粒化高炉矿渣和CaSO₄对高强混凝土收缩特性影响试验研究

Study on the Effect of Ground-granulated Blast Furnace Slag and CaSO₄ on Shrinkage Characteristics of High Strength

2020年3期

粒化高炉矿渣粉；CaSO4；高强混凝土；收缩；水化

GGBFS; CaSO4; High strength concrete; Shrinkage; Hydration

2020年3期

10.19761/j.1000-4637.2020.03.091.05

河南省交通运输厅科技项目（2019J-2-13）。

苏怡1，菅田紀之2

1.河南理工大学土木工程学院，焦作 454003；2.室兰工业大学，北海道050-8585

苏怡1，菅田紀之2

关键词：粒化高炉矿渣粉；CaSO₄；高强混凝土；收缩；水化

Key words：GGBFS; CaSO₄; High strength concrete; Shrinkage; Hydration

期刊：2020年3期 No.287 P91-95

DOI：10.19761/j.1000-4637.2020.03.091.05

基金项目：河南省交通运输厅科技项目（2019J-2-13）

作者：苏怡1，菅田紀之2

单位：1.河南理工大学土木工程学院，焦作 454003；2.室兰工业大学，北海道050-8585

苏怡,菅田紀之.粒化高炉矿渣和CaSO₄对高强混凝土收缩特性影响试验研究[J].混凝土与水泥制品,2020(3):91-95.

SU Y,SUGATA N.Experimental Study on the Effect of Ground-granulated Blast Furnace Slag and CaSO₄ on Shrinkage Characteristics of High Strength Concrete[J].China Concrete and Cement Products,2020(3):91-95.

浏览量:

1000

摘要：基于正交设计方法，在水胶比为0.3的条件下，研究了0、20%、40%的粒化高炉矿渣（GGBFS）和0、1.5%、3.0%、4.5%的CaSO4对高强混凝土凝结时间、收缩性能的影响，并采用XRD分析了水化过程。结果表明，掺入GGBFS和CaSO4能缩短凝结时间；复掺20%GGBFS和CaSO4的高强混凝土抑制自收缩效果优于复掺40%GGBFS和CaSO4的高强混凝土；复掺40％GGBFS和4.5%CaSO4能有效降低高强混凝土的干燥收缩性能。XRD结果表明，掺入GGBFS和CaSO4有利于水泥的水化反应，促进水化产物的生成。 Abstract: Ttheeffectofreplacementrateofground-granulatedblastfurnaceslag(GGBFS)andCaSO4onthesettingtimeandshrinkageperformanceofhighstrengthconcretewithwater-binderratioof0.3wasstudiedbasedontheorthogonaldesignmethod,andthehydrationprocesswasanalyzedbyX-raydiffraction(XRD).TheresultsshowthattheincorporationofGGBFSandCaSO4canshortenthesettingtime,andtheinhibitionofshrinkageofhighstrengthconcretecompoundedwith20%GGBFSandCaSO4isbetterthanthatofconcretewith40%GGBFSandCaSO4.Thehighstrengthconcretewith40%GGBFSand4.5%CaSO4caneffectivelyreduceitsdryingshrinkageperformance.XRDanalysisshowsthattheincorporationofGGBFSandCaSO4isbeneficialtothehydrationreactionofcementandpromotetheformationofhydrationproducts.

英文名 : Study on the Effect of Ground-granulated Blast Furnace Slag and CaSO₄ on Shrinkage Characteristics of High Strength

刊期 : 2020年3期

关键词 : 粒化高炉矿渣粉；CaSO4；高强混凝土；收缩；水化

Key words : GGBFS; CaSO4; High strength concrete; Shrinkage; Hydration

刊期 : 2020年3期

DOI : 10.19761/j.1000-4637.2020.03.091.05

文章编号 :

基金项目 : 河南省交通运输厅科技项目（2019J-2-13）。

作者 : 苏怡1，菅田紀之2

单位 : 1.河南理工大学土木工程学院，焦作 454003；2.室兰工业大学，北海道050-8585

苏怡1，菅田紀之2

关键词：粒化高炉矿渣粉；CaSO₄；高强混凝土；收缩；水化

Key words：GGBFS; CaSO₄; High strength concrete; Shrinkage; Hydration

期刊：2020年3期 No.287 P91-95

DOI：10.19761/j.1000-4637.2020.03.091.05

基金项目：河南省交通运输厅科技项目（2019J-2-13）

作者：苏怡1，菅田紀之2

单位：1.河南理工大学土木工程学院，焦作 454003；2.室兰工业大学，北海道050-8585

苏怡,菅田紀之.粒化高炉矿渣和CaSO₄对高强混凝土收缩特性影响试验研究[J].混凝土与水泥制品,2020(3):91-95.





