减缩剂对水泥砂浆及超高性能混凝土收缩性能的影响
Effect of shrinkage reducer on shrinkage properties of mortar and ultra-high performance concrete
2024年第6期
减缩剂;水泥砂浆;塑性收缩开裂;超高性能混凝土;收缩率
Shrinkage reducer; Cement mortar; Plastic shrinkage cracking; Ultra-high performance concrete; Shrinkage rate
2024年第6期
10.19761/j.1000-4637.2024.06.018.05
邹小童1,武建好1,李星辰1,王佳乐1,光鉴淼2
1.江苏双龙集团有限公司,江苏 南京 211103;2.江苏苏博特新材料股份有限公司,江苏 南京 211108

邹小童1,武建好1,李星辰1,王佳乐1,光鉴淼2

邹小童,武建好,李星辰,等.减缩剂对水泥砂浆及超高性能混凝土收缩性能的影响[J].混凝土与水泥制品,2024(6):18-21,26.

ZOU X T,WU J H,LI X C,et al.Effect of shrinkage reducer on shrinkage properties of mortar and ultra-high performance concrete[J].China Concrete and Cement Products,2024(6):18-21,26.

浏览量:
1000
摘   要:研究了不同掺量的减缩剂(SRA)对水泥砂浆塑性收缩开裂、水泥水化热、水泥砂浆毛细管负压的影响,以及SRA掺量(1%、3%、4%)对超高性能混凝土(UHPC)抗压强度和收缩性能的影响。结果表明:SRA可显著降低水泥砂浆的开裂面积、平均和最大裂缝宽度,当SRA掺量为4%时,缓解塑性收缩开裂的效果最佳,开裂面积、平均和最大裂缝宽度与基准组相比分别降低了52.1%、35.0%和48.4%;SRA通过延缓毛细管负压的发展,降低了水泥砂浆的塑性收缩开裂;随着SRA掺量的增加,UHPC的抗压强度提高越明显,UHPC的收缩显著降低;当减缩剂掺量为4%时,UHPC的28 d抗压强度达140.0 MPa,收缩率最低。 Abstract: The effects of different contents of shrinkage reducer(SRA) on plastic shrinkage cracking of cement mortar, heat of hydration of cement, and negative capillary pressure of cement mortar were studied. The effects of SRA content (1%, 3% and 4%) on the compressive strength and shrinkage properties of ultra-high performance concrete(UHPC) were investigated. The results show that SRA can significantly reduce the cracking area, average and maximum crack width of cement mortar. The best effect of mitigating plastic shrinkage cracking is achieved when the SRA content is 4%, and the cracking area, average and maximum crack widths are reduced by 52.1%, 35.0% and 48.4%, respectively, compared with the baseline group. SRA reduces the plastic shrinkage cracking of cement mortar by delaying the development of capillary negative pressure. With the increase of SRA content, the compressive strength of UHPC improves significantly, and the shrinkage of UHPC decreases significantly. When the content of shrinkage reducer is 4%, the 28 d compressive strength of UHPC reaches 140.0 MPa, with the lowest shrinkage rate.
英文名 : Effect of shrinkage reducer on shrinkage properties of mortar and ultra-high performance concrete
刊期 : 2024年第6期
关键词 : 减缩剂;水泥砂浆;塑性收缩开裂;超高性能混凝土;收缩率
Key words : Shrinkage reducer; Cement mortar; Plastic shrinkage cracking; Ultra-high performance concrete; Shrinkage rate
刊期 : 2024年第6期
DOI : 10.19761/j.1000-4637.2024.06.018.05
文章编号 :
基金项目 :
作者 : 邹小童1,武建好1,李星辰1,王佳乐1,光鉴淼2
单位 : 1.江苏双龙集团有限公司,江苏 南京 211103;2.江苏苏博特新材料股份有限公司,江苏 南京 211108

邹小童1,武建好1,李星辰1,王佳乐1,光鉴淼2

邹小童,武建好,李星辰,等.减缩剂对水泥砂浆及超高性能混凝土收缩性能的影响[J].混凝土与水泥制品,2024(6):18-21,26.

ZOU X T,WU J H,LI X C,et al.Effect of shrinkage reducer on shrinkage properties of mortar and ultra-high performance concrete[J].China Concrete and Cement Products,2024(6):18-21,26.

摘要
参数
结论
参考文献
引用本文

摘   要:研究了不同掺量的减缩剂(SRA)对水泥砂浆塑性收缩开裂、水泥水化热、水泥砂浆毛细管负压的影响,以及SRA掺量(1%、3%、4%)对超高性能混凝土(UHPC)抗压强度和收缩性能的影响。结果表明:SRA可显著降低水泥砂浆的开裂面积、平均和最大裂缝宽度,当SRA掺量为4%时,缓解塑性收缩开裂的效果最佳,开裂面积、平均和最大裂缝宽度与基准组相比分别降低了52.1%、35.0%和48.4%;SRA通过延缓毛细管负压的发展,降低了水泥砂浆的塑性收缩开裂;随着SRA掺量的增加,UHPC的抗压强度提高越明显,UHPC的收缩显著降低;当减缩剂掺量为4%时,UHPC的28 d抗压强度达140.0 MPa,收缩率最低。

