纤维-聚合物混凝土性能研究现状及在巷道中的应用展望
Research Status of Fiber-Polymer Concrete Performance and Its Application in Roadways
浏览量:
关键词：
力学性能；耐久性能；改性机理；软岩巷道
Key words：
Mechanical property; Durability; Modification mechanism; Soft rock roadway
刊期：
2020年2期
DOI：
10.19761/j.1000-4637.2020.02.051.05
文章编号：
基金项目：
河南省科技攻关项目（172102210286）；国家自然科学基金青年基金项目（51704094）；国家自然科学基金重点项目（51834001）。
作者：
史玉良，陈新明，焦华喆，韩晓龙，靳翔飞
单位：
河南理工大学土木工程学院，焦作454000
摘要
摘 要：介绍了国内外纤维-聚合物混凝土的研究进展，总结了纤维-聚合物混凝土的力学性能、韧性、耐久性能等，分析了纤维-聚合物混凝土的改性机理。最后，鉴于纤维-聚合物混凝土相比普通混凝土具有良好的韧性及耐久性能，对纤维-聚合物混凝土在软岩巷道中的应用进行了展望。
Abstract: The research progress of fiber-polymer concrete at home and abroad was introduced, the performance of fiber-polymer concrete from the aspects of mechanical properties, toughness and durability were summarized, and the modification mechanism of fiber-polymer concrete was analyzed. Finally, in view of the good toughness and durability of fiber polymer concrete compared with ordinary concrete, the application of fiber-polymer concrete in soft rock roadway was prospected.
结论
在混凝土中添加纤维与聚合物，纤维增强了混凝土整体强度和韧性，聚合物提高了混凝土基体与纤维的黏结力。巷道支护若采用具有良好工作性的纤维-聚合物喷射混凝土，则可更好地满足巷道的变形要求，起到良好的支护效果，尽可能达到“变形不开裂，开裂不掉落”的理想状况。
参考文献
[1] 吴中伟.纤维增强——水泥基材料的未来(提要)[A].纤维水泥制品行业纤维增强水泥及其制品论文选集（1）（1960～2009）[C].中国硅酸盐学会,2009.
[2] 罗立峰,周建春,黄培彦.聚合物钢纤维混凝土的增强机理分析[J].复合材料学报,2002(3):46-50.
[3] 韩晓龙,陈新明,焦华喆,等.聚合物-水泥基复合注浆材料研究现状及展望[J].硅酸盐通报,2018,37(8):2457-2462.
[4] 王勃,谭亚云,李宏波,等.路用橡胶粉-聚丙烯纤维混凝土力学性能研究[J].混凝土与水泥制品,2012(7):41-44.
[5] 郭建,张荣辉.水性环氧树脂增强钢纤维混凝土的力学性能及在桥面铺装层中的应用研究[J].混凝土与水泥制品,2006(4):52-54.
[6] 王艳艳,滕岩.掺合料增强透水混凝土的试验研究[J].建筑技术,2017,48(10):1030-1033.
[7] XU F,ZHOU M,CHEN J,et al.Mechanical performance evaluation of polyester fiber and SBR latex compound-modified cement concrete road overlay material[J].Construction and Building Materials,2014,63:142-149.
[8] NIAKI M H,FEREIDOON A.Experimental study on the mechanical and thermal properties of basalt fiber and nanoclay reinforced polymer concrete[J].Composite Structures,2018,191:231-238.
[9] 陈依伶.钢纤维聚合物混凝土与旧混凝土界面粘结性能及数值分析[D].重庆:重庆交通大学,2016.
[10] BHOGAYATA A C,ARORA N K.Workability, strength, and durability of concrete containing recycled plastic fibers and styrene-butadiene rubber latex[J].Construction and Building Materials,2018,180:382-395.
[11] 罗振帅.硅灰和聚合物乳液对钢纤维混凝土的断裂性能影响研究[D].重庆:重庆交通大学,2016.
