粉煤灰再生混凝土配筋梁的受弯性能研究
Study on bending performance of fly ash recycled concrete reinforced beams
2024年第8期
粉煤灰再生混凝土;基本力学性能;受弯性能;极限承载力;裂缝特征
Fly ash recycled concrete; Basic mechanical property; Bending performance; Ultimate bearing capacity; Crack characteristic
2024年第8期
10.19761/j.1000-4637.2024.08.075.05
福建省交通运输厅科技项目(Z202212160)。
陈晋华1,周娉婷2,林爱萍1,张 杰2
1.福建船政交通职业学院 土木工程学院,福建 福州 350007;2.福建工大岩土工程研究所有限公司,福建 福州 350002

陈晋华1,周娉婷2,林爱萍1,张 杰2

陈晋华,周娉婷,林爱萍,粉煤灰再生混凝土配筋梁的受弯性能研究[J].混凝土与水泥制品,2024(8):75-78,83.

CHEN J H,ZHOU P T,LIN A P,et al.Study on bending performance of fly ash recycled concrete reinforced beams[J].China Concrete and Cement Products,2024(8):75-78,83.

浏览量:
1000
摘   要:研究了再生粗骨料取代率(0、30%、60%、100%)对粉煤灰混凝土基本力学性能的影响,并设计制作了4根相同配筋率的试验梁,分析了其受弯破坏情况。结果表明:随着再生粗骨料取代率的增加,粉煤灰混凝土的抗压强度、劈裂抗拉强度、轴心抗压强度和弹性模量均先增大后减小;粉煤灰再生混凝土试验梁的正截面应变服从平截面假定,随着再生粗骨料取代率的增加,试验梁的延性和开裂荷载基本呈降低趋势,裂缝数量、裂缝最大宽度和屈服荷载均先增大后减小,极限荷载呈先增大后减小再增大的趋势。 Abstract: The influence of the replacement rate(0, 30%, 60%, 100%) of recycled coarse aggregate on the basic mechanical properties of fly ash concrete was studied, and four test beams with the same reinforcement ratio were designed to analyze their bending failure. The results show that as the replacement rate of recycled coarse aggregate increases, the compressive strength, splitting tensile strength, axial compressive strength, and elastic modulus of fly ash concrete all increase first and then decrease. The normal section strain of the fly ash recycled concrete test beam follows the plane section assumption. With the increase of the replacement rate of recycled coarse aggregate, the ductility and cracking load of the test beam show a decreasing trend, the number of cracks, the maximum width of cracks, and the yield load all increase first and then decrease, and the ultimate load shows a trend of increasing first, then decreasing, and then increasing again.
英文名 : Study on bending performance of fly ash recycled concrete reinforced beams
刊期 : 2024年第8期
关键词 : 粉煤灰再生混凝土;基本力学性能;受弯性能;极限承载力;裂缝特征
Key words : Fly ash recycled concrete; Basic mechanical property; Bending performance; Ultimate bearing capacity; Crack characteristic
刊期 : 2024年第8期
DOI : 10.19761/j.1000-4637.2024.08.075.05
文章编号 :
基金项目 : 福建省交通运输厅科技项目(Z202212160)。
作者 : 陈晋华1,周娉婷2,林爱萍1,张 杰2
单位 : 1.福建船政交通职业学院 土木工程学院,福建 福州 350007;2.福建工大岩土工程研究所有限公司,福建 福州 350002

陈晋华1,周娉婷2,林爱萍1,张 杰2

陈晋华,周娉婷,林爱萍,粉煤灰再生混凝土配筋梁的受弯性能研究[J].混凝土与水泥制品,2024(8):75-78,83.

CHEN J H,ZHOU P T,LIN A P,et al.Study on bending performance of fly ash recycled concrete reinforced beams[J].China Concrete and Cement Products,2024(8):75-78,83.

