膨胀剂掺量对机制砂UHPC工作性和自收缩性能的影响

Effect of expansion agent content on the workability and self-shrinkage performance of UHPC with manufacture sand

2024年第7期

机制砂；超高性能混凝土；膨胀剂；工作性；自收缩性能；凝结时间

Manufacture sand; Ultra-high performance concrete; Expansion agent; Workability; Self-shrinkage performance; Setting time

2024年第7期

10.19761/j.1000-4637.2024.07.029.05

河南省重点研发与推广专项项目（202102310255）。

任蒙恩1，宁利恒1，康海1，何晓丹1，元成方2，*

1.河南汇创实业有限公司，河南郑州 450003；2.郑州大学，河南郑州 450001

任蒙恩1，宁利恒1，康海1，何晓丹1，元成方2，*

任蒙恩,宁利恒,康海,等.膨胀剂掺量对机制砂UHPC工作性和自收缩性能的影响[J].混凝土与水泥制品,2024(7):29-32,37.

REN Meng’en, NING Liheng, KANG Hai,et al.Effect of expansion agent content on the workability and self-shrinkage performance of UHPC with manufacture sand[J].China Concrete and Cement Products,2024(7):29-32,37.

浏览量:

1000

摘要：针对不同膨胀剂掺量下机制砂超高性能混凝土（UHPC）的工作性及自收缩性能进行了试验研究。结果表明：随着膨胀剂掺量的增加，机制砂UHPC的流动性和凝结时间均呈先增后减的趋势，当膨胀剂掺量为10%时，二者皆达到峰值，扩展度为445 mm，初凝时间和终凝时间分别为44.4 h和50.2 h；机制砂UHPC的早期自收缩随着膨胀剂掺量的增加整体呈先减少后增加的趋势，当膨胀剂掺量为10%时，能够起到较好的收缩补偿作用。 Abstract: The workability and self-shrinkage performance of ultra-high performance concrete(UHPC) with manufacture sand under different expansion agent contents were investigated. The results show that with the increase of the content of expansion agents, the flowability and setting time of UHPC with manufacture sand show a trend of first increasing and then decreasing. When the content of expansion agent is 10%, the flowability and setting time can both reach their peak, with the expansion degree of 445 mm, the initial setting time of 44.4 h, and the final setting time of 50.2 h respectively. The early self-shrinkage of UHPC with manufacture sand shows an overall trend of first decreasing and then increasing with the increase of expansion agent content, and when the expansion agent content is 10%, it can achieve a better shrinkage compensation effect.

英文名 : Effect of expansion agent content on the workability and self-shrinkage performance of UHPC with manufacture sand

刊期 : 2024年第7期

关键词 : 机制砂；超高性能混凝土；膨胀剂；工作性；自收缩性能；凝结时间

Key words : Manufacture sand; Ultra-high performance concrete; Expansion agent; Workability; Self-shrinkage performance; Setting time

刊期 : 2024年第7期

DOI : 10.19761/j.1000-4637.2024.07.029.05

文章编号 :

基金项目 : 河南省重点研发与推广专项项目（202102310255）。

作者 : 任蒙恩1，宁利恒1，康海1，何晓丹1，元成方2，*

单位 : 1.河南汇创实业有限公司，河南郑州 450003；2.郑州大学，河南郑州 450001

任蒙恩1，宁利恒1，康海1，何晓丹1，元成方2，*

任蒙恩,宁利恒,康海,等.膨胀剂掺量对机制砂UHPC工作性和自收缩性能的影响[J].混凝土与水泥制品,2024(7):29-32,37.





摘要

参数

结论

参考文献

引用本文

Abstract: The workability and self-shrinkage performance of ultra-high performance concrete(UHPC) with manufacture sand under different expansion agent contents were investigated. The results show that with the increase of the content of expansion agents, the flowability and setting time of UHPC with manufacture sand show a trend of first increasing and then decreasing. When the content of expansion agent is 10%, the flowability and setting time can both reach their peak, with the expansion degree of 445 mm, the initial setting time of 44.4 h, and the final setting time of 50.2 h respectively. The early self-shrinkage of UHPC with manufacture sand shows an overall trend of first decreasing and then increasing with the increase of expansion agent content, and when the expansion agent content is 10%, it can achieve a better shrinkage compensation effect.

