磷渣-磷尾矿制备硅酸钙板的研究
Study of Calcium Silicate Board Prepared by Phosphorus Slag-phosphorus Tailings
2016年第3期
磷渣;磷尾矿;硅酸钙板;抗折强度
Phosphorus slag; Phosphorus tailings; Calcium silicate board; Flexural strength
2016年第3期
1000-4637(2016)03-87-04
国家科技支撑计划项目(2013BAB07B05)
梁兴荣1,2,薛 俊2,曹 宏2
1.甘肃省建材科研设计院,兰州 730020;2.武汉工程大学材料科学与工程学院,430074)

梁兴荣1,2,薛 俊2,曹 宏2

浏览量:
1000
摘 要:通过对比不同粒度磷渣作为胶凝材料的火山灰活性、磷尾矿作为惰性填料和将磷尾矿处理后物料制备硅酸钙板制品,结果表明,S95级磷渣28d火山灰活性指数>90%;磷尾矿作为惰性填料制备出的制品抗折强度<6MPa且尾矿的掺量<10%;磷尾矿处理后物料制备出制品抗折强度>9MPa且配比中废弃物的掺量>40%,制品抗折强度随着保温时间延长逐渐降低,最佳保温时间为6h。 Abstract: Preparation calcium silicate board by using solid waste from phosphorus chemical industry, the volcanic activity of different particle size of phosphorus slag as cementitious material is compared, phosphorus tailings as inert fillers and calcium silicate board is prepared by materials after phosphorus tailings had processed. The results show that, level S95 phosphorus slag of 28d volcanic activity index is more than 90%; flexural strength of the product which is prepared by phosphorus tailings as inert filler is less than 6MPa and the tailings content is less than 10%; flexural strength of the product which is prepared after phosphorus tailings had processed is more than 9MPa and the tailings content is more than 40%, the flexural strength of the products is gradually decreased with the prolonging of holding time, the optimal holding time is 6h.
英文名 : Study of Calcium Silicate Board Prepared by Phosphorus Slag-phosphorus Tailings
刊期 : 2016年第3期
关键词 : 磷渣;磷尾矿;硅酸钙板;抗折强度
Key words : Phosphorus slag; Phosphorus tailings; Calcium silicate board; Flexural strength
刊期 : 2016年第3期
DOI :
文章编号 : 1000-4637(2016)03-87-04
基金项目 : 国家科技支撑计划项目(2013BAB07B05)
作者 : 梁兴荣1,2,薛 俊2,曹 宏2
单位 : 1.甘肃省建材科研设计院,兰州 730020;2.武汉工程大学材料科学与工程学院,430074)

梁兴荣1,2,薛 俊2,曹 宏2

摘要
参数
结论
参考文献
引用本文

摘   要:通过对比不同粒度磷渣作为胶凝材料的火山灰活性、磷尾矿作为惰性填料和将磷尾矿处理后物料制备硅酸钙板制品,结果表明,S95级磷渣28d火山灰活性指数>90%;磷尾矿作为惰性填料制备出的制品抗折强度<6MPa且尾矿的掺量<10%;磷尾矿处理后物料制备出制品抗折强度>9MPa且配比中废弃物的掺量>40%,制品抗折强度随着保温时间延长逐渐降低,最佳保温时间为6h。

Abstract: Preparation calcium silicate board by using solid waste from phosphorus chemical industry, the volcanic activity of different particle size of phosphorus slag as cementitious material is compared, phosphorus tailings as inert fillers and calcium silicate board is prepared by materials after phosphorus tailings had processed. The results show that, level S95 phosphorus slag of 28d volcanic activity index is more than 90%; flexural strength of the product which is prepared by phosphorus tailings as inert filler is less than 6MPa and the tailings content is less than 10%; flexural strength of the product which is prepared after phosphorus tailings had processed is more than 9MPa and the tailings content is more than 40%, the flexural strength of the products is gradually decreased with the prolonging of holding time, the optimal holding time is 6h.

关键词:
磷渣;磷尾矿;硅酸钙板;抗折强度
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)S95级、S105磷渣的火山灰活性指数>90%,28d火山灰活性指数S105级较S95级大不足5%。
(2)磷尾矿作为惰性填料制备出的板材抗折强度<6MPa,尾矿的掺量不足10%,因此,磷尾矿作为惰性填料制备硅酸钙板不具有可行性。
(3)磷尾矿处理后物料制备出的制品随保温时间(6~10h)的延长,制品抗折强度呈现递减的趋势,最佳保温时间为6h。最佳配比、最佳保温时间制备出的制品抗折强度>9.5MPa,导热系数<0.20(W/m·K),其他各项性能均符合标准要求。
(4)利用工业废渣制备高附加值的硅酸钙板除具有可观的经济效益外,还能有效缓解环境污染,使矿产资源得到最大限度的综合利用。
[1] 魏莹,李兆锋,李丙明,等. 磷渣对水泥混凝土性能的影响及机理探讨[J].硅酸盐通报,2008(4):822-826.
[2] 高旭伟,吴勇生.黄磷渣资源化利用的现状及发展趋势[J]. 中国资源综合利用,2010(1):28-30.
[3] 黄芳,刘世荣,李军旗,等.磷尾矿中磷镁赋存状态及其矿物特征研究[J].矿物学报,2010(2):257-261.
[4] 金恒,邱跃琴,张覃,等.磷尾矿制备胶结充填材料试验研究[J].化工矿物与加工,2013(12):21-24.
[5] 陈明,孙振平,刘建山. 磷渣活性激发方法及机理研究进展[J].材料导报,2013,21:112-116.
[6] 梁兴荣,王其林,张英英,等.从反浮选磷尾矿中回收磷的研究[J].非金属矿,2014(5):64-65. 

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州