改性搅拌站废浆在水泥基材料中的再利用研究

Research on the reusing of modified mixing plant waste slurry in cementitious materials

2024年第6期

改性剂；搅拌站废浆；湿拌砂浆；混凝土；工作性；抗压强度；水泥水化

Modifier; Waste slurry from mixing plant; Wet-mixed mortar; Concrete; Workability; Compressive strength; Cement hydration

2024年第6期

10.19761/j.1000-4637.2024.06.106.06

中山市2019年高端科研机构科技创新专项项目（2019AG010）。

陈均侨1，2，水中和1，3，高旭3，4，曹小荣2，郑武1，肖勋光3

1.武汉理工大学材料科学与工程学院，湖北武汉 430070；2.广州浪淘砂新型材料有限公司，广东广州 511400；3.中山市武汉理工大学先进工程技术研究院，广东中山 528400；4.武汉理工大学土木与建筑学院，湖北武汉 430070

陈均侨1，2，水中和1，3，高旭3，4，曹小荣2，郑武1，肖勋光3

陈均侨,水中和,高旭,等.改性搅拌站废浆在水泥基材料中的再利用研究[J].混凝土与水泥制品,2024(6):106-110,114.

CHEN J Q, SHUI Z H,GAO X,et al.Research on the reusing of modified mixing plant waste slurry in cementitious materials[J].China Concrete and Cement Products,2024(6):106-110,114.

浏览量:

1000

摘要：为研究搅拌站废浆（以下简称废浆）在水泥基材料中再利用的可行性，用自主研发的废浆改性剂对废浆进行了改性处理，研究了未改性和改性废浆对湿拌砂浆、混凝土工作性及力学性能的影响，并通过热重法（TG-DTG）分析了改性废浆对胶凝材料水化的影响。结果表明：改性剂延缓了废浆的凝结时间，使废浆保持较高的活性；与未改性废浆相比，掺入改性废浆使湿拌砂浆的8 h稠度损失率降低，凝结时间延长，抗压强度提高；改性废浆的掺入提高了混凝土的工作性及抗压强度。改性废浆再利用具有一定的经济效益。 Abstract: In order to study the feasibility of reusing waste slurry from mixing plant in cementitious materials, a self-developed waste slurry modifier was used to modify the waste slurry, and the effects of unmodified and modified waste slurry on the workability and mechanical properties of wet-mixed mortar and concrete were studied, and the effects of modified waste slurry on hydration of cementitious materials were analyzed by thermogravimetric(TG-DTG). The results show that the modifier delays the setting time of the waste slurry and maintains the waste slurry with high activity. Compared with the unmodified waste slurry, the addition of modified waste slurry reduces the 8 h consistency loss rate of wet-mixed mortar, prolongs the setting time, and increases the compressive strength. The addition of modified waste slurry improves the workability and compressive strength of concrete. Modified waste slurry reuse has a certain economic effect.

英文名 : Research on the reusing of modified mixing plant waste slurry in cementitious materials

刊期 : 2024年第6期

关键词 : 改性剂；搅拌站废浆；湿拌砂浆；混凝土；工作性；抗压强度；水泥水化

Key words : Modifier; Waste slurry from mixing plant; Wet-mixed mortar; Concrete; Workability; Compressive strength; Cement hydration

刊期 : 2024年第6期

DOI : 10.19761/j.1000-4637.2024.06.106.06

文章编号 :

基金项目 : 中山市2019年高端科研机构科技创新专项项目（2019AG010）。

作者 : 陈均侨1，2，水中和1，3，高旭3，4，曹小荣2，郑武1，肖勋光3

单位 : 1.武汉理工大学材料科学与工程学院，湖北武汉 430070；2.广州浪淘砂新型材料有限公司，广东广州 511400；3.中山市武汉理工大学先进工程技术研究院，广东中山 528400；4.武汉理工大学土木与建筑学院，湖北武汉 430070

陈均侨1，2，水中和1，3，高旭3，4，曹小荣2，郑武1，肖勋光3

陈均侨,水中和,高旭,等.改性搅拌站废浆在水泥基材料中的再利用研究[J].混凝土与水泥制品,2024(6):106-110,114.

