机制砂对湿拌砂浆性能的影响研究
Effects Study of Manufactured Sand on Performance of Wet-mixed Mortar
2017年第10期
机制砂;细度模数;湿拌砂浆;颗粒级配
Manufactured sand; Fineness modulus; Wet-mixed mortar; Particle gradation
2017年第10期
1000-4637(2017)10-89-05
重庆市建设科技计划项目(2016-53)
邢光延1,叶建雄1,白 光1,黄利平2
(1.重庆大学材料科学与工程学院,400045;2.重庆众联新型材料有限公司,400074

邢光延1,叶建雄1,白 光1,黄利平2

邢光延,叶建雄,白光,等.机制砂对湿拌砂浆性能的影响研究[J].混凝土与水泥制品,2017(10):89-93.

XING G Y, YE J X, BAI G,et al.Effects Study of Manufactured Sand on Performance of Wet-mixed Mortar[J].China Concrete and Cement Products,2017(10):89-93.

浏览量:
1000
摘  要:通过设计不同粗细和级配的机制砂,研究了机制砂细度模数和级配对湿拌砂浆性能的影响。结果表明,当机制砂细度模数在1.2~3.0时,随着机制砂细度模数的增大,湿拌砂浆单方用水量减小,保水性下降,和易性和抗压强度呈先提高后降低,干缩率呈先减小后增大的变化规律。当机制砂公称粒径在0.315mm以上颗粒的分计筛余相同时,随着机制砂中小于0.315mm颗粒含量的增加,湿拌砂浆力学性能先提高后降低,干缩率先减小后增大。控制机制砂中小于0.315mm细颗粒含量为30%,机制砂中大于1.25mm颗粒含量超过30%时,湿拌砂浆拉伸黏结强度明显降低,干缩率显著增大。Abstract:Throughthedesignofmanufacturedsandwithdifferentfinenessmodulusandgradation,theinfluenceoffinenessmodulusandgradationofmachine-madesandontheperformanceofwet-mixedmortarisstudied.Theresultsshowthatwhenthefinenessmodulusofsandisintherangeof1.2~3.0,withtheincreaseofthemodulusofsand,thewaterconsumptionofwet-mixedmortarisreduced,thewaterretentionisdecreased,theworkabilityandcompressionstrengthincreasesfirstandthendecreases,andtheshrinkageratedecreasesandthenincreases.Whengraderretainedpercentageofsandgreaterthan0.315mmisthesame,themechanicalpropertiesofthewet-mixedmortarareimprovedandthendecreases,andtheshrinkageratedecreasesfirstandthenincreaseswiththeincreaseofthecontentofparticleslessthan0.315mminthesand.Controlmachine-madesandlessthan0.315mmparticlecontentof30%,whenthecontentofgreaterthan1.25mmparticlesismorethan30%,thetensilebondstrengthofwet-mixedmortarisobviouslyreducedandtheshrinkagerateissignificantlyincreased.
英文名 : Effects Study of Manufactured Sand on Performance of Wet-mixed Mortar
刊期 : 2017年第10期
关键词 : 机制砂;细度模数;湿拌砂浆;颗粒级配
Key words : Manufactured sand; Fineness modulus; Wet-mixed mortar; Particle gradation
刊期 : 2017年第10期
DOI :
文章编号 : 1000-4637(2017)10-89-05
基金项目 : 重庆市建设科技计划项目(2016-53)
作者 : 邢光延1,叶建雄1,白 光1,黄利平2
单位 : (1.重庆大学材料科学与工程学院,400045;2.重庆众联新型材料有限公司,400074

邢光延1,叶建雄1,白 光1,黄利平2

邢光延,叶建雄,白光,等.机制砂对湿拌砂浆性能的影响研究[J].混凝土与水泥制品,2017(10):89-93.

XING G Y, YE J X, BAI G,et al.Effects Study of Manufactured Sand on Performance of Wet-mixed Mortar[J].China Concrete and Cement Products,2017(10):89-93.

摘要
参数
结论
参考文献
引用本文

摘   要:通过设计不同粗细和级配的机制砂,研究了机制砂细度模数和级配对湿拌砂浆性能的影响。结果表明,当机制砂细度模数在1.2~3.0时,随着机制砂细度模数的增大,湿拌砂浆单方用水量减小,保水性下降,和易性和抗压强度呈先提高后降低,干缩率呈先减小后增大的变化规律。当机制砂公称粒径在0.315mm以上颗粒的分计筛余相同时,随着机制砂中小于0.315mm颗粒含量的增加,湿拌砂浆力学性能先提高后降低,干缩率先减小后增大。控制机制砂中小于0.315mm细颗粒含量为30%,机制砂中大于1.25mm颗粒含量超过30%时,湿拌砂浆拉伸黏结强度明显降低,干缩率显著增大。

