水泥和钢渣粉协同固化高含水率疏浚泥的力学性能研究

Study on mechanical properties of cement and steel slag powder synergistic solidification of dredged mud with high moisture content

2024年第6期

水泥；钢渣粉；疏浚泥；协同固化；无侧限抗压强度；变形系数

Cement; Steel slag powder; Dredged mud; Synergistic solidification; Unconfined compressive strength; Deformation coefficient

2024年第6期

10.19761/j.1000-4637.2024.06.115.05

江苏省产学研合作项目（BY20221035）；江苏南水北调科技研发项目（JSNSBD202106）；江苏省水利科技项目（2020012）。

张丹1，邱成春1，*，王俊炜1，曹冬惠2，姚达3

1.盐城工学院土木工程学院，江苏盐城 224051；2.盐城市建筑设计研究院有限公司，江苏盐城 224007，3.江苏鸿基水源科技股份有限公司，江苏扬州 225100

张丹1，邱成春1，*，王俊炜1，曹冬惠2，姚达3

张丹,邱成春,王俊炜,等.水泥和钢渣粉协同固化高含水率疏浚泥的力学性能研究[J].混凝土与水泥制品,2024(6):115-119.

ZHANG D,QIU C C,WANG J W,et al.Study on mechanical properties of cement and steel slag powder synergistic solidification of dredged mud with high moisture content[J].China Concrete and Cement Products,2024(6):115-119.

浏览量:

1000

摘要：研究了钢渣粉的掺入方式（内掺、外掺）和掺量（0、5%、10%、15%）对水泥固化高含水率疏浚泥力学性能的影响。结果表明：当水泥掺量一定时，随着钢渣粉外掺量的增加，固化疏浚泥的3、7、14、28、90 d无侧限抗压强度均先增大后减小，14 d峰值应力和峰值应变也呈先增大后减小的趋势，钢渣粉的最佳外掺量为10%；对于纯水泥固化疏浚泥，其变形系数随着水泥掺量的增加而增大，抵抗变形的能力降低；外掺适量钢渣粉降低了固化疏浚泥的变形系数，提高了固化疏浚泥抵抗变形的能力；钢渣粉内掺取代部分水泥降低了固化疏浚泥的无侧限抗压强度，建议钢渣粉采用外掺方式。 Abstract: The influence of the mixing method (internal and external) and content (0, 5%, 10%, 15%) of steel slag powder on the mechanical properties of cement solidified dredged mud with high moisture content was studied. The results show that when the cement content is constant, with the increase of external content of steel slag powder, the unconfined compressive strength of solidified dredged mud at 3 d, 7 d, 14 d, 28 d, and 90 d first increases and then decreases, the peak stress and peak strain at 14 d also show a trend of first increasing and then decreasing, and the optimal external content of steel slag powder is 10%. For pure cement solidified dredged mud, its deformation coefficient increases with the increase of cement content, and its ability to resist deformation decreases. Adding an appropriate external content of steel slag powder reduces the deformation coefficient of solidified dredged mud and improves its ability to resist deformation. Replacing some cement with steel slag powder reduces the unconfined compressive strength of solidified dredged mud. It is recommended to use the external mixing method for steel slag powder.

英文名 : Study on mechanical properties of cement and steel slag powder synergistic solidification of dredged mud with high moisture content

刊期 : 2024年第6期

关键词 : 水泥；钢渣粉；疏浚泥；协同固化；无侧限抗压强度；变形系数

Key words : Cement; Steel slag powder; Dredged mud; Synergistic solidification; Unconfined compressive strength; Deformation coefficient

刊期 : 2024年第6期

DOI : 10.19761/j.1000-4637.2024.06.115.05

文章编号 :

基金项目 : 江苏省产学研合作项目（BY20221035）；江苏南水北调科技研发项目（JSNSBD202106）；江苏省水利科技项目（2020012）。

作者 : 张丹1，邱成春1，*，王俊炜1，曹冬惠2，姚达3

单位 : 1.盐城工学院土木工程学院，江苏盐城 224051；2.盐城市建筑设计研究院有限公司，江苏盐城 224007，3.江苏鸿基水源科技股份有限公司，江苏扬州 225100

张丹1，邱成春1，*，王俊炜1，曹冬惠2，姚达3

张丹,邱成春,王俊炜,等.水泥和钢渣粉协同固化高含水率疏浚泥的力学性能研究[J].混凝土与水泥制品,2024(6):115-119.





摘要

参数

结论

参考文献

引用本文

Abstract: The influence of the mixing method (internal and external) and content (0, 5%, 10%, 15%) of steel slag powder on the mechanical properties of cement solidified dredged mud with high moisture content was studied. The results show that when the cement content is constant, with the increase of external content of steel slag powder, the unconfined compressive strength of solidified dredged mud at 3 d, 7 d, 14 d, 28 d, and 90 d first increases and then decreases, the peak stress and peak strain at 14 d also show a trend of first increasing and then decreasing, and the optimal external content of steel slag powder is 10%. For pure cement solidified dredged mud, its deformation coefficient increases with the increase of cement content, and its ability to resist deformation decreases. Adding an appropriate external content of steel slag powder reduces the deformation coefficient of solidified dredged mud and improves its ability to resist deformation. Replacing some cement with steel slag powder reduces the unconfined compressive strength of solidified dredged mud. It is recommended to use the external mixing method for steel slag powder.

