碱矿渣泡沫混凝土配合比和孔结构研究
Study on Mix Proportion and Pore Structure of Alkali Activated Slag Foam Concrete[J].
2018年第2期
碱矿渣泡沫混凝土;配合比设计;正交试验;孔结构
Alkali activated slag foam concrete; Mix proportion design; Orthogonal test; Pore structure
2018年第2期
1000-4637(2018)02-65-07
国家重点基础研究发展计划(973项目)(2015CB 655100);国家自然科学基金重点国际合作项目(514201050 15);山东省自然科学基金项目(ZR2017MEE040)。
杨保先1,万小梅1,2,赵铁军1,2,曾现琛3,刘国强1,程杨杰1
1.青岛理工大学土木工程学院, 266033;2.青岛理工大学蓝色经济区工程建设与安全 山东省协同创新中心,266033;3.青岛市产品质量监督检验研究院,266101

杨保先1,万小梅1,2,赵铁军1,2,曾现琛3,刘国强1,程杨杰1

杨保先,万小梅,赵铁军,等.碱矿渣泡沫混凝土配合比和孔结构研究[J].混凝土与水泥制品,2018(2):65-71.

YANG B X,WAN X M,ZHAO T J,et al.Study on Mix Proportion and Pore Structure of Alkali Activated Slag Foam Concrete[J].China Concrete and Cement Products,2018(2):65-71.

浏览量:
1000
摘 要:以矿渣掺量系数、溶胶比、碱当量为参数,进行三因素三水平的正交试验,得到以水玻璃为激发剂的碱矿渣泡沫混凝土的最优配合比。试验结果表明,三个因素中,碱当量对碱矿渣泡沫混凝土28d的抗压强度、干密度、导热系数的影响均为最高,其次是溶胶比,矿渣掺量系数影响最小。用Image-ProPlus图像处理与分析软件对碱矿渣泡沫混凝土的孔结构进行分析,得到表征孔隙率、平均圆度系数、平均孔径、孔径分布等孔结构参数,分析可知碱矿渣泡沫混凝土的各项性能与其孔结构之间有着密切的联系,孔隙率和平均孔径越小,抗压强度越高、导热系数越大;碱矿渣泡沫混凝土的干密度与孔隙率有很好的相关性,相关系数R为0.9888。Abstract:Basedontheorthogonalexperiment,theoptimummixproportionofalkaliactivatedslagfoamconcretewithwaterglassasactivatorisobtainedbytakingthreefactorsinvolvesslagcontent,solution-binderratioandequivalentconcentrationofalkalisolution.Theresultsshowthatamongthreefactors,equivalentconcentrationofalkalisolutionhasthehighestimpactonthecompressivestrength,drydensityandthermalconductivityattheageof28d,followedbysolution-binderratio,andinfluenceofslagcontentisthelastone.Theporestructureofalkali-slagfoamconcreteisanalyzedbyImage-ProPlustoobtaintheporestructureparameterssuchasporosity,averagecircularitycoefficient,averageporesizeandporesizedistribution.Itisfoundthatalltheperformanceofalkaliactivatedslagfoamconcreteanditsporestructurearecloselylinked,thesmallertheporosityandaverageporesize,thehigherthecompressivestrength,andthegreaterthethermalconductivity;drydensityofalkaliactivatedslagfoamconcretehasagoodcorrelationwiththeporosity,thecorrelationcoefficientRis0.9888.
英文名 : Study on Mix Proportion and Pore Structure of Alkali Activated Slag Foam Concrete[J].
刊期 : 2018年第2期
关键词 : 碱矿渣泡沫混凝土;配合比设计;正交试验;孔结构
Key words : Alkali activated slag foam concrete; Mix proportion design; Orthogonal test; Pore structure
刊期 : 2018年第2期
DOI :
文章编号 : 1000-4637(2018)02-65-07
基金项目 : 国家重点基础研究发展计划(973项目)(2015CB 655100);国家自然科学基金重点国际合作项目(514201050 15);山东省自然科学基金项目(ZR2017MEE040)。
作者 : 杨保先1,万小梅1,2,赵铁军1,2,曾现琛3,刘国强1,程杨杰1
单位 : 1.青岛理工大学土木工程学院, 266033;2.青岛理工大学蓝色经济区工程建设与安全 山东省协同创新中心,266033;3.青岛市产品质量监督检验研究院,266101

