明挖隧道工程大体积混凝土防裂抗渗性能研究

Research on anti-cracking and anti-seepage performance of mass concrete in open-cut tunnel engineering

2024年第6期

明挖隧道工程；大体积混凝土；防裂抗渗复合材料；温度；微应变

Open-cut tunnel engineering; Mass concrete; Anti-cracking and anti-seepage composite material; Temperature; Microstrain

2024年第6期

10.19761/j.1000-4637.2024.06.083.05

王德民1，朱宇2，张蔚斌2，朱国军1，牛瑞3，舒震林1，张港1

1.武汉三源特种建材有限责任公司，湖北武汉 430083；2.苏州交投建设管理有限公司，江苏苏州 215008；3.中国中铁隧道局集团有限公司，广东广州 511458

王德民1，朱宇2，张蔚斌2，朱国军1，牛瑞3，舒震林1，张港1

王德民,朱宇,张蔚斌,等.明挖隧道工程大体积混凝土防裂抗渗性能研究[J].混凝土与水泥制品,2024(6):83-86,93.

WANG D M,ZHU Y,ZHANG W B,et al.Research on anti-cracking and anti-seepage performance of mass concrete in open-cut tunnel engineering[J].China Concrete and Cement Products,2024(6):83-86,93.

浏览量:

1000

摘要：为了研究采用SY-COM高性能纤维防裂抗渗复合材料（以下简称SY-COM复合材料）所配制的混凝土的防裂抗渗效果，对其力学、抗渗、抗裂等性能进行了测试，并依托某明挖隧道工程，监测了掺SY-COM复合材料大体积混凝土的内部温度和微应变随时间的变化规律。结果表明：与基准组相比，掺SY-COM复合材料混凝土的抗压、劈裂抗拉和抗折强度均有所提高，抗渗等级由P8提高至P12；掺SY-COM复合材料大体积混凝土的早期温降收缩量较小，早期开裂风险较低，防裂抗渗效果较好。 Abstract: In order to study the anti-cracking and anti-seepage effect of concrete prepared with SY-COM high-performance fiber and anti-cracking and anti-seepage composite material (SY-COM composite material), the mechanical, anti-seepage, anti-cracking and other properties were tested. Based on a certain open-cut tunnel engineering, the internal temperature and microstrain of mass concrete mixed with SY-COM composite material were monitored over time. The results show that compared with the benchmark group, the compressive, splitting tensile, and flexural strength of concrete mixed with SY-COM composite material are improved, and the impermeability level is increased from P8 to P12. The early temperature drop shrinkage of mass concrete mixed with SY-COM composite material is relatively small, the risk of early cracking is low, and the anti-cracking and anti-seepage effect is good.

英文名 : Research on anti-cracking and anti-seepage performance of mass concrete in open-cut tunnel engineering

刊期 : 2024年第6期

关键词 : 明挖隧道工程；大体积混凝土；防裂抗渗复合材料；温度；微应变

Key words : Open-cut tunnel engineering; Mass concrete; Anti-cracking and anti-seepage composite material; Temperature; Microstrain

刊期 : 2024年第6期

DOI : 10.19761/j.1000-4637.2024.06.083.05

文章编号 :

基金项目 :

作者 : 王德民1，朱宇2，张蔚斌2，朱国军1，牛瑞3，舒震林1，张港1

单位 : 1.武汉三源特种建材有限责任公司，湖北武汉 430083；2.苏州交投建设管理有限公司，江苏苏州 215008；3.中国中铁隧道局集团有限公司，广东广州 511458

王德民1，朱宇2，张蔚斌2，朱国军1，牛瑞3，舒震林1，张港1

王德民,朱宇,张蔚斌,等.明挖隧道工程大体积混凝土防裂抗渗性能研究[J].混凝土与水泥制品,2024(6):83-86,93.

WANG D M,ZHU Y,ZHANG W B,et al.Research on anti-cracking and anti-seepage performance of mass concrete in open-cut tunnel engineering[J].China Concrete and Cement Products,2024(6):83-86,93.