Abstract: The effects of different contents of shrinkage reducer(SRA) on plastic shrinkage cracking of cement mortar, heat of hydration of cement, and negative capillary pressure of cement mortar were studied. The effects of SRA content (1%, 3% and 4%) on the compressive strength and shrinkage properties of ultra-high performance concrete(UHPC) were investigated. The results show that SRA can significantly reduce the cracking area, average and maximum crack width of cement mortar. The best effect of mitigating plastic shrinkage cracking is achieved when the SRA content is 4%, and the cracking area, average and maximum crack widths are reduced by 52.1%, 35.0% and 48.4%, respectively, compared with the baseline group. SRA reduces the plastic shrinkage cracking of cement mortar by delaying the development of capillary negative pressure. With the increase of SRA content, the compressive strength of UHPC improves significantly, and the shrinkage of UHPC decreases significantly. When the content of shrinkage reducer is 4%, the 28 d compressive strength of UHPC reaches 140.0 MPa, with the lowest shrinkage rate.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)SRA可以降低水泥砂浆的开裂面积、平均裂缝宽度和最大裂缝宽度。随着SRA掺量的增加,SRA降低开裂的效果逐步增强,当SRA掺量为4%时,效果最佳,开裂面积、平均裂缝宽度和最大裂缝宽度分别较基准组降低了52.1%、35.0%和48.4%。
(2)SRA可以降低水泥水化放热峰值,并推迟其出现时间,且这种延缓作用随着其掺量的增加而逐步增强。
(3)掺入SRA可以推迟水泥砂浆毛细管的负压诱导期。
(4)当SRA掺量为4%时,UHPC的抗压强度达到最高,7 d抗压强度较基准组提高了5.8%,28 d抗压强度较于基准组提高了11.5%。
(5)掺入SRA可以降低UHPC的收缩,当SRA掺量为4%时,UHPC收缩率达到最低,较基准组降低了63.6%。

[1] ZUO W Q,FENG P,ZHONG P H,et al.Effects of novel polymer-type shrinkage-reducing admixture on early age autogenous deformation of cement pastes[J].Cement and Concrete Research,2017,100:413-422.
[2] 钱春香,耿飞,李丽.减缩剂的作用及其机理[J].功能材料,2006(2):287-291.
[3] 张志宾,徐玲玲,唐明述.减缩剂对水泥基材料水化和孔结构的影响(英文)[J].硅酸盐学报,2009,37(7):1244-1248.
[4] 龚建清,罗鸿魁,张阳,等.减缩剂和HCSA膨胀剂对UHPC力学性能和收缩性能的影响[J].材料导报,2021,35(8):8042-8048,8063.
[5] 陈美祝,周明凯,吴少鹏,等.减缩剂对水泥基材料早期水化及收缩变形性能的影响[J].武汉大学学报(工学版),2007(1):78-82.
[6] ZUO W Q,FENG P,ZHONG P H,et al.Effects of a novel polymer-type shrinkage-reducing admixture on early age microstructure evolution and transport properties of cement pastes[J].Cement and Concrete Composites,2019,95:33-41.
[7] 刘菲凡.减缩剂对超高性能混凝土性能的影响研究[J].混凝土与水泥制品,2022(6):6-9,16.
[8] 邓宗才,连怡红,赵连志.膨胀剂、减缩剂对超高性能混凝土自收缩性能的影响[J].北京工业大学学报,2021,47(1):61-69.
[9] 龚建清,罗鸿魁,张阳,等.减缩剂和HCSA膨胀剂对UHPC力学性能和收缩性能的影响[J].材料导报,2021,35(8):8042-8048,8063.
[10] 钱晓倩,詹树林,方明晖,等.减水剂对混凝土收缩和裂缝的负影响[J].铁道科学与工程学报,2004(2):19-25.
[11] 王迎飞,黄雁飞.减缩剂对高性能砼收缩开裂性能影响的研究[J].硅酸盐通报,2006(3):189-193.
[12] 王智,郭清春,江楠,等.减缩剂在水泥基材料中的作用历程与机理研究[J]建筑材料学报,2012,15(5):601-606,659.
[13] 乔墩.减缩剂对水泥基材料收缩抑制作用及机理研究[D].重庆:重庆大学,2010.
[14] 中华人民共和国国家发展和改革委员会.水泥砂浆抗裂性能试验方法:JC/T 951—2005[S].北京:中国建材工业出版社,2005.
[15] YANG G,WU J C,HU Q.Rapid detection of building cracks based on image processing technology with double square artificial marks[J]Advances in Structural Engineering,2019,22(5):1186-1193.
[16]  缪昌文,田倩,刘加平,等.基于毛细管负压技术测试混凝土最早期的自干燥效应[J].硅酸盐学报,2007,35(4):509-516.
[17] SALIBA J,ROZIERE E,GRONDIN F.Influence of shrinkage-reducing admixtures on plastic and long-term shrinkage[J].Cement and Concrete Composites,2011,33(2):209-217.
[18] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
[19] LURA P,PEASE B,MAZZOTTA G B,et al.Influence of shrinkage-reducing admixtures on development of plastic shrinkage cracks[J].ACI Materials Journal,2007,104(2):187-194.
[20] 张健.减缩型聚羧酸减水剂对水泥基材料收缩开裂的影响及作用机制[D].南京:东南大学,2022.
[21] 陈美祝.水泥基材料组分对早期水化及收缩开裂影响的研究[D].武汉:武汉大学,2007.
[22] 党玉栋,钱觉时,乔墩,等.减缩剂预饱和轻骨料对水泥砂浆自收缩的影响及机理[J].硅酸盐学报,2011,39:47-53.

邹小童,武建好,李星辰,.减缩剂对水泥砂浆及超高性能混凝土收缩性能的影响[J].混凝土与水泥制品,2024(6):18-21,26.

ZOU X T,WU J H,LI X C,et al.Effect of shrinkage reducer on shrinkage properties of mortar and ultra-high performance concrete[J].China Concrete and Cement Products,2024(6):18-21,26.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州