硫酸盐侵蚀后UHPC-NC结合面的抗渗性能研究
Study on impermeability of the bonding surface of UHPC-NC under sulphate erosion
2025年第1期
超高性能混凝土(UHPC);普通混凝土(NC);结合面;硫酸盐侵蚀;抗渗性能;微观形貌
Ultra-high performance concrete(UHPC); Normal concrete(NC); Bonding surface; Sulphate erosion; Impermeability; Microstructure
2025年第1期
10.19761/j.1000-4637.2025.01.053.06
李 涛1,范 钰1,王爽倩1,龙莉波2,马跃强2
1.上海理工大学 环境与建筑学院,上海 200093;2.上海建工二建集团有限公司,上海 200080

李 涛1,范 钰1,王爽倩1,龙莉波2,马跃强2

李涛,范钰,王爽倩,等.硫酸盐侵蚀后UHPC-NC结合面的抗渗性能研究[J].混凝土与水泥制品,2025(1):53-58.

LI T,FAN Y,WANG S Q,et al.Study on impermeability of the bonding surface of UHPC-NC under sulphate erosion[J].China Concrete and Cement Products,2025(1):53-58.

浏览量:
1000
摘   要:研究了结合面粗糙度(Ⅰ、Ⅱ)、硫酸盐侵蚀龄期(0、45、90、210、330 d)对超高性能混凝土-普通混凝土(UHPC-NC)试件结合面抗渗性能的影响,并分析了微观机理。结果表明:无论结合面的粗糙度多大,随着侵蚀龄期的增加,UHPC-NC试件结合面的抗渗性能基本呈先增后降的趋势,当侵蚀龄期为90 d时,UHPC-NC试件结合面的抗渗性能相对最好;总体而言,相较于粗糙度为Ⅰ的UHPC-NC试件结合面,粗糙度为Ⅱ的UHPC-NC试件结合面的抗渗性能相对更好;在硫酸盐侵蚀下,UHPC-NC试件内部孔隙中生成了具有膨胀性的腐蚀产物(石膏、钙矾石),当其过量时会导致混凝土内部拉应力增大,产生膨胀裂缝,从而削弱UHPC-NC试件结合面的抗渗性能。 Abstract: The effects of the roughness(Ⅰ,Ⅱ) of bonding surface and the age (0, 45, 90, 210 and 330 d) of sulphate erosion on the impermeability of the bonding surface of ultra-high performance concrete-normal concrete(UHPC-NC) specimens were investigated, and the microscopic mechanism was analyzed. The results show that, regardless of the roughness of the bonding surface, with the increase of the erosion age, the impermeability of the bonding surface of UHPC-NC specimens basically shows a trend of first increasing and then decreasing, and the impermeability of the bonding surface of UHPC-NC specimens is basically the best when the erosion age is 90 d. Overall, the impermeability of the bonding surface of UHPC-NC specimens with roughness Ⅱ is better than that of the UHPC-NC specimens with roughness Ⅰ. Under the erosion of sulphate, the expansive corrosion products(gypsum, ettringite) are generated in the internal pores of the UHPC-NC specimen. When excessive, it can cause an increase in the internal tensile stress of the concrete, resulting in expansion cracks, and thus weakening the impermeability of the bonding surface of the UHPC-NC specimens.
英文名 : Study on impermeability of the bonding surface of UHPC-NC under sulphate erosion
刊期 : 2025年第1期
关键词 : 超高性能混凝土(UHPC);普通混凝土(NC);结合面;硫酸盐侵蚀;抗渗性能;微观形貌
Key words : Ultra-high performance concrete(UHPC); Normal concrete(NC); Bonding surface; Sulphate erosion; Impermeability; Microstructure
刊期 : 2025年第1期
DOI : 10.19761/j.1000-4637.2025.01.053.06
文章编号 :
基金项目 :
作者 : 李 涛1,范 钰1,王爽倩1,龙莉波2,马跃强2
单位 : 1.上海理工大学 环境与建筑学院,上海 200093;2.上海建工二建集团有限公司,上海 200080

李 涛1,范 钰1,王爽倩1,龙莉波2,马跃强2

李涛,范钰,王爽倩,等.硫酸盐侵蚀后UHPC-NC结合面的抗渗性能研究[J].混凝土与水泥制品,2025(1):53-58.

