ECC-既有混凝土界面黏结性能研究

Study on the bonding performance of the interface between ECC and existing concrete

2024年第6期

工程水泥基复合材料（ECC）；拉伸黏结强度；界面剂；凿毛；模型

Engineered cementitious composites(ECC); Tensile bond strength; Interfacial agent; Chiseling; Model

2024年第6期

10.19761/j.1000-4637.2024.06.064.04

杨少伟1，2，刘孜睿2，杜义2，赵爱宁2

1.山东省建筑科学研究院有限公司，山东济南 250031；2.山东建科建筑材料有限公司，山东济南 250031

杨少伟1，2，刘孜睿2，杜义2，赵爱宁2

杨少伟,刘孜睿,杜义,等.ECC-既有混凝土界面黏结性能研究[J].混凝土与水泥制品,2024(6):64-67.

YANG S W,LIU Z R,DU Y,et al.Study on the bonding performance of the interface between ECC and existing concrete[J].China Concrete and Cement Products,2024(6):64-67.

浏览量:

1000

摘要：利用工程水泥基复合材料（ECC）对混凝土结构进行维修和加固时，新旧材料的界面黏结强度至关重要。研究了不同养护条件（标准养护、20 ℃水养、-10 ℃自然养护、40 ℃自然养护）下，涂刷界面剂[乙酸乙烯酯（VA）、乙酸乙烯酯-乙烯（VAE）、乙酸乙烯酯-叔碳酸乙烯酯（VA/VeoVa）]对ECC-既有混凝土界面黏结性能的影响，并在标准养护条件下，对比分析了涂刷VA/VeoVa、凿毛、凿毛+涂刷VA/VeoVa对ECC-既有混凝土界面黏结性能的影响。结果表明：与VA、EVA相比，VA/VeoVa在各养护条件下均能有效提高试件的拉伸黏结强度；标准养护条件下，凿毛+涂刷VA/VeoVa对试件拉伸黏结强度的提高效果最好，其次是凿毛，最后是涂刷VA/VeoVa。 Abstract：The interfacial bond strength of the new and old materials is crucial for the repair and reinforcement of concrete structures using engineered cementitious composites (ECC). The effects of brushing interfacial agents [vinyl acetate (VA), vinyl acetate-ethylene (VAE), vinyl acetate-tertiary vinyl carbonate (VA/VeoVa)] on the bonding property of the ECC-existing concrete interface were investigated under different curing conditions (standard curing, water curing at 20 ℃, natural curing at -10 ℃, and natural curing at 40 ℃). The effects of brushing VA/VeoVa, chiseling, chiseling+brushing VA/VeoVa on the bonding property of ECC-existing concrete interface were comparatively analyzed under standard curing conditions. The results show that VA/VeoVa is effective in improving the tensile bond strength of the specimens under all curing conditions compared with VA and EVA. Under standard curing conditions, chiseling + brushing VA/VeoVa has the best effect on improving the tensile bond strength of the specimens, followed by chiseling, and lastly, brushing VA/VeoVa.

英文名 : Study on the bonding performance of the interface between ECC and existing concrete

刊期 : 2024年第6期

关键词 : 工程水泥基复合材料（ECC）；拉伸黏结强度；界面剂；凿毛；模型

Key words : Engineered cementitious composites(ECC); Tensile bond strength; Interfacial agent; Chiseling; Model

刊期 : 2024年第6期

DOI : 10.19761/j.1000-4637.2024.06.064.04

文章编号 :

基金项目 :

作者 : 杨少伟1，2，刘孜睿2，杜义2，赵爱宁2

单位 : 1.山东省建筑科学研究院有限公司，山东济南 250031；2.山东建科建筑材料有限公司，山东济南 250031

杨少伟1，2，刘孜睿2，杜义2，赵爱宁2

杨少伟,刘孜睿,杜义,等.ECC-既有混凝土界面黏结性能研究[J].混凝土与水泥制品,2024(6):64-67.

YANG S W,LIU Z R,DU Y,et al.Study on the bonding performance of the interface between ECC and existing concrete[J].China Concrete and Cement Products,2024(6):64-67.