[12] 刘瑞.钢纤维-水泥石界面特征及对混凝土断裂性能的影响[D].重庆:重庆交通大学,2017.
[13] REIS J M L.A contribution to the study of the fracture energy of polymer concrete and fibre reinforced polymer concrete[J].Polymer testing,2004,23(4):437-440.
[14] 唐瑞.钢纤维超吸水聚合物高性能混凝土耐腐蚀性能试验研究[D].银川:宁夏大学,2013.
[15] LU Y,HU J,LI S,et al.Active and passive protection of steel reinforcement in concrete column using carbon fibre reinforced polymer against corrosion[J].Electrochimica Acta,2018,278:124-136.
[16] PONMALAR V.Durability studies on confined concrete using fiber reinforced polymer[J].Journal of The Institution of Engineers (India):Series A,2014,95(2):91-96
[17] LIANG H,LI S,LU Y,et al.Electrochemical performance of corroded reinforced concrete columns strengthened with fiber reinforced polymer[J].Composite Structures,2019,207:576-588.
[18] 姚树义.纤维增韧聚合物水泥混凝土的性能研究[D].哈尔滨:哈尔滨工业大学,2011.
[19] WANG J.Investigation of properties and performances of Polyvinyl Alcohol (PVA) fiber-reinforced rubber concrete[J].Construction and Building Materials,2018,193:631-642
[20] 向超.硅灰和聚合物乳液对钢纤维混凝土的耐久性影响[D].重庆:重庆交通大学,2015.
[21] ALSAIF A,BERNAL S A,GUADAGNINI M,et al.Freeze-thaw resistance of steel fibre reinforced rubberised concrete[J].Construction and Building Materials,2019,195:450-458
[22] 高国锋.纤维与聚合物复掺对活性粉末混凝土性能的研究[D].重庆:重庆大学,2017.
[23] 成涛华,李玉香.玄武岩纤维增强混凝土力学性能研究[J].混凝土与水泥制品,2017(1):53-56.
[24] 李正,杰德尔别克,赵海涛,等.钢-聚丙烯纤维高性能混凝土力学性能试验研究[J].混凝土与水泥制品,2017(11):50-53.
[25] 焦华喆,韩振宇,陈新明,等.玄武岩纤维对喷射混凝土力学性能及微观结构的影响机制[J].复合材料学报,2019,36(8):1926-1934.
[26] OHAMA Y.Principle of latex modification and some typical properties of latex-modified mortars and concretes adhesion; binders (materials); bond (paste to aggregate); carbonation;chlorides;curing; diffusion[J].Materials Journal,1987,84(6):511-518.
[27] KONIETZKO A.Polymers pezifische auswerkungen auf dast ragverhalten modifizierter zementgebundenen beton (PCC)[D].Braunschweig,1988.
[28] PUTERMAN M.Some doubts and ideas on the microstructure formation of PCC[J].Bologna: Tagungsunterlagen,IX.ICPIC,1998:165-178.
[29] VAN G D,BEELDENS A.Evolution in modeling microstructure formation in polymer-cement concrete[J].Restoration of Buildings and Monuments,2013,19(2-3):97-108.
[30] 张军帅.混杂钢纤维聚合物改性水泥混凝土特殊铺装材料性能研究[D].重庆:重庆交通大学,2017.
[31] 王祉翔.钢纤维聚合物改性水泥混凝土特殊铺装材料性能研究[D].重庆:重庆交通大学,2017.
引用本文
史玉良,陈新明,焦华喆,等.纤维-聚合物混凝土性能研究现状及在巷道中的应用展望[J].混凝土与水泥制品,2020(2):51-54,70.
SHI Y L,CHEN X M,JIAO H Z,Research Status of Fiber-Polymer Concrete Performance and Its Application in Roadways[J].China Concrete and Cement Products,2020(2):51-54,70.
下一个： HRB400钢筋与钢纤维再生混凝土黏结性能及影响因素分析
相关文件