LI T,FAN Y,WANG S Q,et al.Study on impermeability of the bonding surface of UHPC-NC under sulphate erosion[J].China Concrete and Cement Products,2025(1):53-58.

摘要
参数
结论
参考文献
引用本文

摘   要:研究了结合面粗糙度(Ⅰ、Ⅱ)、硫酸盐侵蚀龄期(0、45、90、210、330 d)对超高性能混凝土-普通混凝土(UHPC-NC)试件结合面抗渗性能的影响,并分析了微观机理。结果表明:无论结合面的粗糙度多大,随着侵蚀龄期的增加,UHPC-NC试件结合面的抗渗性能基本呈先增后降的趋势,当侵蚀龄期为90 d时,UHPC-NC试件结合面的抗渗性能相对最好;总体而言,相较于粗糙度为Ⅰ的UHPC-NC试件结合面,粗糙度为Ⅱ的UHPC-NC试件结合面的抗渗性能相对更好;在硫酸盐侵蚀下,UHPC-NC试件内部孔隙中生成了具有膨胀性的腐蚀产物(石膏、钙矾石),当其过量时会导致混凝土内部拉应力增大,产生膨胀裂缝,从而削弱UHPC-NC试件结合面的抗渗性能。

Abstract: The effects of the roughness(Ⅰ,Ⅱ) of bonding surface and the age (0, 45, 90, 210 and 330 d) of sulphate erosion on the impermeability of the bonding surface of ultra-high performance concrete-normal concrete(UHPC-NC) specimens were investigated, and the microscopic mechanism was analyzed. The results show that, regardless of the roughness of the bonding surface, with the increase of the erosion age, the impermeability of the bonding surface of UHPC-NC specimens basically shows a trend of first increasing and then decreasing, and the impermeability of the bonding surface of UHPC-NC specimens is basically the best when the erosion age is 90 d. Overall, the impermeability of the bonding surface of UHPC-NC specimens with roughness Ⅱ is better than that of the UHPC-NC specimens with roughness Ⅰ. Under the erosion of sulphate, the expansive corrosion products(gypsum, ettringite) are generated in the internal pores of the UHPC-NC specimen. When excessive, it can cause an increase in the internal tensile stress of the concrete, resulting in expansion cracks, and thus weakening the impermeability of the bonding surface of the UHPC-NC specimens.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)随着侵蚀龄期的增加,粗糙度为Ⅰ的UHPC-NC试件结合面最大渗水高度平均值呈先降后增的趋势,粗糙度为Ⅱ的UHPC-NC试件结合面最大渗水高度平均值基本呈先降后增的趋势,当侵蚀龄期为90 d时,两种粗糙度结合面的最大渗水高度平均值均相对最低,分别为88.33 mm和80.00 mm。当侵蚀龄期相同时,相较于粗糙度为Ⅰ的UHPC-NC试件结合面,粗糙度为Ⅱ的UHPC-NC试件结合面的最大渗水高度相对较低。
(2)无论结合面粗糙度多大,随着侵蚀龄期的增加,UHPC-NC试件结合面的硫酸根离子浓度均呈增大的趋势,在90 d后,硫酸根离子浓度的增幅减缓并趋于平缓,且粗糙度为Ⅱ的UHPC-NC试件结合面的硫酸根离子浓度相对更低。
(3)随着侵蚀龄期的增加,粗糙度为Ⅱ的UHPC-NC试件结合面的相对渗透系数呈先略微增大后降低再增大的趋势,在90 d侵蚀龄期时,UHPC-NC试件结合面的相对渗透系数相对最低,较未侵蚀组提高了-15.45%。
(4)在硫酸盐侵蚀下,UHPC-NC 试件内部孔隙中生成了具有膨胀性的腐蚀产物(石膏、钙矾石),且随着侵蚀龄期的增加,UHPC-NC试件结合面的二水石膏浓度呈先降低后略微增大再降低的趋势,UHPC-NC试件结合面的钙矾石浓度呈增大趋势。适量的腐蚀产物体积膨胀能填充混凝土内部孔隙,但过量则会导致混凝土内部拉应力增大,产生膨胀裂缝,从而削弱UHPC-NC 结合面的抗渗性能。

