聚羧酸减水剂制备及性能评价[J].硅酸盐通报,2018,37(11):3386-3391.
[6] 王稷良,周明凯,贺图升,等.石粉对机制砂混凝土抗渗透性和抗冻融性能的影响(英文)[J].硅酸盐学报,2008(4):482-486.
[7] 赖华珍.高适应性聚羧酸减水剂的制备及性能研究[J].高分子通报,2022(12):107-112.
[8] 田润,张永兴,周晟,等.抗泥敏感性聚羧酸减水剂的研究进展[J].高分子材料科学与工程,2020,36(11):175-182,190.
[9] 张兰芳,刘丽娜,曹胜.响应面方法优化碱激发矿渣-石粉水泥砂浆的研究[J].材料导报,2017,31(24):15-19.
[10] 张翠珍,唐新德,陈晓东,等.聚羧酸减水剂的粘土耐受性研究进展[J].材料导报,2022,36(增刊):503-507.
[11] 陈晓东,唐新德,张翠珍,等.缓释型聚羧酸减水剂的研究进展[J].材料导报,2022,36(增刊):499-502.
[12] 黄泽文,杨海明,谭洪波,等.不同酯类单体对缓释型聚羧酸减水剂分散性能及分散保持性能的影响[J].硅酸盐通报,2022,41(10):3485-3492,3500.
[13] 汪源,汪苏平,张亚利,等.降粘型聚羧酸减水剂的制备及性能[J].材料导报,2019,33(增刊):646-650.
[14] 王倩,王立彬,任建波,等.不同释放时间保坍型聚羧酸高性能减水剂研究[J].混凝土与水泥制品,2020(11):20-25.
[15] 张少敏.新型聚醚大单体低温制备聚羧酸减水剂及其性能研究[J].硅酸盐通报,2020,39(9):2844-2848.
[16] 刘少兵,程绍娟,陈森章,等.EPEG缓释型聚羧酸减水剂的常温制备与性能研究[J].混凝土与水泥制品,2023(2):23-27.
[17] 周俊,杨睿,王稚阳,等.VPEG-保坍型聚羧酸减水剂的制备及其性能研究[J].功能材料,2023,54(2):2189-2196,2216.
[18] 史绘洲,王辉.高保坍型聚羧酸减水剂的合成及其对混凝土性能的影响分析[J].功能材料,2022,53(8):8196-8201.
[19] 李修固,王立艳,戚龙娟,等.一种缓释保坍聚羧酸减水剂的制备及性能研究[J].化学研究与应用,2022,34(9):2186-2192.
[20] 何廷树,杨仁和,徐一伦,等.酯醚型聚羧酸减水剂的制备及性能（英文）[J].硅酸盐学报,2018,46(2):218-223.
[21] 戢文占,赵亚丁,郭海山,等.高强钢筋连接用套筒灌浆料的试验研究[J].建筑结构,2020,50(增刊):640-644.

上一个

基于响应面法的UHPC复合胶凝材料体系优化研究

下一个

水泥基自修复微胶囊的制备及其修复效果研究

头部文案

粉末状缓释型聚羧酸减水剂的制备及性能研究

相关文件