原生混凝土强度对再生混凝土力学性能及界面区微结构的影响
2019年1期  
再生混凝土;再生骨料;力学性能;界面区微结构
Recycled concrete; Recycled aggregate; Mechanical property; Micro-structure
2019年第1期
10.19761/j.1000-4637.2019.01.010.05
国家自然科学基金资助项目(U1504508);河南省教育厅高等学校重点科研项目(15A430015);河南省高等学校青年骨干教师培养计划(2015GGJS-013);河南省省级新型墙体材料专项基金项目(20160304)。
王继娜,徐开东,李志新,马先伟,牛季收,杨 欢,金 彪
河南城建学院材料与化工学院,平顶山 467036

王继娜,徐开东,李志新,马先伟,牛季收,杨 欢,金 彪

王继娜,徐开东,李志新,等.原生混凝土强度对再生混凝土力学性能及界面区微结构的影响[J].混凝土与水泥制品,2019(1):10-14.

WANG J N,XU K D,LI Z X,et al.The Influence of Original Concrete Strength on Mechanical Properties and Interface Micro-structure of Recycled Aggregate Concrete[J].China Concrete and Cement Products,2019(1):10-14.

浏览量:
1000
摘要:为了改善再生骨料混凝土的性能,研究了原生混凝土强度对再生混凝土力学性能及界面区微结构的影响,并对比分析了相同强度等级和水灰比情况下普通混凝土和再生混凝土的力学性能和界面区微观形貌。结果表明:强度等级相同时,为了达到与普通混凝土相同的流动度,再生混凝土中除了加入一定量的附加水之外,还需要加入一定量的水泥浆,且随着原生混凝土强度的增加,水泥浆的加入量逐渐增加;在侧向无限制受压破坏时,再生混凝土与普通混凝土破坏形式基本相同,且原生混凝土强度对再生混凝土的破坏形式影响不大;强度等级相同时,再生混凝土的28d抗压强度高于普通混凝土,且随着原生混凝土强度的增加,早期强度逐渐降低,28d强度逐渐增大;水灰比相同时,普通混凝土各个龄期的抗压强度均高于再生混凝土。 Abstract: Inordertoimprovethepropertiesofrecycledconcrete,theeffectoforiginalconcretestrengthonthemechanicalpropertyandinterfacemicro-structureofrecycledaggregateconcretewerestudied.AndthepropertiesaboveofrecycledconcretewerecomparedwiththatofcommonconcreteunderthesameofstrengthgradeandW/C.Theresultsshowthatacertainamountofadditionalwaterandcementpasteshouldbeaddedtorecycledconcreteinordertoachievethesamefluiditywiththecommonconcreteundersamestrengthgrade.Andtheadditionalquantityofcementpasteincreasesaswellastheoriginalconcretestrengthincrease.Whentheconcreteisdamagedunderpressureandthelateralnolimit,thefailuremodeofrecycledconcreteisalmostthesameasthecommonconcrete.Andtheeffectoforiginalconcretestrengthonthefailuremodeofrecycledconcreteissmall.The28daycompressionstrengthofrecycledconcreteishigherthanthatofcommonconcreteundersamestrengthgrade.Earlystrengthdecreasesand28daycompressionstrengthincreasesastheoriginalconcretestrengthincrease.ThecompressionstrengthofeachageofcommonconcreteishigherthanthatofrecycledconcreteunderthesameW/C.
英文名 :
刊期 : 2019年1期  
关键词 : 再生混凝土;再生骨料;力学性能;界面区微结构
Key words : Recycled concrete; Recycled aggregate; Mechanical property; Micro-structure
刊期 : 2019年第1期
DOI : 10.19761/j.1000-4637.2019.01.010.05
文章编号 :
基金项目 : 国家自然科学基金资助项目(U1504508);河南省教育厅高等学校重点科研项目(15A430015);河南省高等学校青年骨干教师培养计划(2015GGJS-013);河南省省级新型墙体材料专项基金项目(20160304)。
作者 : 王继娜,徐开东,李志新,马先伟,牛季收,杨 欢,金 彪
单位 : 河南城建学院材料与化工学院,平顶山 467036

王继娜,徐开东,李志新,马先伟,牛季收,杨 欢,金 彪

王继娜,徐开东,李志新,等.原生混凝土强度对再生混凝土力学性能及界面区微结构的影响[J].混凝土与水泥制品,2019(1):10-14.

WANG J N,XU K D,LI Z X,et al.The Influence of Original Concrete Strength on Mechanical Properties and Interface Micro-structure of Recycled Aggregate Concrete[J].China Concrete and Cement Products,2019(1):10-14.

