掺钢渣粉尾矿高性能混凝土的制备
Preparation of High Performance Concrete Adding Steel Slag Powder Tailing
2016年第9期
钢渣粉;混凝土;抗压强度;微观形貌
Steel slag powder; Concrete; Compressive strength; Microstructure
2016年第9期
1000-4637(2016)09-78-04
陕西省尾矿资源综合利用重点实验室开放基金(2014SKY-WK001);商洛市科技计划项目(SK2014-01-03)
崔孝炜,狄燕清,徐朝阳
商洛学院 陕西省尾矿资源综合利用重点实验室,726000)

崔孝炜,狄燕清,徐朝阳

浏览量:
1000
摘 要:研究了钢渣粉掺量和养护方式对全固废混凝土抗压强度的影响,并通过SEM分析了掺钢渣胶凝材料水化产物微观形貌。研究结果表明,钢渣粉掺量对混凝土的抗压强度有较大影响,湿热养护能够有效激发钢渣的活性,提高胶凝材料早期强度。掺入20%钢渣粉,采用56℃湿热养护,可以制备出28d抗压强度达77.26MPa的混凝土。掺入钢渣粉对水化产物种类不会造成影响,在反应的中后期,体系中C-S-H凝胶和钙矾石的协同生成能够促进体系强度的增长。 Abstract: The effect of steel slag powder proportion and curing process on compressive strength of solid waste concrete was investigated. The microstructure of hydration products was analyzed by SEM. The results showed that, steel slag content has great influence on the compressive strength of concrete. Steam curing can effectively stimulate the activity of steel slag and improve the early strength of gelling material. Mixed with 20% steel slag, curing at 56℃, the compressive strength of the concrete can achieve 77.26MPa at 28d. The addition of steel slag power has no effect on the type of hydration, the coordinated growth of the ettringite and C-S-H gel is significant for the strength of system in the middle and late stage of the reaction.
英文名 : Preparation of High Performance Concrete Adding Steel Slag Powder Tailing
刊期 : 2016年第9期
关键词 : 钢渣粉;混凝土;抗压强度;微观形貌
Key words : Steel slag powder; Concrete; Compressive strength; Microstructure
刊期 : 2016年第9期
DOI :
文章编号 : 1000-4637(2016)09-78-04
基金项目 : 陕西省尾矿资源综合利用重点实验室开放基金(2014SKY-WK001);商洛市科技计划项目(SK2014-01-03)
作者 : 崔孝炜,狄燕清,徐朝阳
单位 : 商洛学院 陕西省尾矿资源综合利用重点实验室,726000)

崔孝炜,狄燕清,徐朝阳

摘要
参数
结论
参考文献
引用本文

摘   要:研究了钢渣粉掺量和养护方式对全固废混凝土抗压强度的影响,并通过SEM分析了掺钢渣胶凝材料水化产物微观形貌。研究结果表明,钢渣粉掺量对混凝土的抗压强度有较大影响,湿热养护能够有效激发钢渣的活性,提高胶凝材料早期强度。掺入20%钢渣粉,采用56℃湿热养护,可以制备出28d抗压强度达77.26MPa的混凝土。掺入钢渣粉对水化产物种类不会造成影响,在反应的中后期,体系中C-S-H凝胶和钙矾石的协同生成能够促进体系强度的增长。

Abstract: The effect of steel slag powder proportion and curing process on compressive strength of solid waste concrete was investigated. The microstructure of hydration products was analyzed by SEM. The results showed that, steel slag content has great influence on the compressive strength of concrete. Steam curing can effectively stimulate the activity of steel slag and improve the early strength of gelling material. Mixed with 20% steel slag, curing at 56℃, the compressive strength of the concrete can achieve 77.26MPa at 28d. The addition of steel slag power has no effect on the type of hydration, the coordinated growth of the ettringite and C-S-H gel is significant for the strength of system in the middle and late stage of the reaction.

关键词:
钢渣粉;混凝土;抗压强度;微观形貌
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)钢渣粉的掺入对混凝土的抗压强度具有较为明显的影响,尤其是对早期强度有较大的影响。随着钢渣粉掺量的不断增加,混凝土在3d、7d和28d龄期时的抗压强度均呈现出下降的趋势。钢渣粉较为适宜的掺量为20%。
(2)养护工艺对于全固废混凝土的抗压强度影响作用较为明显。高温湿热养护有利于混凝土早期强度的提高,但是温度过高会出现钙矾石的脱水和重结晶,对混凝土的后期稳定性不利。
(3)钢渣粉开始时水化速度较慢,但在反应中后期,RO相和少量f-CaO会慢慢参与到水化反应当中,其水化产物主要为Ca(OH)2、C-S-H凝胶,同时还有少量的Fe6(OH)12(CO3)。体系中的钙矾石和C-S-H 凝胶二者协同生成,有效地促进了混凝土体系强度的增长。
[1] 孙树杉,杨景玲,朱桂林.我国钢铁渣资源化利用现状及发展趋势[J].中国废钢铁,2010(1):10-12.
[2] 黄辉.钢渣的活性激发及其应用现状[J].粉煤灰综合利用, 2012(2):51-54.
[3] 张朝晖,廖杰龙,巨建涛,等.钢渣处理工艺与国内外钢渣利用技术[J].钢铁研究学报,2013,25(7):1-4.  
[4] 张柱银,王应乐,陈开明,等.钢渣掺量对混凝土胶砂强度影响研究[J].硅酸盐通报,2015,34(1):120-124.
[5] 严丽君,潭潭,张捷宇,等.钢渣掺入料对矿渣水泥性能的影响[J].上海大学学报:自然科学版,2013,19(5):448-453.
[6] 吴辉,倪文,崔孝炜,等.利用热闷钢渣制备低收缩铁路轨枕混凝土[J].材料热处理学报,2014,35(4):7-12.
[7] 张波,胡瑾,阎培渝.钢渣在蒸养条件下的安定性[J].电子显微学报,2014,33(3):246-250.
[8] 阎培渝,王强.高温养护对钢渣复合胶凝材料早期水化性能的影响[J].清华大学学报:自然科学版,2009,49(6):790-793.
[9] 王善拔.钙矾石热稳定性的研究[J].膨胀剂与膨胀混凝土, 2007(1):8-11,22.
[10] 王强,阎培渝.大掺量钢渣复合胶凝材料早期水化性能和浆体结构[J].硅酸盐学报,2008,36(10):1406-1410. 
[11] 狄燕清,崔孝炜.掺尾矿高性能混凝土的制备[J].商洛学院学报,2015,29(6):32-36.
[12] 赵海晋,余其俊,韦江雄,等.组成和温度对重构钢渣结构及其早期水化活性的影响[J].建筑材料学报,2012,15(3):399-405.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州