[1] 钟蕴为,吴永魁,文许高媛,等.超高性能混凝土(UHPC)基本性能研究综述[J].混凝土与水泥制品,2021(9):1-4.
[2] HUANG Y,WANG J H,WEI Q,et al.Creep behaviour of ultra-high-performance concrete(UHPC): A review[J].Journal of Building Engineering,2023,69:106187.
[3] 刘阳阳,郑七振,龙莉波,等.基于超高性能水泥基材料的预制装配式框架结构体系创新研究[J].建筑施工,2018,40(9):1600-1602.
[4] 郑七振,陈威钢,龙莉波,等.UHPC连接的节点预制-构件预制装配式框架抗震性能试验研究[J].上海理工大学学报,2019,41(6):584-590.
[5] PENG Q,QIAN J X.Experimental investigation on properties of interface between concrete layers[J].Construction and Building Materials,2018,174:120-129.
[6] 高丹盈,程红强,冯虎.钢纤维混凝土与老混凝土黏结面渗透性能[J].水力发电学报,2009,28(1):152-158.
[7] 李平先,张雷顺,赵国藩,等.新老混凝土粘结面渗透性能试验研究[J].水利学报,2005(5):602-607.
[8] 吴应雄,郑新颜,黄伟,等.超高性能混凝土-既有普通混凝土界面粘结性能研究综述[J].材料导报,2023,37(16):144-154.
[9] 易成,谢和平,孙华飞,等.混凝土抗渗性能研究的现状与进展[J].混凝土,2003(2):7-11,34.
[10] 曹芳,马保国,李友国,等.混凝土的渗透性能及测试方法的对比分析[J].混凝土,2002(10):15-17.
[11] 苏安双,巴恒静,叶金蕊,等.混凝土渗透性测定方法比较与选择[J].工业建筑,2006(9):57-61.
[12] 杨志辉,祝雯,陈晋栋,等.混凝土抗渗透性能测试方法及其相关性综述[J].广东建材,2022,38(5):25-30,70.
[13] 钱觉时,张琳,贾兴文,等.基于电场作用的混凝土渗透性评价方法研究进展与展望[J].材料导报,2011,25(21):124-128.
[14] 赵顺波,陈记豪,高润东,等.硫酸盐侵蚀混凝土内部硫酸根离子浓度测试方法[J].港工技术,2008(3):31-33.
[15] 冯虎.钢纤维混凝土与既有混凝土粘结劈拉及抗渗性能试验研究[D].河南:郑州大学,2007.
[16] LI T,WANG S S.Modeling diffusion coefficient of sulfate ion in concrete using probabilistic approach[J].Construction and Building Materials,2019,215:435-446.
[17] 李涛,朱鹏涛,张彬,等.硫酸盐侵蚀下混凝土内腐蚀反应-扩散过程的实验研究[J].硅酸盐通报,2020,39(1):50-55.

李涛,范钰,王爽倩,.硫酸盐侵蚀后UHPC-NC结合面的抗渗性能研究[J].混凝土与水泥制品,2025(1):53-58.

LI T,FAN Y,WANG S Q,et al.Study on impermeability of the bonding surface of UHPC-NC under sulphate erosion[J].China Concrete and Cement Products,2025(1):53-58.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州