摘要

参数

结论

参考文献

引用本文

Abstract: In order to study the anti-cracking and anti-seepage effect of concrete prepared with SY-COM high-performance fiber and anti-cracking and anti-seepage composite material (SY-COM composite material), the mechanical, anti-seepage, anti-cracking and other properties were tested. Based on a certain open-cut tunnel engineering, the internal temperature and microstrain of mass concrete mixed with SY-COM composite material were monitored over time. The results show that compared with the benchmark group, the compressive, splitting tensile, and flexural strength of concrete mixed with SY-COM composite material are improved, and the impermeability level is increased from P8 to P12. The early temperature drop shrinkage of mass concrete mixed with SY-COM composite material is relatively small, the risk of early cracking is low, and the anti-cracking and anti-seepage effect is good.

扫二维码用手机看

[1] 《中国公路学报》编辑部.中国交通隧道工程学术研究综述·2022[J].中国公路学报,2022,35(4):1-40.
[2] 龚琛杰,丁文其.盾构隧道钢纤维混凝土管片接头极限承载力试验[J].中国公路学报,2017,30(8):134-142.
[3] 刘强,黄绵松,金峰.临海隧道混凝土结构耐久性和使用寿命研究[J].北京交通大学学报,2018,42(6):1-8.
[4] 王小敏,张巍,王浩,等.基于改进RABT升温曲线分析受火地铁隧道管片温度场[J].防灾减灾工程学报,2016,36(3):463-470.
[5] 刘建文,施成华,雷明锋,等.基于混凝土损伤模型的卸载作用下盾构隧道损伤机理[J].中南大学学报(自然科学版),2021,52(3):758-769.
[6] 徐可,赵娟,闵强,等.明挖隧道工程混凝土抗裂防渗常见问题及提升技术研究综述[J].新型建筑材料,2022(12):144-150.
[7] 林立文,王晨光,康健,等.抗裂剂与冷却水管协同控制金鸡湖隧道侧墙结构开裂应用研究[J].混凝土与水泥制品,2022(2):82-86.
[8] 周欣,夏文俊,王峻,等.太湖隧道结构混凝土收缩裂缝闭环控制关键技术[J].混凝土,2021(2):151-156.
[9] 王丙垒,纪宪坤,徐可,等.苏州某穿湖隧道大体积混凝土工程裂缝控制应用研究[J].新型建筑材料,2021(10):142-147,177.

[10] 王涛,胡琪,吴绍明,等.微珠对隧道工程混凝土性能的影响及机理研究[J].混凝土与水泥制品,2022(1):12-16,21.
[11] 同月苹,王艳,张少辉.隧道衬砌纤维混凝土力学性能与耐久性能的研究进展[J].材料科学与工程学报,2022,40(3):528-536.
[12] 周庆国,陈俊,胡景波.结构防水融合体系在川藏高速公路隧道中的应用[J].铁道建筑,2020,60(12):43-47.
[13] 曹妍,王芮文,赵蔚蔚,等.隧道二次衬砌混凝土仿生自愈技术应用研究[J].现代隧道技术,2022,59(6):250-257.
[14] 柳献,张晨光,张宸,等.FRP加固盾构隧道纵缝接头试验研究[J].铁道科学与工程学报,2016,13(2):316-324.
[15] 周红芳.木寨岭公路隧道高弹模PVA合成纤维喷射混凝土抗裂技术研究与探讨[J].隧道建设(中英文),2020,40(4):490-495.
[16] 张家伟,陈晓柳,罗玉萍,等.新型防裂抗渗复合材料在混凝土中应用研究[J].建筑科学,2018,34(1):116-121.
[17] 韦庆东,耿晓滨,孙俊,等.一种新型防裂抗渗复合材料的研究及性能测试[J].工程质量,2016,34(11):57-61.
[18] 沈文龙,程书剑,黄士奎,等.防裂抗渗复合材料对改进核电厂用混凝土性能的影响[J].核科学与工程,2018,38(1):1-8.
[19] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
[20] 中华人民共和国住房和城乡建设部.普通混凝土长期性能和耐久性能试验方法标准:GB/T 50082—2009[S].北京:中国建筑工业出版社,2009.

上一个

水泥和钢渣粉协同固化高含水率疏浚泥的力学性能研究

下一个

连续刚构-钢管混凝土拱桥0号块水化热及有限元模拟分析

头部文案

明挖隧道工程大体积混凝土防裂抗渗性能研究

相关文件