摘要

参数

结论

参考文献

引用本文

Abstract：The interfacial bond strength of the new and old materials is crucial for the repair and reinforcement of concrete structures using engineered cementitious composites (ECC). The effects of brushing interfacial agents [vinyl acetate (VA), vinyl acetate-ethylene (VAE), vinyl acetate-tertiary vinyl carbonate (VA/VeoVa)] on the bonding property of the ECC-existing concrete interface were investigated under different curing conditions (standard curing, water curing at 20 ℃, natural curing at -10 ℃, and natural curing at 40 ℃). The effects of brushing VA/VeoVa, chiseling, chiseling+brushing VA/VeoVa on the bonding property of ECC-existing concrete interface were comparatively analyzed under standard curing conditions. The results show that VA/VeoVa is effective in improving the tensile bond strength of the specimens under all curing conditions compared with VA and EVA. Under standard curing conditions, chiseling + brushing VA/VeoVa has the best effect on improving the tensile bond strength of the specimens, followed by chiseling, and lastly, brushing VA/VeoVa.

扫二维码用手机看

[1] 张品乐,朱昊天,胡静,等.高性价比混杂纤维工程水泥基复合材料的力学性能研究[J].硅酸盐通报,2023,42(11):3816-3826.
[2] 王磊,尹梦环,张继旺,等.纤维对再生砖混ECC力学性能及微观结构的影响[J].硅酸盐通报,2023,42(10):3479-3488.
[3] 张品乐,邓让,胡静,等.钢-PVA混杂纤维增强工程水泥基复合材料弯曲性能研究[J].硅酸盐通报,2023,42(9):3125-3134.
[4] 宋梦凡,高新刚,周宗辉.改性碳酸钙晶须对工程水泥基材料力学性能的影响研究[J].新型建筑材料,2023,50(4):145-150.
[5] 孙亚颇.纳米碳纤维增韧水泥基复合材料的力学性能和耐久性能研究[J].功能材料,2023,54(1):1115-1119.
[6] LI V C.Advancese in ECC research[J].ACI Special Publications,2002,206:373-400.
[7] GAO S,WANG Z,WANG W,et al.Effect of shrinkage-reducing admixture and expansive agent on mechanical properties and drying shrinkage of engineered cementitious composite(ECC)[J].Construction and Building Materials,2018,179(10):172-185.
[8] 车佳玲,杨鹏宇,舒宏博,等.高延性混凝土加固泥浆砖柱抗压性能研究[J].建筑结构,2022,52(增刊1):2126-2131.
[9] 彭晓,黄晓斌,阙海群,等.ECC-BFRP加固地铁车站抗震性能研究[J].地震工程与工程振动,2022,42(6):184-191.
[10] 王少伟,肖焰钰,朱平华,等.高延性水泥基复合材料与既有混凝土结合面的抗溶蚀性[J].硅酸盐学报,2022,50(10):2692-2700.
[11] 李艳,赵一多,周明杨.ECC修复既有RC梁界面粘结与受弯性能试验研究[J].硅酸盐通报,2019,38(9):2794-2800.
[12] 崔涛,何浩祥,闫维明,等.ECC与既有混凝土结合面的抗剪性能[J].建筑材料学报,2020,23(5):1030-1037.
[13] 魏鹏,周明洋.ECC与既有混凝土粘结界面抗剪性能研究[J].中原工学报,2019,30(4):49-54.
[14] 王孟伟.ECC与既有混凝土粘结性能的影响因素研究[D].南京:东南大学,2018.
[15] 张婵韬,段政彬.胶粉对玻化微珠保温砂浆抗干湿循环性能影响研究[J].湖南工程学院学报(自然科学版),2020,30(2):91-94.
[16] 林沁,王静峰,丁敬华,等.地下结构水泥基渗透结晶型防水材料试验与分析[J].合肥工业大学学报(自然科学版),2019,42(5):664-670.
[17] 王月明,唐永志,刘开伟,等.纤维和胶粉对水泥砂浆力学和抗裂性能的影响[J].硅酸盐通报,2018,37(9):2775-2781.
[18] 王子明,王亚丽.可再分散乳胶粉的制备与应用[C]//中国建筑业协会材料分会预拌砂浆推广委员会.2004年中国国际建筑干混砂浆生产应用技术研讨会论文集.北京:中国建筑业协会材料分会预拌砂浆推广委员会,2004:105-109.
[19] 秦昊.高分子聚合物在混凝土表面修复中的应用研究[D].北京:北京建筑大学,2019.
[20] 王小威.复合机械锚固下FRP加固钢筋混凝土梁弯剪性能研究[D].深圳:深圳大学,2019.

上一个

粗骨料对超高性能应变硬化水泥基复合材料（UHP-SHCC）性能的影响

下一个

钢纤维增强聚合物水泥砂浆性能研究

头部文案

ECC-既有混凝土界面黏结性能研究

相关文件