建筑旧桩的桩身材料耐久性能试验研究

Experimental study on the durability of pile materials for old building piles

2024年第11期

旧桩再利用；桩身材料；耐久性能；抗拉强度；碳化深度；氯离子含量

Reuse of old pile; Pile material; Durability; Tensile strength; Carbonization depth; Chloride ion content

2024年第11期

10.19761/j.1000-4637.2024.11.090.06

国家自然科学基金青年基金项目（52108328）；上海市“科技创新行动计划”软科学项目（22692193700）；2024年上海市建筑建材业科研项目计划项目（沪建科2024-005-004）；上海理工大学市级“大学生创新创业训练计划”项目（SH2023152）。

崔纪飞，夏宝华*，饶平平，胡宇航，张开弥，宋劭勋，陈鹏伟，张锟

上海理工大学土木工程系，上海 200093

崔纪飞，夏宝华*，饶平平，胡宇航，张开弥，宋劭勋，陈鹏伟，张锟

崔纪飞,夏宝华,饶平平,等.建筑旧桩的桩身材料耐久性能试验研究[J].混凝土与水泥制品,2024(11):90-95.

CUI J F,XIA B H,RAO P P,et al.Experimental study on the durability of pile materials for old building piles[J].China Concrete and Cement Products,2024(11):90-95.

浏览量:

1000

摘要：对旧桩进行桩身材料耐久性能检测是评估旧桩承载性能的重要方面，也是旧桩再利用的前提。依托上海曹家渡花鸟市场改造工程，对桩身混凝土开展了碳化深度、抗压强度和氯离子含量试验，并检测了混凝土中钢筋的锈蚀程度和抗拉性能。结果表明：随着距桩顶距离的增加，桩身混凝土的碳化深度和氯离子含量均逐渐减小，抗压强度逐渐增大；随着距桩顶距离的增加，混凝土中钢筋的直径、屈服强度和极限抗拉强度均略有减小，但仍满足HRB335级钢筋的强度要求；该工程旧桩满足原位再利用要求。 Abstract: Testing the durability of pile materials for old piles is an important aspect of evaluating the bearing capacity of old piles and a prerequisite for their reuse. Based on the renovation project of the Caojiadu Bird and Flower Market in Shanghai, the carbonation depth, compressive strength, and chloride ion content tests of the pile concrete were conducted, and the corrosion degree and tensile performance of the steel bars in the concrete were tested. The results show that as the distance from the pile top increases, the carbonation depth and chloride ion content of the pile concrete gradually decrease, and the compressive strength gradually increases. As the distance from the pile top increases, the diameter, yield strength, and ultimate tensile strength of the steel bars in the concrete slightly decrease, but still meet the strength requirements of HRB335 grade steel bars. The old piles in this project meet the requirements for in-situ reuse.

英文名 : Experimental study on the durability of pile materials for old building piles

刊期 : 2024年第11期

关键词 : 旧桩再利用；桩身材料；耐久性能；抗拉强度；碳化深度；氯离子含量

Key words : Reuse of old pile; Pile material; Durability; Tensile strength; Carbonization depth; Chloride ion content

刊期 : 2024年第11期

DOI : 10.19761/j.1000-4637.2024.11.090.06

文章编号 :

基金项目 : 国家自然科学基金青年基金项目（52108328）；上海市“科技创新行动计划”软科学项目（22692193700）；2024年上海市建筑建材业科研项目计划项目（沪建科2024-005-004）；上海理工大学市级“大学生创新创业训练计划”项目（SH2023152）。

作者 : 崔纪飞，夏宝华*，饶平平，胡宇航，张开弥，宋劭勋，陈鹏伟，张锟

单位 : 上海理工大学土木工程系，上海 200093

崔纪飞，夏宝华*，饶平平，胡宇航，张开弥，宋劭勋，陈鹏伟，张锟

崔纪飞,夏宝华,饶平平,等.建筑旧桩的桩身材料耐久性能试验研究[J].混凝土与水泥制品,2024(11):90-95.

CUI J F,XIA B H,RAO P P,et al.Experimental study on the durability of pile materials for old building piles[J].China Concrete and Cement Products,2024(11):90-95.