CHEN J Q, SHUI Z H,GAO X,et al.Research on the reusing of modified mixing plant waste slurry in cementitious materials[J].China Concrete and Cement Products,2024(6):106-110,114.





摘要

参数

结论

参考文献

引用本文

Abstract: In order to study the feasibility of reusing waste slurry from mixing plant in cementitious materials, a self-developed waste slurry modifier was used to modify the waste slurry, and the effects of unmodified and modified waste slurry on the workability and mechanical properties of wet-mixed mortar and concrete were studied, and the effects of modified waste slurry on hydration of cementitious materials were analyzed by thermogravimetric(TG-DTG). The results show that the modifier delays the setting time of the waste slurry and maintains the waste slurry with high activity. Compared with the unmodified waste slurry, the addition of modified waste slurry reduces the 8 h consistency loss rate of wet-mixed mortar, prolongs the setting time, and increases the compressive strength. The addition of modified waste slurry improves the workability and compressive strength of concrete. Modified waste slurry reuse has a certain economic effect.

扫二维码用手机看

[1] 赵虎.压滤后的混凝土废浆干粉对水泥砂浆性能的影响[D].桂林:桂林理工大学,2023.
[2] 张云艺.搅拌站混凝土废料的性能及再利用试验研究[D].吉林:东北电力大学,2022.
[3] 段开瑞.混凝土废浆-单组分碱激发胶凝材料体系的制备及路用性能研究[D].长沙:长沙理工大学,2021.
[4] SANDROLINI F,FRANZONI E.Waste wash water recycling in ready-mixed concrete plants[J].Cement and Concrete Research, 2001,31(3):485-489.
[5] PAOLINI M,KHURANA R.Admixtures for recycling of waste concrete[J].Cement and Concrete Composites,1998,20(2):221-229.
[6] YAGUE A,VALLS S,VAZQUEZ E,et al.Durability of concrete with addition of dry sludge from waste water treatment plants[J].Cement and Concrete Research,2005,35(6):1064-1073.
[7] 王玥,李丹洋,张慧爱.废水泥浆水在预拌混凝土生产中的循环利用[J].山西建筑,2015,41(5):95-96.
[8] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.水泥标准稠度用水量、凝结时间、安定性检验方法:GB/T 1346—2011[S].北京:中国标准出版社,2011.
[9] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.用于水泥和混凝土中的粉煤灰:GB/T 1596—2017[S].北京:中国标准出版社,2017.
[10] 中华人民共和国住房和城乡建设部.建筑砂浆基本性能试验方法标准:JGJ/T 70—2009[S].北京:中国建筑工业出版社,2009.
[11] 中华人民共和国住房和城乡建设部.普通混凝土拌合物性能试验方法标准:GB/T 50080—2016[S].北京:中国建筑工业出版社,2016.
[12] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.

[13] 李崇智,冯乃谦,牛全林.聚羧酸系减水剂结构模型与高性能化分子设计[J].建筑材料学报,2004(2):194-201.
[14] 易卓然,肖建庄,薛松涛,等.不合格新拌混凝土回收利用基本试验研究[J].建筑材料学报,2021,24(3):637-643.
[15] 彭小芹,兰聪,王淑萍,等.水化硅酸钙粉体对水泥水化反应过程及机理的影响[J].建筑材料学报,2015,18(2):195-201.
[16] 马梦阳.湿磨商砼废浆-水泥体系水化性能与微结构研究[D].武汉:湖北工业大学,2019.
[17] 李小玲,何廷树.混凝土搅拌站废水对水泥及胶砂性能影响[J].混凝土,2011(3):139-141.
[18] 刘数华,王磊,谢国帅,等.掺玻璃粉水泥净浆水化性能[J].建筑材料学报,2015,18(1):31-37.
[19] 徐菲,韦华,钱文勋,等.水泥土组成矿物的热重-热力学模拟联用分析[J].建筑材料学报,2022,25(4):424-433.
[20] 周明凯,王宇强,陈潇.CFB炉渣代机制砂对混凝土强度的影响机理[J].建筑材料学报,2022,25(12):1241-1247.

上一个

掺废玻璃粉水泥基材料性能研究综述

下一个

基于一次回归正交试验的再生混凝土配合比优化研究

头部文案

改性搅拌站废浆在水泥基材料中的再利用研究

相关文件