杨保先1,万小梅1,2,赵铁军1,2,曾现琛3,刘国强1,程杨杰1

杨保先,万小梅,赵铁军,等.碱矿渣泡沫混凝土配合比和孔结构研究[J].混凝土与水泥制品,2018(2):65-71.

YANG B X,WAN X M,ZHAO T J,et al.Study on Mix Proportion and Pore Structure of Alkali Activated Slag Foam Concrete[J].China Concrete and Cement Products,2018(2):65-71.

摘要
参数
结论
参考文献
引用本文
摘  要:以矿渣掺量系数、溶胶比、碱当量为参数,进行三因素三水平的正交试验,得到以水玻璃为激发剂的碱矿渣泡沫混凝土的最优配合比。试验结果表明,三个因素中,碱当量对碱矿渣泡沫混凝土28d的抗压强度、干密度、导热系数的影响均为最高,其次是溶胶比,矿渣掺量系数影响最小。用Image-Pro Plus图像处理与分析软件对碱矿渣泡沫混凝土的孔结构进行分析,得到表征孔隙率、平均圆度系数、平均孔径、孔径分布等孔结构参数,分析可知碱矿渣泡沫混凝土的各项性能与其孔结构之间有着密切的联系,孔隙率和平均孔径越小,抗压强度越高、导热系数越大;碱矿渣泡沫混凝土的干密度与孔隙率有很好的相关性,相关系数R为0.9888。
Abstract: Based on the orthogonal experiment, the optimum mix proportion of alkali activated slag foam concrete with waterglass as activator is obtained by taking three factors involves slag content, solution-binder ratio and equivalent concentration of alkali solution. The results show that among three factors, equivalent concentration of alkali solution has the highest impact on the compressive strength, dry density and thermal conductivity at the age of 28d, followed by solution-binder ratio, and influence of slag content is the last one. The pore structure of alkali-slag foam concrete is analyzed by Image-Pro Plus to obtain the pore structure parameters such as porosity, average circularity coefficient, average pore size and pore size distribution. It is found that all the performance of alkali activated slag foam concrete and its pore structure are closely linked, the smaller the porosity and average pore size, the higher the compressive strength, and the greater the thermal conductivity; dry density of alkali activated slag foam concrete has a good correlation with the porosity, the correlation coefficient R is 0.9888.
关键词:
碱矿渣泡沫混凝土;配合比设计;正交试验;孔结构
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)以碱矿渣泡沫混凝土的抗压强度、干密度、导热系数为试验指标,以矿渣掺量系数、溶胶比、碱当量为因素,进行三因素三水平的正交试验,通过极差分析,得到三个因素对碱矿渣泡沫混凝土性能的影响,碱当量>溶胶比>矿渣掺量系数。当碱当量为9%、溶胶比为0.46、矿渣掺量系数为1.4时,碱矿渣泡沫混凝土的性能最优。