关键词:

the

and

expansion

uhpc

with

膨胀剂

agent

setting

扫二维码用手机看

[1] 陈宝春,李聪,黄伟,等.超高性能混凝土收缩综述[J].交通运输工程学报,2018,18(1):13-18.
[2] 余睿,范定强,水中和,等.基于颗粒最紧密堆积理论的超高性能混凝土配合比设计[J].硅酸盐学报,2020,48(8):1145-1154.
[3] 王哲,肖勋光,水中和,等.基于最紧密堆积理论合理选择UHPC的减水剂掺量[J].硅酸盐通报,2019,38(5):1503-1509.
[4] 赵明宇,方兴旺,李志强,等.机制砂高抗冲磨超高性能混凝土(UHPC)的组成设计与工程应用[J].混凝土,2023(1):159-164.
[5] 卫煜,陈平,明阳,等.超细高活性矿物掺合料对UHPC水化和收缩性能的影响[J].硅酸盐通报,2022,41(2):461-468.
[6] 王超,陈阳,李好飞,等.再生砖粉UHPC收缩性能试验研究[J].混凝土,2024(2):93-97.
[7] 林添琦,孙强顺,张鸿儒,等.饱和面干处理方式对再生细骨料UHPC自收缩性能的影响[J/OL].福州大学学报(自然科学版),2024(4):1-6[2024-05-22].http://kns.cnki.net/kcms/detail/35.
1337.N.20240517.1840.028.html.
[8] 赵顺增,刘立,郑万廪,等.Expansive agent for high performance shrinkage compensating concrete-advantages application of HCSA[C]//中国硅酸盐学会膨胀与自应力混凝土专业委员会.第五届全国膨胀剂和混凝土应用技术研讨会论文集(2).北京:中国建筑材料科学研究总院,2009:4.
[9] LI B,XU L H,GU Y S,et al.Investigation on influence of HCSA expansive agent on dosage on performance of high-strength self-compacting concrete[J].Engineering Journal of Wuhan University,2017,50(1):90-96.
[10] 龚建清,罗鸿魁,张阳,等.减缩剂和HCSA膨胀剂对UHPC力学性能和收缩性能的影响[J].材料导报,2021,35(8):8042-8048,8063.
[11] 杨宁,韩圣铭.HCSA膨胀剂掺量对水泥砂浆性能的影响研究[J].混凝土与水泥制品,2020(3):19-23.
[12] 黄政宇,刘永强,李操旺.掺HCSA膨胀剂超高性能混凝土性能的研究[J].材料导报,2015,29(4):116-121.
[13] 邓宗才,连怡红,赵连志.膨胀剂、减缩剂对超高性能混凝土自收缩性能的影响[J].北京工业大学学报,2021,47(1):61-69.
[14] PARK J J,YOO D Y,KIM S W,et al.Benefifits of using expansive and shrinkage-reducing agents in UHPC for volume stability[J].Magzine of Concrete Research,2014,66(14):745-750．
[15] YANG R,YU R,SHUI Z H,et al.The physical and chemical impact of manufactured sand as a partial replacement material in ultra-high performance concrete(UHPC)[J].Cement and Concrete Composites,2019,99:203-213.
[16] 中华人民共和国住房和城乡建设部,中华人民共和国国家质量监督检验检疫总局.普通混凝土拌合物性能试验方法标准:GB/T 50080—2016[S].北京中国建筑工业出版社,2016.
[17] 中国工程建设标准化协会.超高性能混凝土试验方法标准:T/CECS 864—2021[S].北京:中国建筑工业出版社,2021.
[18] 黄登标.机制砂特性及其混凝土配制技术的实验研究[D].南昌:南昌大学,2021.
[19] 刘永强.掺膨胀剂HCSA的超高性能混凝土性能的研究[D].长沙:湖南大学,2014.
[20] 马增琦,孙文晋,赖雄.石粉对机制砂混凝土工作性能的影响研究[J].湖南交通科技,2021,47(4):23-26,117.
[21] 叶林,张同波,李翠翠,等.基于试验的超长混凝土墙体温度应力计算及开裂原因分析[J].施工技术(中英文),2021,50(17):158-162,165.

上一个

新型复合降黏剂在C60主塔混凝土中的应用研究

下一个

气泡结构对新拌混凝土工作性的影响研究

头部文案

膨胀剂掺量对机制砂UHPC工作性和自收缩性能的影响

相关文件