大流动度混杂纤维增强混凝土耐久性试验研究
Experimental Research on Durability of Hybrid Fiber Reinforced Concrete with High Fluidity
2017年第8期
大流动度混杂纤维增强混凝土;基本力学性能;耐久性能
Hybrid fiber reinforced concrete with high fluidity; Basic mechanical property; Durability
2017年第8期
1000-4637(2017)08-52-04
惠建许,杜增强,高建军,刘向坤
中核混凝土股份有限公司,武汉 430100)

惠建许,杜增强,高建军,刘向坤

惠建许,杜增强,高建军,等.大流动度混杂纤维增强混凝土耐久性试验研究[J].混凝土与水泥制品,2017(8):52-55.

HUI J X, DU Z Q, GAO J J,et al.Experimental Research on Durability of Hybrid Fiber Reinforced Concrete with High Fluidity[J].China Concrete and Cement Products,2017(8):52-55.

浏览量:
1000
摘  要:在纤维总体积掺率不超过1%的情况下,采用钢纤维、塑钢纤维及聚丙烯纤维单掺、双掺和三掺配制得到高流动度纤维增强混凝土。通过稠度试验、基本力学性能试验以及耐久性试验,对比分析了纤维混杂方式和纤维混掺比例对基体混凝土工作性能、基本力学性能以及耐久性的影响。结果表明,钢纤维/塑钢纤维/聚丙烯三元混杂可有效改善基体混凝土的抗压强度和劈裂强度,最大分别提高了25%和32.61%;大流动度混杂纤维增强混凝土的抗渗等级可满足P8要求,具有良好的抗渗性能,最大渗水高度仅为29mm;大流动度混杂纤维增强混凝土的抗冻等级可满足F250要求,且前175次冻融循环质量损失率维持在1%~2%;基于工作性能、基本力学性能以及耐久性最优的混掺比例为0.4%SF、0.4%HF、0.11%PPF。Abstract:Withthetotalvolumefractionoffibersbelow1.1%,thefiberreinforcedconcretewithhighfluidityispreparedbyaddingsteelfiber,steelfiberandpolypropylenefibersingle,doubleortriple.Experimentonmechanicalproperties,frost-resistanceandimpermeabilityofhybridreinforcedconcretewerecarriedout.Basedonthetestresults,theeffectoffibervolumefractionandhybridmodeuponthemechanicalpropertyanddurabilityoftheHFRCareanalyzed.TheresultsshowthatSF/HF/PPFHFRCcansignificantlyimprovethecompressivestrengthandsplittingstrengthofthematrixconcretewithlargely25%and32.61%respectively.ThefiberreinforcedconcretewithhighfluidityownswonderfulimperviousperformanceanditcanmeettherequirementsofP8withtheminimumpenetrationheightof29mm.Thefiberreinforcedconcretewithhighfluidityownswonderfulanti-freezingpropertyanditcanmeettherequirementsofF250.Andthemasslossrateof175freeze-thawcyclesisonly1%~2%.Onthebasisoftheworkingperformance,mechanicalpropertyanddurability,themostsuitablefibersproportionofCF60is0.4%SF,0.4%HFand0.11%PPF.
英文名 : Experimental Research on Durability of Hybrid Fiber Reinforced Concrete with High Fluidity
刊期 : 2017年第8期
关键词 : 大流动度混杂纤维增强混凝土;基本力学性能;耐久性能
Key words : Hybrid fiber reinforced concrete with high fluidity; Basic mechanical property; Durability
刊期 : 2017年第8期
DOI :
文章编号 : 1000-4637(2017)08-52-04
基金项目 :
作者 : 惠建许,杜增强,高建军,刘向坤
单位 : 中核混凝土股份有限公司,武汉 430100)

惠建许,杜增强,高建军,刘向坤

惠建许,杜增强,高建军,等.大流动度混杂纤维增强混凝土耐久性试验研究[J].混凝土与水泥制品,2017(8):52-55.

HUI J X, DU Z Q, GAO J J,et al.Experimental Research on Durability of Hybrid Fiber Reinforced Concrete with High Fluidity[J].China Concrete and Cement Products,2017(8):52-55.

