成达万高铁资阳沱江大桥C60高抗裂主塔混凝土的研究

Study on the C60 high crack resistance main tower concrete of Ziyang Tuojiang Bridge of Chengdu-Dazhou-Wanzhou high-speed railway

2024年第5期

大体积混凝土；降黏剂；抗裂剂；抗压强度；孔结构；干燥收缩；绝热温升

Mass concrete; Viscosity reducer; Anti-cracking agent; Compressive strength; Pore structure; Drying shrinkage; Adiabatic temperature rise

2024年第5期

10.19761/j.1000-4637.2024.05.090.04

罗德立

成兰铁路有限责任公司，四川成都 610037

罗德立

罗德立.成达万高铁资阳沱江大桥C60高抗裂主塔混凝土的研究[J].混凝土与水泥制品,2024(5):90-93.

LUO D L.Study on the C60 high crack resistance main tower concrete of Ziyang Tuojiang Bridge of Chengdu-Dazhou-Wanzhou high-speed railway[J].China Concrete and Cement Products,2024(5):90-93.

浏览量:

1000

摘要：为了解决成达万高铁资阳沱江大桥C60主塔混凝土高空养护作业难、开裂风险高等问题，通过单掺降黏剂、复掺降黏剂和抗裂剂对C60主塔混凝土的配合比进行了优化设计。结果表明：与基准组相比，单掺降黏剂、复掺降黏剂和抗裂剂均可改善混凝土的孔结构，降低孔隙率、干燥收缩和绝热温升，提高混凝土的抗裂性；与单掺降黏剂相比，复掺降黏剂和抗裂剂对混凝土的抗压强度略有不利，但仍满足设计要求，且对温度裂缝的抑制效果略差。 Abstract: In order to solve the problems of difficult high-altitude curing operation and high cracking risk of C60 main tower concrete of Ziyang Tuojiang Bridge of Chengdu-Dazhou-Wanzhou high-speed railway, the mix proportions of C60 main tower concrete was optimized by adding single viscosity reducer, compound viscosity reducer and anti-cracking agent. The results show that compared with the benchmark group, single addition of viscosity reducer, and compound addition of viscosity reducer and anti-cracking agent can improve the pore structure of concrete, reduce porosity, drying shrinkage and adiabatic temperature rise, and improve the crack resistance of concrete. Compared with single addition of viscosity reducer, compound addition of viscosity reducer and anti-cracking agent has a slightly unfavorable effect on the compressive strength of concrete, but still meets the design requirements and has a slightly poorer inhibition effect on the temperature cracks.

英文名 : Study on the C60 high crack resistance main tower concrete of Ziyang Tuojiang Bridge of Chengdu-Dazhou-Wanzhou high-speed railway

刊期 : 2024年第5期

关键词 : 大体积混凝土；降黏剂；抗裂剂；抗压强度；孔结构；干燥收缩；绝热温升

Key words : Mass concrete; Viscosity reducer; Anti-cracking agent; Compressive strength; Pore structure; Drying shrinkage; Adiabatic temperature rise

刊期 : 2024年第5期

DOI : 10.19761/j.1000-4637.2024.05.090.04

文章编号 :

基金项目 :

作者 : 罗德立

单位 : 成兰铁路有限责任公司，四川成都 610037

罗德立

罗德立.成达万高铁资阳沱江大桥C60高抗裂主塔混凝土的研究[J].混凝土与水泥制品,2024(5):90-93.

LUO D L.Study on the C60 high crack resistance main tower concrete of Ziyang Tuojiang Bridge of Chengdu-Dazhou-Wanzhou high-speed railway[J].China Concrete and Cement Products,2024(5):90-93.