摘要
参数
结论
参考文献
引用本文
摘要:为了改善再生骨料混凝土的性能,研究了原生混凝土强度对再生混凝土力学性能及界面区微结构的影响,并对比分析了相同强度等级和水灰比情况下普通混凝土和再生混凝土的力学性能和界面区微观形貌。结果表明:强度等级相同时,为了达到与普通混凝土相同的流动度,再生混凝土中除了加入一定量的附加水之外,还需要加入一定量的水泥浆,且随着原生混凝土强度的增加,水泥浆的加入量逐渐增加;在侧向无限制受压破坏时,再生混凝土与普通混凝土破坏形式基本相同,且原生混凝土强度对再生混凝土的破坏形式影响不大;强度等级相同时,再生混凝土的28 d抗压强度高于普通混凝土,且随着原生混凝土强度的增加,早期强度逐渐降低,28 d强度逐渐增大;水灰比相同时,普通混凝土各个龄期的抗压强度均高于再生混凝土。
 
Abstract: In order to improve the properties of recycled concrete, the effect of original concrete strength on the mechanical property and interface micro-structure of recycled aggregate concrete were studied. And the properties above of recycled concrete were compared with that of common concrete under the same of strength grade and W/C. The results show that a certain amount of additional water and cement paste should be added to recycled concrete in order to achieve the same fluidity with the common concrete under same strength grade. And the additional quantity of cement paste increases as well as the original concrete strength increase. When the concrete is damaged under pressure and the lateral no limit, the failure mode of recycled concrete is almost the same as the common concrete. And the effect of original concrete strength on the failure mode of recycled concrete is small. The 28 day compression strength of recycled concrete is higher than that of common concrete under same strength grade. Early strength decreases and 28 day compression strength increases as the original concrete strength increase. The compression strength of each age of common concrete is higher than that of recycled concrete under the same W/C. 
关键词:
再生混凝土;再生骨料;力学性能;界面区微结构
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)随着原生混凝土强度的增大,再生混凝土的流动性逐渐降低,黏聚性和保水性良好,为了达到相同的流动度,再生混凝土中除了加入相应的附加水之外,还需加入一定的水泥浆,水泥浆的加入量随着原生混凝土强度的增大而增加。
(2)普通混凝土和再生混凝土在侧向无限制受压破坏时,再生混凝土与普通混凝土破坏形式基本相同,且原生混凝土强度对再生混凝土的破坏形式影响不大。
(3)原生混凝土强度对再生混凝土影响比较大。3 d和7 d龄期时,水泥的水化不完全,对再生混凝土的强度和界面区微结构影响较大的是再生骨料的孔隙率和吸水率;28 d龄期时,水泥水化较完全,此时再生骨料本身的强度和附着砂浆层的数量(反应活性)对再生混凝土的强度和界面区微结构影响较大。因此,随着原生混凝土强度的增加,再生骨料混凝土的3 d和7 d抗压强度逐渐降低,28 d抗压强度逐渐升高。C30的再生混凝土与普通混凝土相比,早期抗压强度均较高,原生强度较低的混凝土制得的再生骨料混凝土28 d强度略低于普通混凝土,当原生混凝土强度较高时制得的再生骨料混凝土28 d强度略高于普通混凝土;如果普通混凝土和再生混凝土采用同一水灰比,则普通混凝土各个龄期的抗压强度均高于再生混凝土。
[1] G. Santha Kumar, A. K. Minocha. Studies on thermo-chemical treatment of recycled concrete fine aggregates for use in concrete[J]. Journal of Material Cycles and Waste Management,2018,20(1):469-480.
[2] 郭远新,李秋义,孔哲,等.再生粗骨料强化处理工艺对再生混凝土性能的影响[S].混凝土与水泥制品,2015(6):11-17.
[3] 元成方,李爽,曾力,等. 砖砼混合再生粗骨料混凝土力学性能研究[J].硅酸盐通报,2018,37(2):398-402.
[4] 张玉栋,张立群,郭强,等.基于骨料掺配的再生混凝土界面和力学性能研究[J].混凝土与水泥制品,2018(4):99-101.
[5] 肖建庄,黄凯文,李龙.模型再生混凝土单轴受压静力与疲劳性能数值仿真[J].东南大学学报:自然科学版,2016,46(3):552-558.
[6] Seyedhamed Sadati, Kamal H. Khayat. Restrained shrinkage cracking of recycled aggregate concrete [J]. Materials and Structures,2017,50(4):206-220.
[7] 史才军,曹芷杰,谢昭彬. 再生混凝土力学性能的研究进展[J].材料导报,2016,30(12):96-103,126.
[8] M. Chakradhara Rao. Properties of recycled aggregate and recycled aggregate concrete: effect of parent concrete [J]. Asian Journal of Civil Engineering, 2018,19(1):103-110.
[9] 李军涛,陈宇良,陈宗平,等.不同骨料来源再生混凝土常规三轴受压性能研究[J].混凝土,2015(2):65-68.
[10]  Shi-cong Kouab, Chi-sun Poona. Effect of the quality of parent concrete on the properties of high performance recycled aggregate concrete [J]. Construction and Building Materials, 2015,77:501-508.
[11] 邓寿昌,罗冠祥.再生混凝土配合比设计新方法研究与验证[R].广东:第三届全国再生混凝土学术交流会,2014.
王继娜,徐开东,李志新,等.原生混凝土强度对再生混凝土力学性能及界面区微结构的影响[J].混凝土与水泥制品,2019(1):10-14.
WANG J N,XU K D,LI Z X,et al.The Influence of Original Concrete Strength on Mechanical Properties and Interface Micro-structure of Recycled Aggregate Concrete[J].China Concrete and Cement Products,2019(1):10-14.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州