扫二维码用手机看

[1] 王山,徐桂中,罗凤华,等.秸秆排水体联合真空预压处理对疏浚淤泥有机质和养分影响研究[J].中国农村水利水电,2023(4):33-39.
[2] 武冬青,董志良,徐文雨.化学-物理复合法在海底淤泥填海造地工程中的应用[J].岩石力学与工程学报,2013,32(9):1779-1784.
[3] 张福海,陈庆,张晓阳,等.海砂-海泥混合料作为海堤填料的可行性试验研究[J].岩土工程学报,2017,39(增刊1):182-186.
[4] 章荣军,于同生,郑俊杰.材料参数空间变异性对水泥固化淤泥填筑路堤稳定性影响研究[J].岩土工程学报,2018,40(11):2078-2086.
[5] 徐超,董天林,叶观宝.水泥土搅拌桩法在连云港海相软土地基中的应用[J].岩土力学,2006,27(3):495-498.
[6] 刘泉声,屈家旺,柳志平,等.侵蚀影响下水泥土的力学性质试验研究[J].岩土力学,2014,35(12):3377-3384.
[7] 吴跃东,彭犇,吴龙,等.国内外钢渣处理与资源化利用技术发展现状综述[J].环境工程,2021,39(1):161-165.
[8] 赵立杰,张芳.钢渣资源综合利用及发展前景展望[J].材料导报,2020,34(增刊2):1319-1322,1333.
[9] RASHSD A M.A synopsis manual about recycling steel slag as a cementitious material[J].Journal of Materials Research and Technology,2019,8(5):4940-4955.
[10] JIA R Q,LIU J X,JIA R Q.A study of factors that influence the hydration activity of mono-component CaO and bi-component CaO/Ca2Fe2O5 systems[J].Cement and Concrete Research,2017,91:123-132.
[11] 陈嘉杰.固废钢渣用于水泥稳定碎石基层性能研究[D].重庆:重庆交通大学,2023.
[12] 黄婧,周志云,陈新星.钢渣-矿渣-粉煤灰复合微粉混凝土的抗冻性能研究[J].混凝土与水泥制品,2022(12):85-89.
[13] LANG L,SONG C Y,XUE L,et al.Effectiveness of waste steel slag powder on the strength development and associated micro-mechanisms of cement-stabilized dredged sludge[J].Construction and Building Materials,2020,240:117975.
[14] WU Y K,HU X S,HU R,et al.Study on the application of an activator for steel slag powder-cement in muddy soil[J]. European Journal of Environmental and Civil Engineering,2017(7):1-13.
[15] 吴燕开,胡锐,赵位莹,等.钢渣粉固化淤泥质水泥土强度特性试验研究[J].科学技术与工程,2017,17(15):306-311.
[16] 冯兴国,朱超,沈阳,等.含水率对水泥-钢渣复合固化疏浚土性能的影响[J].水运工程,2021(7):1-6.
[17] XIAO Z Y,XU W.Assessment of strength development in cemented coastal silt admixed granite powder[J].Construction and Building Materials,2019,206:470-482.
[18] WANG Q,YANG J W,YAN P Y.Influence of initial alkalinity on the hydration of steel slag[J].Science China(Technological Sciences),2012,55(12):3378-3387.
[19] 郭印.淤泥质土的固化及力学特性的研究[D].杭州:浙江大学,2007.
[20] 张丹,吴振威,宋苗苗,等.盐分侵蚀对水泥固化土力学特性的影响研究[J].土木工程与管理学报,2022,39(5):94-99.
[21] 丁建文,张帅,洪振舜,等.水泥-磷石膏双掺固化处理高含水率疏浚淤泥试验研究[J].岩土力学,2010,31(9):2817-2822.
[22] 汤怡新,刘汉龙,朱伟.水泥固化土工程特性试验研究[J].岩土工程学报,2000(5):549-554.
[23] 朱伟,张春雷,高玉峰,等.海洋疏浚泥固化处理土基本力学性质研究[J].浙江大学学报(工学版),2005(10):103-107.
[24] 范晓秋,洪宝宁,胡昕,等.水泥砂浆固化土物理力学特性试验研究[J].岩土工程学报,2008(4):605-610.

上一个

基于一次回归正交试验的再生混凝土配合比优化研究

下一个

明挖隧道工程大体积混凝土防裂抗渗性能研究

头部文案

水泥和钢渣粉协同固化高含水率疏浚泥的力学性能研究

相关文件