摘要

参数

结论

参考文献

引用本文

摘要：基于正交设计方法，在水胶比为0.3的条件下，研究了0、20%、40%的粒化高炉矿渣（GGBFS）和0、1.5%、3.0%、4.5%的CaSO₄对高强混凝土凝结时间、收缩性能的影响，并采用XRD分析了水化过程。结果表明，掺入GGBFS和CaSO₄能缩短凝结时间；复掺20%GGBFS和CaSO₄的高强混凝土抑制自收缩效果优于复掺40%GGBFS和CaSO₄的高强混凝土；复掺40％GGBFS和4.5%CaSO₄能有效降低高强混凝土的干燥收缩性能。XRD结果表明，掺入GGBFS和CaSO₄有利于水泥的水化反应，促进水化产物的生成。

Abstract: Tthe effect of replacement rate of ground-granulated blast furnace slag(GGBFS) and CaSO₄ on the setting time and shrinkage performance of high strength concrete with water-binder ratio of 0.3 was studied based on the orthogonal design method, and the hydration process was analyzed by X-ray diffraction(XRD). The results show that the incorporation of GGBFS and CaSO₄ can shorten the setting time, and the inhibition of shrinkage of high strength concrete compounded with 20% GGBFS and CaSO₄ is better than that of concrete with 40% GGBFS and CaSO₄. The high strength concrete with 40% GGBFS and 4.5% CaSO₄ can effectively reduce its drying shrinkage performance. XRD analysis shows that the incorporation of GGBFS and CaSO₄ is beneficial to the hydration reaction of cement and promote the formation of hydration products.

关键词:

粒化高炉矿渣粉；CaSO4；高强混凝土；收缩；水化

扫二维码用手机看

[1] THOMAS M,BREMNER T.Performance of lightweight aggregate concrete containing slag after 25years in a harsh marine environment [J].Cement and Concrete Research,2012,42(2):358-364.

[2] 小亀大佑,菅田紀之,横川慶介.高炉スラグ微粉末とシリカフュームを用いた高強度コンクリートの自己収縮について[C].コンクリート工学年次論文集,2016(1):183-188.

[3] G?譈NEYISI E,GESOLU M,KARAOGLU S,et al.Strength, permeability and shrinkage cracking of silica fume and metakaolin concretes [J].Construction and Building Materials,2012,34:120-130.

[4] MERMERDAS K,ARBILI M M.Explicit formulation of drying and autogenous shrinkage of concretes with binary and ternary blends of silica fume and fly ash [J].Construction and Building Materials,2015,94:371-379.

[5] 阎培渝,陈志城.含不同矿物掺合料的高强混凝土的自收缩特性[J].工业建筑,2011,41(6):124-127.

[6] 程书凯,水中和,杨荣辉,等.复掺偏高岭土-矿渣对轻骨料混凝土性能的影响[J].硅酸盐通报,2016,35(5):1349-1355.

[7] LIU Z C,HANSEN W.Aggregate and slag cement effects on autogenous shrinkage in cementitious materials [J].Construction and Building Materials,2016,121:429-436.

[8] 佐川孝広,濱幸雄,塚本康誉.高炉セメントA 種の強度発現と水和反応に及ぼす無水石こうと石灰石微粉末の影響[C].セメント·コンクリート論文集,2014(68): 239-245.

[9] 日本工业标准调查会(JISC).JIS A1147-2001用耐渗透性测试混凝土混合物固结时间的试验方法[S].日本工業規格,2001.

[10] 佐川孝広,名和豊春.リートベルト法による高炉セメントの水和反応解析[C].コンクリート工学論文集,2006(3):1-11.

[11] 高松伸之,丸山一平,五十嵐豪,等.高炉スラグ微粉末を用いたセメント硬化体の若材齢体積変化と水和反応に関する研究[C].コンクリート工学年次論文集,2009(1):187-192.

[12] SHARIQ M,PRASAD J,BBAS H A.Creep and drying shrinkage of concrete containing GGBFS[J].Cement and Concrete Composites,2016,68:35-45.

[13] 崔素萍,郑焱,王子明,等.PC-CSA复合水泥收缩特性与微观结构[J].北京工业大学学报,2018,44(4):602-610.

[14] JIANG C H,JIN C,WANG Y Z.Effect of heat curing treatment on the drying shringkage behavior and microstructure characteristics of mortar incorporating different content ground granulated blast-furnace slag [J].Construction and Building Materials,2018,186:379-387.

[15] DING W W,TAN K F,LIU L B.Effect of curing temperature on compressive strength and drying shrinkage of cement paste with fly ash/silica fume[J].J.Southwest.Univ.Sci.Tech,2016,21:63-67.

[14] PENG Y Z,ZHANG J,LIU I Y,et al.Properties and microstructure of reactive power concrete having a high content of phosphorous slag powder and silica fume [J].Construction and Building Materials,2015,101:482-787.

上一个

再生微粉掺量对再生透水混凝土性能的影响研究

下一个

铬铁渣新级配优化方法及对砂浆性能的影响

头部文案

粒化高炉矿渣和CaSO4对高强混凝土收缩特性影响试验研究

相关文件

粒化高炉矿渣和CaSO₄对高强混凝土收缩特性影响试验研究