摘要
参数
结论
参考文献
引用本文

摘   要:在纤维总体积掺率不超过1%的情况下,采用钢纤维、塑钢纤维及聚丙烯纤维单掺、双掺和三掺配制得到高流动度纤维增强混凝土。通过稠度试验、基本力学性能试验以及耐久性试验,对比分析了纤维混杂方式和纤维混掺比例对基体混凝土工作性能、基本力学性能以及耐久性的影响。结果表明,钢纤维/塑钢纤维/聚丙烯三元混杂可有效改善基体混凝土的抗压强度和劈裂强度,最大分别提高了25%和32.61%;大流动度混杂纤维增强混凝土的抗渗等级可满足P8要求,具有良好的抗渗性能,最大渗水高度仅为29mm;大流动度混杂纤维增强混凝土的抗冻等级可满足F250要求,且前175次冻融循环质量损失率维持在1%~2%;基于工作性能、基本力学性能以及耐久性最优的混掺比例为0.4%SF、0.4%HF、0.11%PPF。

Abstract: With the total volume fraction of fibers below 1.1%, the fiber reinforced concrete with high fluidity is prepared by adding steel fiber, steel fiber and polypropylene fiber single, double or triple. Experiment on mechanical properties, frost-resistance and impermeability of hybrid reinforced concrete were carried out. Based on the test results, the effect of fiber volume fraction and hybrid mode upon the mechanical property and durability of the HFRC are analyzed. The results show that SF/HF/PPF HFRC can significantly improve the compressive strength and splitting strength of the matrix concrete with largely 25% and 32.61% respectively. The fiber reinforced concrete with high fluidity owns wonderful impervious performance and it can meet the requirements of P8 with the minimum penetration height of 29mm. The fiber reinforced concrete with high fluidity owns wonderful anti-freezing property and it can meet the requirements of F250. And the mass loss rate of 175 freeze-thaw cycles is only 1%~2%. On the basis of the working performance, mechanical property and durability, the most suitable fibers proportion of CF60 is 0.4%SF, 0.4%HF and 0.11% PPF.


关键词:
大流动度混杂纤维增强混凝土;基本力学性能;耐久性能
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)通过掺加(0.4±0.1)%的引气剂和提高基准混凝土的工作性能[坍落度(160±20)mm,坍落扩展度(280±20)mm],可以确保纤维掺入后基体混凝土仍具有良好的工作性能。
(2)混杂纤维的掺入可以显著提高基体混凝土的抗压强度和劈裂抗拉强度,抗压强度最大可提高25%,劈裂抗拉强度最大可提高32.61%。
(3)纤维的掺入对基体混凝土抗冻等级和抗渗等级的提升效果并不明显,但可有效降低基本混凝土的渗水高度和前175次冻融循环的质量损失率,并可以保证基体混凝土的相对动弹性模量维持在较高水平。
(4)综合考虑大流动度混杂纤维增强混凝土的工作性能、基本力学性能以及耐久性能,最佳纤维混掺比例为0.4%SF、0.4%HF、0.11%PPF。
[1] 赵亮平,高丹盈,朱海堂.钢纤维对混凝土强度和韧性的影响[J].华北水利水电学院学报,2012,33(6):29-32.
[2] 闫长旺,贾金青,张菊.钢纤维增强超高强混凝土拉压比试验研究[J].大连理工大学学报,2012,52(2):233-238.
[3] 梅国栋,李继祥,刘肖凡,等.混杂纤维混凝土抗弯性能及混杂效应试验研究[J].混凝土,2013(2):21-24.
[4] 孙海燕,何真.混杂纤维对混凝土力学及抗裂性能的影响[J].混凝土与水泥制品,2009(2):48-51.
[5] 王海超,刘校源.较高韧性混杂纤维混凝土弯曲抗拉性能试验研究[J].混凝土与水泥制品,2011(4):46-49.
[6] 夏冬桃,刘向坤,夏广政,等.混杂纤维增强高性能混凝土弯曲韧性研究[J].华中科技大学学报:自然科学版,2013,41(6):108-112. 
[7] 王德志,孟云芳,万良兴.纤维素纤维矿物掺合料复掺改善高性能混凝土抗渗性研究[J].混凝土与水泥制品,2009(6):35-38.
[8] 钱红萍,李书进.矿物掺合料与纤维双掺对混凝土抗渗性能的影响及工程应用[J].混凝土与水泥制品,2011(10):46-47.
[9] 王学志,郑淑文,贺晶晶,等.基于抗渗性的纤维混凝土耐久性评价体系[J].混凝土与水泥制品,2015(1):46-51.
[10] 张永存,李青宁,房辰泽.基于细观分析的纤维混凝土力学性能及耐久性研究[J].混凝土,2016(8):48-50.
[11] 杨成蛟,黄承逵,车轶,等.混杂纤维混凝土的力学性能及抗渗性能[J].建筑材料学报,2008(1):89-93.
[12] 向阳开,蓝祥雨.隧道聚丙烯纤维混凝土抗渗性能分析及试验比较[J].土木建筑与环境工程,2010(5):114-118.

惠建许,杜增强,高建军,.大流动度混杂纤维增强混凝土耐久性试验研究[J].混凝土与水泥制品,2017(8):52-55.

HUI J X, DU Z Q, GAO J J,et al.Experimental Research on Durability of Hybrid Fiber Reinforced Concrete with High Fluidity[J].China Concrete and Cement Products,2017(8):52-55.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州