摘要

参数

结论

参考文献

引用本文

Abstract: Testing the durability of pile materials for old piles is an important aspect of evaluating the bearing capacity of old piles and a prerequisite for their reuse. Based on the renovation project of the Caojiadu Bird and Flower Market in Shanghai, the carbonation depth, compressive strength, and chloride ion content tests of the pile concrete were conducted, and the corrosion degree and tensile performance of the steel bars in the concrete were tested. The results show that as the distance from the pile top increases, the carbonation depth and chloride ion content of the pile concrete gradually decrease, and the compressive strength gradually increases. As the distance from the pile top increases, the diameter, yield strength, and ultimate tensile strength of the steel bars in the concrete slightly decrease, but still meet the strength requirements of HRB335 grade steel bars. The old piles in this project meet the requirements for in-situ reuse.

扫二维码用手机看

[1] JIN R Y,LI B,ZHOU T Y,et al.An empirical study of perceptions towards construction and demolition waste recyclingand reuse in China[J].Resources Conservation and Recycling,2017,126:86-98.
[2] CUI J F,LI J P,XIAO J Z,et al.Reclamation pathway of waste piles: A case study in Shanghai[J].Journal of Cleaner Production,2019,253:119919.
[3] GRAYBEAL B,TANESI J.Durability of an ultrahigh-performance concrete[J].Journal of Materials in Civil Engineering,2007,19(10):848-854.
[4] AIT-MOKHTAR A,BELARBI R,BENBOUDJEMA F,et al.Experimental investigation of the variability of concrete durability properties[J].Cement and Concrete Research,2013,45:21-36.
[5] MEHTA P K,MONTEIRO P J M.Concrete microstructure, properties, and materials[M].覃维祖,王栋民,丁建彤,译.北京:中国电力出版社,2008.
[6] 杜斌,刘祖德,聂向珍.城市中的旧桩基问题及处理方法探讨[C]//中国岩石力学与工程学会.第二届全国岩土与工程学术大会会议集(下册).北京:科学出版社,2006:29-35.
[7] 程哗,龚维明,潘建伍,等.旧桥桩基利用试验研究[J].中外公路,2012,32(2):111-114.
[8] 焦兴华,程晔,龚维明,等.旧桥桩基利用的材性耐久性试验研究[J].公路,2011(4):188-192.
[9] 王龙胜.海洋环境下既有桩基耐久性评估研究[D].青岛:青岛理工大学,2017.
[10] 张大利,宁作君,郑秀梅,等.复杂环境下钢筋混凝土结构寿命预测研究进展[J].混凝土,2023(8):8-13,22.
[11] 中华人民共和国住房和城乡建设部.普通混凝土长期性能和耐久性能试验方法标准:GB/T 50082—2009[S].北京:中国建筑工业出版社,2009.
[12] 中华人民共和国住房和城乡建设部.建筑基桩检测技术规范:JGJ 106—2014[S].北京:中国建筑工业出版社,2014.
[13] 张璐,施养杭.在役混凝土构件耐久性的评判准则[J].华侨大学学报(自然科学版),2009,30(3):315-320
[14] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
[15] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.钢筋混凝土用钢材试验方法:GB/T 28900—2012[S].北京:中国标准出版社,2012.
[16] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.钢筋混凝土用钢第2部分:热轧带肋钢筋:GB/T 1499.2—2018[S].北京:中国标准出版社,2018.
[17] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.金属材料拉伸试验第1部分:室温试验方法:GB/T 228.1—2010[S].北京:中国标准出版社,2010.
[18] 中华人民共和国住房和城乡建设部.混凝土耐久性检验评定标准:JGJ/T 193—2009[S].北京:中国建筑工业出版社,2009.
[19] 中华人民共和国住房和城乡建设部.混凝土质量控制标准:GB 50164—2011[S].北京:中国建筑工业出版社,2011.
[20] 中华人民共和国住房和城乡建设部.混凝土结构设计规范(2015年版):GB 50010—2010[S].北京:中国建筑工业出版社,2010.

上一个

混凝土结构自防水厚度试验方法研究

下一个

JC/T 888—2023《预应力混凝土薄壁管桩》标准解读

头部文案

建筑旧桩的桩身材料耐久性能试验研究

相关文件