轻骨料多孔混凝土的制备与性能
Preparation and Performance of Lightweight Aggregate Porous Concrete
2016年第8期
轻骨料多孔混凝土;强度;导热系数;干燥收缩
Lightweight aggregate concrete; Strength; Thermal conductivity; Drying shrinkage
2016年第8期
1000-4637(2016)08-70-03
孙友康,庞超明,王少华,徐世豪
东南大学材料科学与工程学院,南京 211189

孙友康,庞超明,王少华,徐世豪

浏览量:
1000
摘 要:研究了轻骨料种类、粒径、掺量对轻骨料多孔混凝土抗压强度、导热系数、吸水率、干燥收缩的影响。研究结果表明,轻骨料的筒压强度越高,轻骨料多孔混凝土的抗压强度越高;粒径较小的轻骨料在浆体中分布更为均匀,不易出现上浮现象,抗压强度更高;适量的轻骨料可增加轻骨料混凝土的抗压强度、降低多孔混凝土的导热系数;轻骨料的合理使用可以降低多孔混凝土吸水率与干燥收缩值,提高轻骨料多孔混凝土的耐久性。 Abstract: The effect of lightweight aggregate type, particle size, content on the compressive strength, thermal conductivity, water absorption, drying shrinkage of the lightweight aggregate porous concrete were studied. Compared with lightweight aggregate concrete, the results showed that, the compressive strength of lightweight aggregate is increased with the increase of the cylinder pressure strength of the lightweight aggregate porous concrete. The light aggregate with smaller particle size distributes uniformly can increase the compressive strength. Appropriate lightweight aggregate concrete can increase the compressive strength of lightweight aggregate concrete and reduce the thermal conductivity of porous concrete. The reasonable use of lightweight aggregate can reduce the water absorption and drying shrinkage of the porous concrete and improve the durability of lightweight aggregate concrete.
英文名 : Preparation and Performance of Lightweight Aggregate Porous Concrete
刊期 : 2016年第8期
关键词 : 轻骨料多孔混凝土;强度;导热系数;干燥收缩
Key words : Lightweight aggregate concrete; Strength; Thermal conductivity; Drying shrinkage
刊期 : 2016年第8期
DOI :
文章编号 : 1000-4637(2016)08-70-03
基金项目 :
作者 : 孙友康,庞超明,王少华,徐世豪
单位 : 东南大学材料科学与工程学院,南京 211189

孙友康,庞超明,王少华,徐世豪

摘要
参数
结论
参考文献
引用本文

摘  要:研究了轻骨料种类、粒径、掺量对轻骨料多孔混凝土抗压强度、导热系数、吸水率、干燥收缩的影响。研究结果表明,轻骨料的筒压强度越高,轻骨料多孔混凝土的抗压强度越高;粒径较小的轻骨料在浆体中分布更为均匀,不易出现上浮现象,抗压强度更高;适量的轻骨料可增加轻骨料混凝土的抗压强度、降低多孔混凝土的导热系数;轻骨料的合理使用可以降低多孔混凝土吸水率与干燥收缩值,提高轻骨料多孔混凝土的耐久性。

Abstract: The effect of lightweight aggregate type, particle size, content on the compressive strength, thermal conductivity, water absorption, drying shrinkage of the lightweight aggregate porous concrete were studied. Compared with lightweight aggregate concrete, the results showed that, the compressive strength of lightweight aggregate is increased with the increase of the cylinder pressure strength of the lightweight aggregate porous concrete. The light aggregate with smaller particle size distributes uniformly can increase the compressive strength. Appropriate lightweight aggregate concrete can increase the compressive strength of lightweight aggregate concrete and reduce the thermal conductivity of porous concrete. The reasonable use of lightweight aggregate can reduce the water absorption and drying shrinkage of the porous concrete and improve the durability of lightweight aggregate concrete.

关键词:
轻骨料多孔混凝土;强度;导热系数;干燥收缩
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)轻骨料多孔混凝土的破坏通常发生在轻骨料处,即从骨料中间破坏,因此,轻骨料自身的强度直接影响到轻骨料混凝土的强度,轻骨料的筒压强度越高,轻骨料混凝土的抗压强度越高。
(2)骨料的粒径大小是影响轻骨料多孔混凝土性能的一个关键因素,粒径较小的骨料与水泥石结合的有效面积大,机械啮合作用增强,强度提高;粒径较小,表观密度较大的轻骨料在浆体中分布更为均匀,不容易出现上浮现象。
(3)轻骨料掺量较低时,随着轻骨料掺量增加,轻骨料多孔混凝土的强度提高,但是“内养护”增强效果有限,当超过一定量的时候,增加轻骨料的量反而会因轻骨料自身强度低的原因而降低轻骨料多孔混凝土的强度。
(4)当多孔混凝土密度等级在1400kg/m3时,掺入轻骨料可以提高多孔混凝土的孔隙率,进而降低多孔混凝土的导热系数。
(5)轻骨料的合理使用可以降低多孔混凝土吸水率与干燥收缩,提高轻骨料掺量和使用低粒径的轻骨料均可显著降低混凝土28d的干燥收缩值,提高多孔混凝土的耐久性。
[1] 中国建筑材料联合会.推动墙体材料转型升级[J].建设科技,2012(23):14.
[2] 周志敏.高强度泡沫混凝土研究[D].长沙:湖南大学,2011.
[3] Jones M R, McCarthy A. Preliminary views on the potential of foamed concrete as a structural material[J]. Magazine of concrete research,2005,57(1):21-31.
[4] 刘丽芳.轻集料混凝土匀质性的研究[D].哈尔滨:哈尔滨工业大学,2006.
[5] Weigler H, Karl S. Structural lightweight aggregate concrete with reduced density-lightweight aggregate foamed concrete[J]. International Journal of Cement Composites and Lightweight Concrete, 1980,2(2):101-104.
[6] 邹定华.掺不同级配轻集料混凝土的力学性能和长期性能[J].混凝土,2011(9):87-89.
[7] B.NaitAli, KHaberko, H.Vesteghem. Preparation and thermal conduetivity characterization of  highly porous ceramics colnparison between experimental results, analytic alealeulation andnumeri ealsimulations[J].Joumal of EuroPean Ceralnie Soeiety,2007,27:1345-1350.
[8] 丁庆军.高强次轻混凝土的研究与应用[D].武汉:武汉理工大学,2006.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州