摘要

参数

结论

参考文献

引用本文

Abstract: In order to solve the problems of difficult high-altitude curing operation and high cracking risk of C60 main tower concrete of Ziyang Tuojiang Bridge of Chengdu-Dazhou-Wanzhou high-speed railway, the mix proportions of C60 main tower concrete was optimized by adding single viscosity reducer, compound viscosity reducer and anti-cracking agent. The results show that compared with the benchmark group, single addition of viscosity reducer, and compound addition of viscosity reducer and anti-cracking agent can improve the pore structure of concrete, reduce porosity, drying shrinkage and adiabatic temperature rise, and improve the crack resistance of concrete. Compared with single addition of viscosity reducer, compound addition of viscosity reducer and anti-cracking agent has a slightly unfavorable effect on the compressive strength of concrete, but still meets the design requirements and has a slightly poorer inhibition effect on the temperature cracks.

扫二维码用手机看

[1] 陈宇.桥梁大体积混凝土水化热温度控制研究[D].成都:西南交通大学,2016.
[2] 陈开桥,陈志鹏,李勇波.抗裂材料在桥梁主塔大体积混凝土施工中的应用研究[J].交通科技,2023(2):107-111.
[3] 龙勇,刘爱林,董继红,等.马鞍山公铁两用长江大桥主航道桥桥塔混凝土抗裂技术研究[J].桥梁建设,2023,53(3):8-15.
[4] 安瑞楠,林鹏,陈道想,等.锚碇大体积混凝土智能通水温控方法与系统[J].清华大学学报(自然科学版),2024,64(4):601-611.
[5] 范中晶,郑晨路.基于深度学习的隧道混凝土温度滚动预测方法研究[J].隧道建设(中英文),2023,43(4):611-617.
[6] 刘毅,辛建达,张国新,等.大体积混凝土温控防裂智能监控技术[J].硅酸盐学报,2023,51(5):1228-1233.
[7] 庞超明,刘钊,冒云瑞,等.大体积混凝土中功能轻集料的应用与控温技术[J].建筑材料学报,2023,26(8):853-861.
[8] 王晴,任晓丹.基于徐变损伤理论的早龄期大体积混凝土化学-热-力多场耦合模型研究[J].工程力学,2023,40(3):225-237.
[9] 尹必晶.斜拉桥桥塔高强度混凝土的收缩综合调控研究[D].北京:北京交通大学,2020.
[10] 丁庆军,曹健,李超,等.应用于超高桥塔的低收缩C60自密实混凝土的研究[J].混凝土,2016(6):84-87.
[11] 闫志刚,安明喆,尹必晶,等.超高桥塔高强混凝土性能研究及收缩调控[J].铁道工程学报,2020,37(3):40-46.
[12] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
[13] 中华人民共和国住房和城乡建设部.普通混凝土长期性能和耐久性能试验方法标准:GB/T 50082—2009[S].北京:中国建筑工业出版社,2009.
[14] 中华人民共和国住房和城乡建设部.普通混凝土拌合物性能试验方法标准:GB/T 50080—2016[S].北京:中国建筑工业出版社,2016.
[15] 高超,曹永,汤国芳,等.降黏型复合矿物掺合料对C60超高泵送混凝土性能的影响[J].新型建筑材料,2022,49(9):23-26,34.
[16] 田帅,吕剑锋,李世华,等.矿物掺合料对高性能混凝土耐久性的影响[J].混凝土与水泥制品,2020(10):12-16.
[17] 吴中伟.混凝土科学技术近期发展方向的探讨[J].硅酸盐学报,1979(3):262-270.
[18] 余以明,徐文冰,吴柯,等.掺氧化镁抗裂剂的海工大体积混凝土配制及应用研究[J].新型建筑材料,2018,45(1):77-79,87.
[19] 曹丰泽,高玉亭,张慧杰,等.MgO膨胀剂在大体积混凝土结构中的抗裂效果研究[J].混凝土与水泥制品,2021(8):24-27.
[20] 王丙垒,明阳,沈超,等.掺MgO混凝土结构微膨胀发展历程的监测方法[J].新型建筑材料,2023,50(5):149-154,163.

上一个

地铁车站大体积混凝土温控抗裂防渗性能研究

下一个

试验方法对喷射混凝土用液体无碱速凝剂检测结果的影响

头部文案

成达万高铁资阳沱江大桥C60高抗裂主塔混凝土的研究

相关文件