混凝土表面电阻率与电通量的相关性研究

Relevant Research on Surface Resistivity and Electric Flux of Concrete

浏览量:

关键词：

表面电阻率；四电极法；电通量；渗透性

Key words：

Surface resistivity; Wenner four-probe measurement; Electric flux; Permeability

刊期：

２０16年第6期

DOI：

文章编号：

1000-4637（2016）06-11-04

基金项目：

上海建科院（2014-KF04）：上海市工程结构安全重点实验室资助项目；住建部（2014-H-003）：绿色建筑建材引入碳排放LCA计算评价体系及建材产品碳排放信息共享平台研究；上海市科委（15DZ1204605）：基于互联网的低碳建筑材料智慧应用平台关键

作者：

张贺，杨辉，俞海勇

单位：

上海建科检验有限公司，201108）

摘要

摘要：采用四电极法测试了不同混凝土配合比试件的表面电阻率，分析了表面电阻率随水灰比及胶凝材料配比的变化，并进一步对表面电阻率与电通量的相关性进行了回归分析。试验结果显示，表面电阻率随水灰比增大而减小，双掺矿渣和粉煤灰时混凝土的表面电阻率较大，表面电阻率与电通量具有较好相关性。

Abstract: Surface resistivity(SR) of concrete specimen with different mix proportions was tested by Wenner four-probe measurement. The change of SR with water cement ratio and cementitious materials mix proportion was analyzed, and the relativity of SR and electric flux was discussed in this paper. The results show that, with water cement ratio increases, the SR decreases. When slag and fly ash both added in concrete, the SP of concrete is relatively high. SP and electric flux has good correlation.

结论

通过测试不同配合比混凝土试件的28d龄期抗压强度、表面电阻率和电通量，并将表面电阻率与抗压强度和电通量分别进行回归分析，发现表面电阻率与抗压强度具有较好的指数函数关系，与电通量具有较好的幂函数关系。因此，采用四电极法测试混凝土表面电阻率，对工程质量控制具有重要意义，可根据回归方程快速、无损推定混凝土的抗压强度及抗氯离子性能。

参考文献

[1]王彩文.粉煤灰掺量对混凝土抗氯离子渗透性能的影响[J].武汉工程大学学报,2009,31(7):64-68.

[2]叶建雄,李晓筝,廖佳庆,等.矿物掺和料对混凝土氯离子渗透性扩散性研究[J].重庆建筑大学学报,2005,27(3):89-92.

[3] Lataste JF, Behloul M, Breysse D. Characterization of fiber distribution in a steel fiber reinforced concrete with electrical resistivity measurements[J]. NDT&E Int, 2008:41(8):638-647.

[4] Jin-Kiang Su, Chung-Chia Yang, Wen-Bean, et al. Effect of moisture content on concrete resistivity measurement[J]. Journal of the Chinese Institute of Engineers,2002,25(1):117-122.

[5] F. Presuel-Moreno, Y. Liu, Y.-Y. Wu. Numerical modeling of the effects of rebar presence and/or multilayered concrete resistivity on the apparent resistivity measured via the Wenner method[J]. Construction and Building Materials, 2013,48:16-25.

[6] W. Morris, E.I. Moreno and A.A. Sagues. Practical evaluation of resistivity of concrete in test cylinders using a Wenner array probe[J]. Cement and Concrete Research,1996,26(12):1779-1787.

[7] Chun-Tao Chen, Jiang-Jhy Chang, Wei-chung Yeih. The effects of specimen parameters on the resistivity of concrete[J]. Construction and Building Materials, 2014,71:35-43.

[8] 王翩翩,董桂洪,李克非. 港珠澳大桥沉管隧道预制节段无损检测方法研究[J].混凝土,2015(8):135-142.

[9] 王甲春,张照华,苏宁.混凝土渗透性的原位测试与评价[J].山东大学学报:工学版,2013,43(5):74-79.

[10] 魏小胜,夏玉英,王延伟. 用电阻率法评定混凝土的氯离子渗透[J].华中科技大学学报:城市科学版,2008,25(2):19-22.

[11] 沈威.水泥工艺学[M].武汉:武汉理工大学出版社,2008:237-242.

[12] 贾金青,胡玉龙,王东来,等.混凝土抗压强度与孔隙率关系的研究[J].混凝土,2015(10):56-59.

引用本文

上一个：聚羧酸系减水剂组成与结构对水泥颗粒表面电性质的影响

下一个：高原型泵送剂在共玉高速中的应用研究