Abstract: Through the design of manufactured sand with different fineness modulus and gradation, the influence of fineness modulus and gradation of machine-made sand on the performance of wet-mixed mortar is studied. The results show that when the fineness modulus of sand is in the range of 1.2~3.0, with the increase of the modulus of sand, the water consumption of wet-mixed mortar is reduced, the water retention is decreased, the workability and compression strength increases first and then decreases, and the shrinkage rate decreases and then increases. When grader retained percentage of sand greater than 0.315mm is the same, the mechanical properties of the wet-mixed mortar are improved and then decreases, and the shrinkage rate decreases first and then increases with the increase of the content of particles less than 0.315mm in the sand. Control machine-made sand less than 0.315mm particle content of 30%, when the content of greater than 1.25mm particles is more than 30%, the tensile bond strength of wet-mixed mortar is obviously reduced and the shrinkage rate is significantly increased.

关键词:
机制砂;细度模数;湿拌砂浆;颗粒级配
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)当机制砂细度模数在1.2~3.0时,随着机制砂细度模数的增大,湿拌砂浆单方用水量减小,保水性下降,和易性和抗压强度呈先提高后降低,干缩率呈先减小后增大的变化规律。机制砂细度模数为2.1~2.4时,湿拌砂浆的和易性良好,抗压强度较高,干缩率较小。
(2)当机制砂公称粒径在0.315mm以上颗粒的分计筛余相同时,随着机制砂中小于0.315mm细颗粒含量的增加,湿拌砂浆的各项力学性能先提高后降低,干缩率先减小后增大。控制机制砂中小于0.315mm细颗粒含量为30%,机制砂中大于1.25mm颗粒含量超过30%时,湿拌砂浆各龄期的抗压强度都略有增长,但拉伸黏结强度明显降低,干缩率显著增大。
(3)选用细颗粒(公称粒径小于0.315mm)含量在20%~30%,各级粗颗粒(公称粒径大于0.315mm)分计筛余在25%左右,细度模数在2.1~2.4范围左右的机制砂可以配制出工作性能、力学性能和收缩性能较好的湿拌抹灰砂浆。
[1] 豆晓玲.湿拌砂浆和传统现场搅拌砂浆施工性能对比[J]. 广东建材,2014(11):102-104.
[2] 鲁恩侨.浅谈机制砂的应用[J].建筑与预算,2014(2):49-51.
[3] 王稷良.机制砂特性对混凝土性能的影响及机理研究[D]. 武汉:武汉理工大学,2008.
[4] 蒋正武,孙振平,梅世龙,等.矿物掺合料对机制砂砂浆性能的影响[J].粉煤灰综合利用,2006(5):17-19.
[5] 王磊,赵顺波,梁娜.聚丙烯纤维机制砂水泥砂浆早期抗裂性能试验研究[J].河南大学学报:自然科学版,2014(3):370-374.
[6] 李凤兰,梁娜,李长永.聚丙烯纤维和机制砂中石粉对水泥砂浆抗裂性能的影响[J].应用基础与工程科学学报,2012(5):895-901.
[7] 孔凌宇,王磊,韩冰.石粉含量对机制砂水泥砂浆抗冻性能的影响[J].河南理工大学学报:自然科学版,2015(5):717-721.
[8] 周爱军,周红.机制砂在普通砂浆中应用试验研究[J].硅酸盐通报,2016(1):310-315,321.
[9] 刘桂凤,陈正发,秦彦龙,等.石粉部分替代水泥对机制砂干混砂浆力学性能的影响[J].混凝土与水泥制品,2011(12):49-52.
[10] 王雨利,刘素霞,王卫东,等.机制砂砂浆干缩性能的研究[J].材料导报,2011(18):113-116.
[11] Goncalves J P,Tavares L M,Toledo Filho R D,et al.Compari sion of natural and manufactured fine aggregates in cement mortars[J].Cement and Concret Research,2007,37(6):924-932.
[12] Cortes D D, Kim H K, Palomino A M, et al.Rheological and mechanical properties of mortars prepared with  natural and manufactured sands[J].Cement and Concret Research,2008,38(10):1142-1147. 
[13] 刘桂凤,李世超,秦彦龙,等.不同机制砂级配对干混砂浆性能的影响[J].混凝土,2013(9):112-114,117.
[14] 胡建伟,闻宝联.机制砂级配对水泥砂浆性能的影响规律及作用效应[J].混凝土世界,2015(11):88-91. 
[15] 陈景,刘永道,王晶晶,等.机制砂湿拌抹灰砂浆研究与生产应用[J].混凝土与水泥制品,2015(3):66-70.

邢光延,叶建雄,白光,.机制砂对湿拌砂浆性能的影响研究[J].混凝土与水泥制品,2017(10):89-93.

XING G Y, YE J X, BAI G,et al.Effects Study of Manufactured Sand on Performance of Wet-mixed Mortar[J].China Concrete and Cement Products,2017(10):89-93.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州