(2)碱当量对碱矿渣泡沫混凝土性能的影响最为显著,当碱当量为5%~9%时,随着碱当量的提高,矿渣的水化进度加快、反应程度更高,混合在浆体中的泡沫越不容易损失,得到的泡沫混凝土性能更加稳定,其抗压强度更高、干密度能更好地符合设计值。
(3)通过用Image Pro Plus软件对各组试块的孔结构进行分析,得到表征孔隙率、平均圆度系数、平均孔径、孔径分布的参数。孔隙率越小、平均孔径越小、小孔所占比例越大,碱矿渣泡沫混凝土的抗压强度越高;碱矿渣泡沫混凝土的干密度与孔隙率有很好的相关性,拟合公式为y=-19.99x+1921.37,相关系数R为0.9888;孔隙率越大、平均圆度系数越小、平均孔径越大,碱矿渣泡沫混凝土的导热系数越小。
[1] 李应权,朱立德,李菊丽,等.泡沫混凝土配合比设计[J].徐州工程学院学报,2011,26(2):1-5.
[2] 黄政宇,孙庆丰,周志敏,等.硅酸盐-硫铝酸盐水泥超轻泡沫混凝土孔结构及性能研究[J].硅酸盐通报,2013(9):1894-1899.
[3] 张英,杨小芳,赵芊,等.泡沫混凝土在屋面保温工程中的应用[J].新型建筑材料,2011(9):19-21.
[4] 李国栋,毕万利,孙晓婷,等.物理发泡泡沫混凝土的制备与性能研究[J].硅酸盐通报,2017(2):733-737.
[5] 史才军.碱激发水泥和混凝土[M].北京:化学工业出版社, 2008.
[6] 杨长辉,蒲心诚.论碱矿渣水泥及混凝土的缓凝问题及缓凝方法[J].重庆建筑大学学报,1996,18(3):67-72.
[7] 中华人民共和国住房和城乡建设部.JGJ/T 341—2014 泡沫混凝土应用技术规程[S].北京:中国建筑工业出版社,2014.
[8] 杨长辉,王磊,田义.碱矿渣泡沫混凝土性能研究[J].硅酸盐通报,2016(2):555-560.
[9] 中华人民共和国住房和城乡建设部.JG/T 266—2011 泡沫混凝土[S].北京:中国标准出版社,2011.
[10] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.GB/T 10294—2008 绝热材料稳态热阻及有关特性的测定防护热板法[S].北京:中国标准出版社,2008.
[11] 蒲心诚.碱矿渣水泥与混凝土[M].北京:科学出版社,2010.
[12] Krizan D, Zivanovic B. Effects of dosage and modulus of waterglass on early hydration of alkali-slag cements [J]. Cement and Concrete Research,2002,32(8):1181-1188.
[13] 刘国权,王浩,肖翔,等.经典体视学:基本功能、独特应用与标准化应用[J].中国体视学与图像分析,2012(4):293-300.
[14] 张雄,黄廷皓,张永娟,等.Image-Pro Plus混凝土孔结构图像分析方法[J].建筑材料学报,2015,18(1):177-182.
[15] 陈贤瑞,卢都友,孙亚峰,等.图像分析法表征泡沫地质聚合物宏观孔结构[J].材料导报,2015,29(26):113-117.
[16] 方永浩,王锐,庞二波,等.水泥-粉煤灰泡沫混凝土抗压强度与气孔结构的关系[J].硅酸盐学报,2010,38(4):621-626.
[17] 朱明,王方刚,张旭龙,等.泡沫混凝土孔结构与导热性能的关系研究[J].武汉理工大学学报,2013,35(3):21-25.
[18] 李相国,刘敏,马保国,等.孔结构对泡沫混凝土性能的影响与控制技术[J].材料导报,2012,26(4):141-144.
[19] Mydin M A O.Effective thermal conductivity of foamcrete of different densities[J].Concrete Research Letters,2011,2(1):181-189.
[20] 顾亚敏,方永浩.碱矿渣水泥的收缩与开裂特性及其减缩与增韧[J].硅酸盐学报,2012,40(1):76-84.

杨保先,万小梅,赵铁军,.碱矿渣泡沫混凝土配合比和孔结构研究[J].混凝土与水泥制品,2018(2):65-71.

YANG B X,WAN X M,ZHAO T J,et al.Study on Mix Proportion and Pore Structure of Alkali Activated Slag Foam Concrete[J].China Concrete and Cement Products,2018(2):65-71.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州