摘要
参数
结论
参考文献
引用本文

摘   要:研究了再生粗骨料取代率(0、30%、60%、100%)对粉煤灰混凝土基本力学性能的影响,并设计制作了4根相同配筋率的试验梁,分析了其受弯破坏情况。结果表明:随着再生粗骨料取代率的增加,粉煤灰混凝土的抗压强度、劈裂抗拉强度、轴心抗压强度和弹性模量均先增大后减小;粉煤灰再生混凝土试验梁的正截面应变服从平截面假定,随着再生粗骨料取代率的增加,试验梁的延性和开裂荷载基本呈降低趋势,裂缝数量、裂缝最大宽度和屈服荷载均先增大后减小,极限荷载呈先增大后减小再增大的趋势。

Abstract: The influence of the replacement rate(0, 30%, 60%, 100%) of recycled coarse aggregate on the basic mechanical properties of fly ash concrete was studied, and four test beams with the same reinforcement ratio were designed to analyze their bending failure. The results show that as the replacement rate of recycled coarse aggregate increases, the compressive strength, splitting tensile strength, axial compressive strength, and elastic modulus of fly ash concrete all increase first and then decrease. The normal section strain of the fly ash recycled concrete test beam follows the plane section assumption. With the increase of the replacement rate of recycled coarse aggregate, the ductility and cracking load of the test beam show a decreasing trend, the number of cracks, the maximum width of cracks, and the yield load all increase first and then decrease, and the ultimate load shows a trend of increasing first, then decreasing, and then increasing again.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)随着再生粗骨料取代率的增加,试块的抗压强度、劈裂抗拉强度、轴心抗压强度、弹性模量均呈先增大后减小的趋势,说明掺入适量再生粗骨料能在一定程度上改善粉煤灰混凝土的基本力学性能。
(2)粉煤灰再生混凝土试验梁的受弯破坏属于适筋梁破坏。随着再生粗骨料取代率的增加,试验梁开始出现裂缝的时间变早,延性和开裂荷载基本呈降低趋势,裂缝数量、裂缝最大宽度和屈服荷载均先增大后减小,极限荷载呈先增大后减小再增大的趋势。

[1] 陈宇良,张绍松,徐金俊,等.压剪作用下PVA纤维再生混凝土力学性能试验研究[J].材料导报,2023,37(11):112-118.
[2] 王晓敏,郑建岚,朱艺婷.粉煤灰颗粒特性对再生混凝土水化性质的影响[J].福州大学学报(自然科学版),2021,49(2):238-244.
[3] 叶世昌,罗素蓉,郑建岚.矿物掺合料对再生混凝土早龄期拉伸徐变的影响[J].福州大学学报(自然科学版),2018,46(5):700-704.
[4] 黄海生,郑建岚.粉煤灰和矿粉对再生混凝土徐变性能影响的研究[J].福州大学学报(自然科学版),2017,45(2):206-211.
[5] 孙家瑛,孙浩,王培铭.活性掺合料对再生混凝土耐久性的影响[J].混凝土与水泥制品,2006(1):1-4.
[6] 肖建庄,兰阳.再生粗骨料混凝土梁抗弯性能试验研究[J].特种结构,2006(1):9-12.
[7] 孙燕群.纳米CaCO3对混凝土性能的影响研究[D].青岛:青岛理工大学,2018.
[8] 王丕祥,郭环宇,修振宇.纳米SiO2改性再生粗骨料混凝土改性机理及力学性能研究[J].混凝土,2023(1):108-113,119.
[9] 刘元德,安旭文,黄天翔.再生集料沥青混凝土物理力学性能的试验研究[J].武汉大学学报(工学版),2022,55(10):1027-1033.
[10] 宋灿,陈爱玖.再生粗骨料对再生混凝土基本性能的影响[J].煤炭技术,2011,30(6):159-161.
[11] 黄显智,王子明,姜德义.再生集料混凝土循环利用的试验研究[J].混凝土,2003(10):24-27.
[12] 沈大钦,朋改非.再生混凝土基本性能的研究[J].山西建筑,2006(14):151-153.
[13] 游帆,念梦飞,郑建岚,等.再生骨料混凝土弯曲疲劳性能研究[J].建筑结构学报,2022,43(4):134-141.
[14] 彭卓,朱德举,史才军,等.玄武岩织物增强碱激发矿渣粉煤灰水泥砂浆的耐久性研究[J].材料导报,2021,35(16):16058-16064.
[15] 张锋剑,马政伟,冯旭东,等.加掺粉煤灰再生混凝土梁受弯性能试验研究[J].河南城建学院学报,2016,25(3):9-14,57.

陈晋华,周娉婷,林爱萍,粉煤灰再生混凝土配筋梁的受弯性能研究[J].混凝土与水泥制品,2024(8):75-78,83.

CHEN J H,ZHOU P T,LIN A P,et al.Study on bending performance of fly ash recycled concrete reinforced beams[J].China Concrete and Cement Products,2024(8):75-78,83.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州